Water treatment composite material with high anti-bacterial efficiency and slow release performance

A water quality treatment and composite material technology, applied in the direction of sterilization/microdynamic water/sewage treatment, water/sewage treatment, water/sludge/sewage treatment, etc., can solve water pollution, endanger human health, and affect industrial and agricultural production And other issues

Inactive Publication Date: 2018-06-05
安徽阳城化工科技有限公司
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Industrial wastewater is the process wastewater, cooling water, waste washing water, equipment and site flushing water and other wastewater discharged in chemical production. If these wa...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A water quality treatment composite material with high antibacterial efficiency and slow release performance, the raw materials of which include, by weight, 100 parts of aluminum trichloride, 50 parts of phosphorus trichloride, 40 parts of modified slow release aids, modified antibacterial 25 parts of filler, 6 parts of tributyl citrate, 3.5 parts of octyl methoxycinnamate, 4.5 parts of sodium carbonate, 30 parts of polylactic acid, 20 parts of chitosan, 6 parts of zinc phosphate, 3.5 parts of zinc oxide, wollastonite powder 3 parts, 3 parts of kaolin, 6 parts of nano-titanium dioxide, 6 parts of alumina, 4 parts of sodium borate, 3.5 parts of hydroxyethyl cellulose, 6 parts of sodium tetraborate, 20 parts of 1,3-butanediol.

[0015] The modified slow-release aid was prepared according to the following process: 6 parts of attapulgite, 4.5 parts of yellow clay, 3.5 parts of zeolite, 3 parts of diatomaceous earth, 6 parts of shell powder and 4.5 parts of carbon nanotubes w...

Embodiment 2

[0018] A water quality treatment composite material with high antibacterial efficiency and sustained release performance, the raw materials of which include by weight: 120 parts of aluminum trichloride, 40 parts of phosphorus trichloride, 50 parts of modified slow release aids, modified antibacterial 15 parts of filler, 9 parts of tributyl citrate, 2 parts of octyl methoxycinnamate, 6 parts of sodium carbonate, 20 parts of polylactic acid, 25 parts of chitosan, 4 parts of zinc phosphate, 5 parts of zinc oxide, wollastonite powder 1 part, 5 parts of kaolin, 4 parts of nano titanium dioxide, 9 parts of alumina, 2 parts of sodium borate, 5 parts of hydroxyethyl cellulose, 4 parts of sodium tetraborate, 25 parts of 1,3-butanediol.

[0019] The modified slow-release aid was prepared according to the following process: 8 parts of attapulgite, 3 parts of yellow clay, 5 parts of zeolite, 1 part of diatomaceous earth, 8 parts of shell powder and 3 parts of carbon nanotubes were mixed in...

Embodiment 3

[0022] A water quality treatment composite material with high antibacterial efficiency and sustained release performance, the raw materials of which include by weight: 80 parts of aluminum trichloride, 60 parts of phosphorus trichloride, 30 parts of modified slow release aids, modified antibacterial 35 parts of filler, 3 parts of tributyl citrate, 5 parts of octyl methoxycinnamate, 3 parts of sodium carbonate, 40 parts of polylactic acid, 15 parts of chitosan, 8 parts of zinc phosphate, 2 parts of zinc oxide, wollastonite powder 5 parts, 1 part of kaolin, 8 parts of nano titanium dioxide, 3 parts of aluminum oxide, 6 parts of sodium borate, 2 parts of hydroxyethyl cellulose, 8 parts of sodium tetraborate, 15 parts of 1,3-butanediol.

[0023] The modified slow-release aid is prepared according to the following process: 4 parts of attapulgite, 6 parts of yellow clay, 2 parts of zeolite, 5 parts of diatomaceous earth, 4 parts of shell powder and 6 parts of carbon nanotubes are mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a water treatment composite material with high anti-bacterial efficiency and slow release performance. The water treatment composite material is prepared from the raw materials: aluminum trichloride, phosphorus trichloride, a modified slow release auxiliary, a modified anti-bacterial filler, tributyl citrate, octyl methoxycinnamate, sodium carbonate, polylactic acid, chitosan, zinc phosphate, zinc oxide, wollastonite powder, kaolin, nanometer titania, aluminum oxide, sodium borate, hydroxyethyl cellulose, sodium tetraborate, and 1,3-butanediol. The water treatment composite material provided by the invention has an excellent slow release performance, and can be beneficial to effectively improving of water treatment efficiency and quality.

Description

technical field [0001] The invention relates to the technical field of water quality treatment, in particular to a water quality treatment composite material with high antibacterial efficiency and slow release performance. Background technique [0002] Industrial wastewater is the process wastewater, cooling water, waste washing water, equipment and site flushing water discharged in chemical production. If these wastewater is discharged without treatment, it will cause different properties and degrees of pollution to the water body, thus Harmful to human health, affecting industrial and agricultural production. Contents of the invention [0003] In order to solve the technical problems existing in the background technology, the present invention proposes a water treatment composite material with high antibacterial efficiency and slow release performance, which can improve the efficiency and quality of water treatment. [0004] A water quality treatment composite material ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F1/00C02F1/50
CPCC02F1/00C02F1/50C02F2303/04
Inventor 韩华良
Owner 安徽阳城化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap