Preparation method of high-toughness silicone nipple

A high-toughness, silicone technology, used in the field of pacifiers, can solve the problems of less toughness than latex, latex produces toxins, short service life, etc., and achieves safe, hygienic and reliable use, good biocompatibility, and reduced breakage rate and tear rate. Effect

Inactive Publication Date: 2018-06-29
FENGYANG JIASONG NEW MATERIALS CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the baby pacifiers on the market are divided into two types according to the material, which are mainly latex and silica gel; latex pacifiers are generally light yellow, and the main material is natural latex, which is a soft and extremely elastic material that can resist pulling. It will not accumulate static electricity and is harmless to the environment. However, since latex is a natural material, it may produce rubbery smell, short service life, and easy aging. Inferior latex will produce toxins at high temperatures; silicone pacifiers are made of food-grade silicone This material has a smooth and transparent surface, is non-toxic and tasteless, and can resist drastic changes in ambient temperature and can be boiled, but its toughness is not as good as latex, and it is easy to tear once the surface is damaged; therefore, it is urgent to invent a High tenacity silicone nipple

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] In an embodiment of the present invention, a method for preparing a high-toughness silicone nipple specifically includes the following steps:

[0018] (1) Weigh raw materials by weight, 85 parts of liquid silica gel, 4.4 parts of amino silicone oil, 0.32 parts of gallic acid, 0.41 parts of pullulan, 6.3 parts of sodium caseinate, 2.1 parts of sodium carboxymethylcellulose, gum arabic 4.4 parts, 26~28 parts of water;

[0019] (2) Mix liquid silica gel, amino silicone oil, gallic acid, pullulan, sodium caseinate and sodium carboxymethyl cellulose, stir with a stirrer at a speed of 75r / min for 8min, adjust the speed to 110r / min and continue Stir for 13 minutes, put it into the freezer for freezing treatment, and obtain a primary mixture;

[0020] (3) Mix the primary mixture, gum arabic and water, stir for 10 minutes with a stirrer with a rotating speed of 75r / min, put it in a magnetic field for magnetization treatment, and obtain the secondary mixture;

[0021] (4) Put t...

Embodiment 2

[0027] In an embodiment of the present invention, a method for preparing a high-toughness silicone nipple specifically includes the following steps:

[0028] (1) Weigh raw materials by weight, 88 parts of liquid silica gel, 4.6 parts of amino silicone oil, 0.34 parts of gallic acid, 0.43 parts of pullulan, 6.6 parts of sodium caseinate, 2.2 parts of sodium carboxymethylcellulose, gum arabic 4.6 parts, 27 parts of water;

[0029] (2) Mix liquid silica gel, amino silicone oil, gallic acid, pullulan, sodium caseinate and sodium carboxymethyl cellulose, stir with a stirrer at a speed of 80r / min for 9min, adjust the speed to 115r / min and continue Stir for 14 minutes, put it into the freezer for freezing treatment, and obtain a primary mixture;

[0030] (3) Mix the primary mixture, gum arabic and water, stir for 11 minutes with a stirrer with a rotating speed of 80r / min, put it in a magnetic field for magnetization treatment, and obtain the secondary mixture;

[0031] (4) Put the ...

Embodiment 3

[0037] In an embodiment of the present invention, a method for preparing a high-toughness silicone nipple specifically includes the following steps:

[0038] (1) Weigh raw materials by weight, 90 parts of liquid silica gel, 4.8 parts of amino silicone oil, 0.36 parts of gallic acid, 0.45 parts of pullulan, 6.9 parts of sodium caseinate, 2.3 parts of sodium carboxymethylcellulose, gum arabic 4.8 parts, 28 parts of water;

[0039] (2) Mix liquid silica gel, amino silicone oil, gallic acid, pullulan, sodium caseinate and sodium carboxymethyl cellulose, stir with a stirrer at a speed of 85r / min for 10min, adjust the speed to 120r / min and continue Stir for 15 minutes, put it into the freezer for freezing treatment, and obtain a primary mixture;

[0040] (3) Mix the primary mixture, gum arabic and water, stir for 12 minutes with a stirrer with a rotating speed of 85r / min, put it in a magnetic field for magnetization treatment, and obtain the secondary mixture;

[0041] (4) Put the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of nipples, and particularly relates to a preparation method of a high-toughness silicone nipple. The method concretely comprises the following steps of (1) weighing raw materials according to the parts by weight; (2) mixing liquid silicone rubber, amino silicon oil, gallic acid, Pulullan, sodium caseinate and sodium carboxymethylcellulose, stirring through a stirrer, and freezing in a freezing tank, so as to obtain a primary mixture; (3) mixing the primary mixture, Arabic gum and water, stirring through the stirrer, and magnetizing in a magnetic field, so as to obtain a secondary mixture; (4) putting the second mixture into a vacuum kneading machine, and vacuum kneading, so as to obtain a mixture; (5) injecting the mixture into a mould throughan injection moulding machine, moulding, and cooling, so as to obtain the high-toughness silicone nipple. The tensile strength, the tearing strength, the elongation and the resilience rate of the nipple are effectively improved, so that the nipple has higher toughness, the damage rate and the tearing rate of the nipple are effectively reduced, the service life of the nipple is prolonged, and the nipple is safe, health and reliable to use.

Description

technical field [0001] The invention belongs to the technical field of pacifiers, in particular to a method for preparing a high-toughness silicone pacifier. Background technique [0002] At present, the baby pacifiers on the market are divided into two types according to the material, which are mainly latex and silica gel; latex pacifiers are generally light yellow in color, and the main material is natural latex, which is a soft and extremely elastic material that can resist pulling. It will not accumulate static electricity and is harmless to the environment. However, since latex is a natural material, it may produce rubbery smell, short service life, and easy aging. Inferior latex will produce toxins at high temperatures; silicone pacifiers are made of food-grade silicone This material has a smooth and transparent surface, is non-toxic and tasteless, and can resist drastic changes in ambient temperature and can be boiled, but its toughness is not as good as latex, and it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08L83/08C08L5/00C08L5/02C08L1/28C08K5/13
CPCC08L83/04C08L2205/035C08L83/08C08L5/00C08L5/02C08L1/286C08K5/13
Inventor 庄加松
Owner FENGYANG JIASONG NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products