Multifunctional composite filter screen material for air purifier and preparation method thereof

An air purifier and composite material technology, which is applied in chemical instruments and methods, botanical equipment and methods, separation methods, etc., can solve the problems of few multi-functional composite filter screens and high cost of purifiers, and achieve improved specific surface area and Adsorption capacity, beneficial to enrichment, and the effect of improving visible light response

Inactive Publication Date: 2018-06-29
XIAOGAN YUANDA NEW MATERIAL TECH CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the more filter layers are usually added, the higher the cost of the purifier. Sterilization filters and photocatalyst filters generally appear on mid-to-high-end products. At present, there are few existing air purifiers on the market. Multifunctional composite filter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) Preparation of N-aryl-2-(benzisothiazolin-3-one-2-yl)formamide organic antibacterial agent. Weigh 20mmol of bistrichloromethyl carbonate and 10mL of toluene, add to a three-necked flask with a volume of 100mL equipped with stirring, reflux condenser and constant pressure funnel and stir, add 30mmol of o-methyl to the constant pressure funnel The mixed solution of aniline and 10mL of toluene was slowly added dropwise to the flask. When the dropwise addition was completed, the reaction was heated under reflux for 5h. When the reaction was completed, 30mmol of benzisothiazolin-3-one was directly added to the flask, and Add 20mL of toluene to carry out reflux reaction. After the reaction is completed, naturally cool to room temperature, filter under reduced pressure, wash with acetone to remove unreacted substances, and place in a vacuum drying oven to dry at 50°C for 24h. The white needle-like crystals obtained were N-aryl-2-(benzisothiazolin-3-one-2-yl)formamide;

[...

Embodiment 2

[0037] (1) Preparation of N-aryl-2-(benzisothiazolin-3-one-2-yl)formamide organic antibacterial agent. Weigh 20mmol of bistrichloromethyl carbonate and 10mL of toluene, add to a three-necked flask with a volume of 100mL equipped with stirring, reflux condenser and constant pressure funnel and stir, add 30mmol of o-methyl to the constant pressure funnel The mixed solution of aniline and 10mL of toluene was slowly added dropwise to the flask. When the dropwise addition was completed, the reaction was heated under reflux for 5h. When the reaction was completed, 30mmol of benzisothiazolin-3-one was directly added to the flask, and Add 20mL of toluene to carry out reflux reaction. After the reaction is completed, naturally cool to room temperature, filter under reduced pressure, wash with acetone to remove unreacted substances, and place in a vacuum drying oven to dry at 50°C for 24h. The white needle-like crystals obtained were N-aryl-2-(benzisothiazolin-3-one-2-yl)formamide; (2),...

Embodiment 3

[0039] (1) Preparation of N-aryl-2-(benzisothiazolin-3-one-2-yl)formamide organic antibacterial agent. Weigh 20mmol of bistrichloromethyl carbonate and 10mL of toluene, add to a three-necked flask with a volume of 100mL equipped with stirring, reflux condenser and constant pressure funnel and stir, add 30mmol of o-methyl to the constant pressure funnel The mixed solution of aniline and 10mL of toluene was slowly added dropwise to the flask. When the dropwise addition was completed, the reaction was heated under reflux for 5h. When the reaction was completed, 30mmol of benzisothiazolin-3-one was directly added to the flask, and Add 20mL of toluene to carry out reflux reaction. After the reaction is completed, naturally cool to room temperature, filter under reduced pressure, wash with acetone to remove unreacted substances, and place in a vacuum drying oven to dry at 50°C for 24h. The white needle-like crystals obtained were N-aryl-2-(benzisothiazolin-3-one-2-yl)formamide; (2),...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a multifunctional composite filter screen material for an air purifier and a preparation method thereof. The multifunctional composite filter screen material is prepared from the following ingredients in percentage by weight: 5 to 10 mass percent of N-aryl-2-(benzisothiazolin-3-ketone-2-yl)methanamide organic antibacterial agents, 10 to 15 mass percent of Ag-MOFs compositematerials, 25 to 30 mass percent of terbium-doping mesoporous TiO2 nanometer photocatalysts and 50 mass percent of active carbon fiber. The bacteriostasis rate of the composite filter screen materialon escherichia coli can reach 98 percent; the removal rate on formaldehyde reaches up to 99 percent.

Description

[0001] This application is a divisional application, the original patent number is: 201710513744.7, the application date is June 23, 2017, and the title of the invention is: a multifunctional composite filter material for an air purifier and its preparation method. technical field [0002] The invention relates to a multifunctional composite filter material for an air purifier and a preparation method thereof, which belongs to the technical field of composite functional materials and is suitable for the filter material of an air purifier. Background technique [0003] Air purifiers are small household appliances used to purify indoor air, mainly to solve the problem of indoor air pollution caused by decoration or other reasons. Since the release of pollutants in indoor air is characterized by persistence and uncertainty, the use of air purifiers to purify indoor air is an internationally recognized method to improve indoor air quality. [0004] The filter screen is the core ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/22B01J20/30B01D39/14B01D53/02B01D53/86B01D53/72B01J23/10A01N59/16A01N43/80A01P3/00
CPCB01D39/14B01D53/02B01D53/8668B01J20/20B01J20/226A01N43/80A01N59/16B01J23/10B01D2257/91B01D2255/802B01D2258/06B01J35/39A01N2300/00
Inventor 冷建军
Owner XIAOGAN YUANDA NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com