Core making process of resin sand

A technology of resin sand and process, applied in the direction of manufacturing tools, cores, metal processing equipment, etc., can solve the problems of easy cracking and missing corners of sand cores, image product quality, rough surface, etc., to achieve good adhesion effect and stable overall structure , The structure is stable and reliable

Inactive Publication Date: 2018-06-15
湖南精量重工科技有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Casting process is the technology and method of producing castings by applying casting related theory and systematic knowledge, including molding material preparation, modeling, core making, metal smelting, pouring and solidification control, etc. Core making is an important step in the casting process, and the manufactured core The quality of the mold directly affects the quality of the cast product. However, the sand core produced by the existing core-making process is prone to cracking and chipping, the surface is not smooth, and the exhaust channel is blocked, which leads to the surface of the final casting produced parts. Conditions such as burrs or cracks, image product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The invention discloses a resin sand core making process, comprising the following steps:

[0025] s1. Mix resin, curing agent and raw sand in proportion to form mixed sand, wherein the SiO2 content in the raw sand is not less than 96%, the moisture content is not more than 0.2%, the mud content is not more than 2%, and the large-sized particles in the raw sand The particle size range is between 40-70 mesh, and the particle size range of small-sized particles is between 70-140 mesh; the resin mass accounts for 1.4-2.0% of the original sand mass, and the curing agent mass accounts for 30-40% of the resin mass; first Mix the resin with half of the raw sand, the curing agent with the other half of the raw sand, and then mix the resin-mixed raw sand with the curing agent-mixed raw sand to improve the strength and gas generation of the mixed sand;

[0026] s2. Check and clean the core box, and apply a release agent on the core box;

[0027] s3. Wait for the release agent to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a core making process of resin sand. The core making process comprises the following steps that s1, resin, a curing agent and roughing sand are mixed in proportion to form mixed sand; s2, a releasing agent is brushed on a mold; s3, after the releasing agent is dried, a core box is closed, a core bar, a chilling block and a moving block are put in the core box, the core boxis fast filled with the mixed sand, and the mixed sand is pounded; s4, after the mixed sand is pounded, an air outlet needle or an air outlet rope is pulled out to form an exhaust channel; s5, after the surface of the mixed sand is hardened, the core box is opened; s6, after the sand is cured, core finishing is carried out, rough edges and burrs on the surface of the sand are removed, unfilled corners and holes are checked, repair paste is used for repairing, and finished sand can be obtained; s7, ethyl alcohol is added into coating for mixing, and the surface of the finished sand is evenly coated with the coating through a brush; and s8, after coating is completed, the coating is immediately ignited, sufficient combustion is achieved, after cooling, the finished sand is dried, and a resinsand core is obtained. According to the core making process, the resin, the curing agent and the roughing sand are mixed in proportion, and the made sand core is good in adhesion effect, stable in structure and smooth in surface.

Description

technical field [0001] The invention relates to the field of casting, in particular to a resin sand core-making process. Background technique [0002] Casting process is the technology and method of producing castings by applying casting related theory and systematic knowledge, including molding material preparation, modeling, core making, metal smelting, pouring and solidification control, etc. Core making is an important step in the casting process, and the manufactured core The quality of the mold directly affects the quality of the cast product. However, the sand core produced by the existing core-making process is prone to cracking and chipping, the surface is not smooth, and the exhaust channel is blocked, which leads to the surface of the final casting produced parts. Burrs or cracks, etc., image product quality. Contents of the invention [0003] In order to solve the above technical problems, the object of the present invention is to provide a resin sand core mak...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C9/10B22C9/18B22C3/00
CPCB22C3/00B22C9/10B22C9/18
Inventor 陈文涛何建新彭建荣
Owner 湖南精量重工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products