Method for preparing coated straw fiber-based water-retaining slow-release fertilizer

A straw fiber and coated technology, which is applied in the field of preparing coated straw fiber-based water-retaining slow-release fertilizer, can solve the problems of poor water-retaining performance and slow-release effect, waste of straw waste resources, and poor mechanical strength, etc., to achieve It is beneficial to the load capacity and retention, enhances the slow-release effect, and increases the effect of diffusion resistance

Inactive Publication Date: 2019-09-24
INST OF ENVIRONMENT & SUSTAINABLE DEV IN AGRI CHINESE ACADEMY OF AGRI SCI
View PDF9 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the above-mentioned prior art, the object of the present invention is to provide a method for preparing coated straw fiber-based water-retaining slow-release fertilizer, which solves the problem of high prepa

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing coated straw fiber-based water-retaining slow-release fertilizer

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] Example 1

[0030] 1) Cellulose extraction: the wheat straw is washed and dried to remove impurities, crushed through 20 meshes to obtain straw powder, and then 10% nitric acid solution is added to the straw powder with a solid-liquid ratio of 1:30. Then heat and stir at 85°C for 3 hours. After the extraction is completed, cool to room temperature, and then filter, dry and grind to extract the cellulose powder;

[0031] 2) Preparation of cellulose-based super absorbent resin: add the cellulose powder prepared in step 1) to deionized water, stir and disperse in a water bath at 75°C for 30 minutes, and then add potassium persulfate and sodium sulfite to stir under nitrogen protection 15min, the total mass ratio of cellulose powder to potassium persulfate and sodium sulfite mixed powder is 1:0.25, and then add acrylic acid, urea and N,N-methylenebisacrylamide with a degree of neutralization of 70%, cellulose powder, The mass ratio of acrylic acid, urea and N,N-methylenebisacry...

Example Embodiment

[0034] Example 2

[0035] 1) Extraction of cellulose: the corn stalks are washed and dried to remove impurities, pulverized through 20 meshes to obtain straw powder, and then 10% nitric acid solution is added to the straw powder with a solid-liquid ratio of 1:50. Then heat and stir at 110°C for 5 hours. After the extraction, cool to room temperature, filter, dry and grind to extract the cellulose powder;

[0036] 2) Preparation of cellulose-based super absorbent resin: add the cellulose powder prepared in step 1) to deionized water, stir and disperse in a water bath at 80°C for 50 minutes, and then add potassium persulfate and sodium sulfite under nitrogen protection. 20min, the total mass ratio of cellulose powder mixed with potassium persulfate and sodium sulfite (the mass ratio of potassium persulfate and sodium sulfite is 1:1) is 1:0.4, and then add acrylic acid, urea and N with a neutralization degree of 70% in sequence ,N-methylene bisacrylamide, make the mass ratio of cellu...

Example Embodiment

[0039] Example 3

[0040] 1) Cellulose extraction: the rape straw is washed and dried to remove impurities, pulverized through 20 meshes to obtain straw powder, and then 10% nitric acid solution is added to the straw powder, the solid-liquid ratio is 1:50, Then heat and stir at 100°C for 4 hours. After the extraction, cool to room temperature, filter, dry and grind to obtain the cellulose powder;

[0041] 2) Preparation of cellulose-based super absorbent resin: Add the cellulose powder prepared in step 1) to deionized water, stir and disperse in a water bath at 70°C for 30 minutes, and then add potassium persulfate and sodium sulfite under nitrogen protection. 30min, the total mass ratio of the mixed powder of cellulose powder, potassium persulfate and sodium sulfite (the mass ratio of potassium persulfate and sodium sulfite is 1:1) is 1:0.3, and then add acrylic acid, urea and N with a neutralization degree of 80%. ,N-methylene bisacrylamide, make the mass ratio of cellulose powd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a coated straw fiber-based water-retaining slow-release fertilizer. According to the method, a straw cellulose polysaccharide chain is used as a framework; acrylic acid and acrylamide substances generated by a reaction of acrylic acid and urea are grafted to a cellulose main chain; then crosslinking is carried out by a cross-linking agent to form a polymer with a three-dimensional network structure; meanwhile, the polymer with the three-dimensional network structure and polyvinyl alcohol interpenetrate through each other to form high-water-absorbing resin with a semi-interpenetrating network structure; then the high-water-absorbing resin with the semi-interpenetrating network structure coats fertilizer particles; and a mixed solution of polyvinyl alcohol, sodium alginate and carboxymethyl cellulose forms a membrane by crosslinking to coat the outermost layer of the fertilizer particles to obtain the coated straw fiber-based water-retaining slow-release fertilizer. The fertilizer disclosed by the invention has good mechanical properties and water absorption performance, has excellent slow release effects on the fertilizer, reduces nutrient loss, improves the utilization rate of the fertilizer, reduces maintenance cost of farmland in the later period, and improves the yield and quality of crops. The method provided by the invention has the advantages that the operation method is simple and convenient, cost is low, the additional value of straw application is improved, and the new idea of straw resourceful utilization is further expanded.

Description

technical field [0001] The invention relates to the technical field of material engineering, in particular to a method for preparing a coated straw fiber-based water-retaining slow-release fertilizer. Background technique [0002] Crop straw is a huge amount of natural polymer resources accompanied by uninterrupted agricultural production. my country is a large agricultural country with a huge amount of straw, with an annual output of more than 900 million tons, but the comprehensive utilization rate of straw resources is still low. How to rationally utilize renewable straw cellulose resources is an important content of current environmental green technology, and it is also One of the key points of current research work in the field of resource development and ecological environment protection. On the other hand, in the process of agricultural production in our country, a large amount of nitrogen and phosphate fertilizers are used and the utilization rate is too low, resulti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C05G3/00C05G3/04C08F251/02C08F261/04C08F220/06C08F222/38C05G3/80
CPCC05C9/00C05B7/00C05G3/00C08F251/02C08F261/04C05G5/30C05G3/80C08F220/06
Inventor 王惟帅杨世琦邢磊
Owner INST OF ENVIRONMENT & SUSTAINABLE DEV IN AGRI CHINESE ACADEMY OF AGRI SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap