Preparation and application of a short-chain fluorine-containing copolymer water and oil repellent finishing agent

A water- and oil-repellent, finishing agent technology, used in fiber treatment, liquid repellent fibers, textiles and papermaking, etc., can solve problems such as unfavorable industrial production, poor water- and oil-repellent effect, and poor emulsion stability. Eliminate the problem of bioconcentration, reduce the impact on the environment, the effect of the safety of the production process

Active Publication Date: 2020-02-07
JIANGNAN UNIV
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide the preparation and application of a short-chain fluorine-containing copolymer water-repellent and oil-repellent finishing agent. While imparting excellent water- and oil-repellent properties to the fabric, the finishing agent ensures the original fabric wearability and overcomes the The long carbon chain fluorine-containing compounds in the prior art are difficult to degrade, bioaccumulation, poor emulsion stability, unfavorable to industrial production, environmental pollution and other problems, meet the needs of production or life, and overcome the problems of fluorocarbons in the prior art. When the number of chains is less than 8, the shorter carbon chains cannot be crystallized, the prepared emulsion cannot remain uniform and stable for a long time, and the water and oil repellency effect is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation and application of a short-chain fluorine-containing copolymer water and oil repellent finishing agent
  • Preparation and application of a short-chain fluorine-containing copolymer water and oil repellent finishing agent
  • Preparation and application of a short-chain fluorine-containing copolymer water and oil repellent finishing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] 1) Weighing: Weigh 9.96 g of (perfluorobutyl) ethyl methacrylate, 4.65 g of cetyl methacrylate, and 0.20 g of hydroxyethyl methacrylate, and mix the three monomers evenly. Weigh 0.59g of cationic emulsifier tetradecyltrimethylammonium bromide, 0.36g of nonionic emulsifier (Brij L23), 27g of deionized water, add 0.10g of cetyl alcohol co-emulsifier to emulsifier aqueous solution Afterwards, it was stirred for 15 minutes in a water bath at 50°C.

[0060] 2) Emulsification: drop the monomer mixture into the aqueous emulsifier solution drop by drop, and stir at 50° C. for 30 minutes to obtain a pre-emulsion.

[0061] 3) Fine emulsification: the above-prepared pre-emulsion was stirred on a homogenizer at a speed of 10,000 r / min for 15 min in a water bath at 50° C. to obtain a finely emulsified monomer pre-emulsion.

[0062] 4) Polymerization: The monomer pre-emulsion after fine emulsification is poured into a four-necked flask with a condenser, a thermometer, and an agitato...

Embodiment 2

[0065] 1) Weighing: Weigh (perfluorobutyl) ethyl methacrylate 9.96g, stearyl methacrylate 5.40g, butyl methacrylate 1.07g, hydroxyethyl methacrylate 0.16g, and The four monomers are mixed evenly. Weigh cationic emulsifier cetyltrimethylammonium bromide 0.57g, nonionic emulsifier (Brij L4) 0.57g, deionized water 53g, 0.28g dodecyl mercaptan co-emulsifier is added to emulsifier The aqueous solution was then stirred in a 50 °C water bath for 15 min.

[0066] 2) Emulsification: drop the monomer mixture into the aqueous emulsifier solution drop by drop, and stir at 50° C. for 30 minutes to obtain a pre-emulsion.

[0067] 3) Fine emulsification: the pre-emulsion prepared above was ultrasonicated on an ultrasonic cell pulverizer with a power of 500 W for 15 min in a water bath environment of 50° C. to obtain a finely emulsified monomer pre-emulsion.

[0068] 4) Polymerization: The monomer pre-emulsion after fine emulsification is poured into a four-necked flask with a condenser, a ...

Embodiment 3

[0071] 1) Weighing: Weigh 8.2 g of (perfluorobutyl)(sulfonamide) ethyl acrylate, 9.72 g of stearyl acrylate, and 0.852 g of hydroxyethyl acrylate, and mix the three monomers evenly. Weigh 1.03g of cationic emulsifier octadecyltrimethylammonium bromide, 0.69g of nonionic emulsifier (Brij L20), 80g of deionized water, add 1.72g of cetyl alcohol co-emulsifier to the emulsifier aqueous solution Afterwards, it was stirred for 15 minutes in a water bath at 50°C.

[0072] 2) Emulsification: drop the monomer mixture into the aqueous emulsifier solution drop by drop, and stir at 50° C. for 30 minutes to obtain a pre-emulsion.

[0073] 3) Fine emulsification: the above-prepared pre-emulsion was stirred on a homogenizer at a speed of 10,000 r / min for 15 min in a water bath at 50° C. to obtain a finely emulsified monomer pre-emulsion.

[0074] 4) Polymerization: The monomer pre-emulsion after fine emulsification is poured into a four-necked flask with a condenser, a thermometer, and an a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This paper discloses the preparation and application of a short-chain fluorine-containing copolymer water- and oil-repellent finishing agent. The preparation method of the finishing agent is: take short-chain perfluoroalkyl acrylate, non-fluorine-containing acrylate Cross-linking monomers, the above-mentioned monomers are emulsified under the action of cationic and non-ionic compound emulsifiers, and further finely emulsified in a homogenizer or ultrasonic environment, and finally dripped with a water-soluble initiator to initiate polymerization to prepare short-chain containing Fluorine copolymer miniemulsion, the present invention adopts the miniemulsion polymerization method in the preparation process, does not need to add organic solvent, has guaranteed the stability of the copolymer emulsion, in addition, the present invention utilizes the short-chain fluorine-containing segment with carbon chain number less than 6, While ensuring excellent water and oil repellency, it meets environmental protection requirements.

Description

technical field [0001] The invention relates to the field of functional finishing agents for textiles, in particular to the preparation and application of a short-chain fluorine-containing copolymer water- and oil-repellent finishing agent. Background technique [0002] Fluorine-containing finishing agents are widely used in the field of textile functional finishing because of their excellent water and oil repellency properties. Surface tension works best with -CF 3 group. Among them, due to the good film-forming properties of acrylic polymers, the polymers containing perfluoroalkyl side chains on fluorinated acrylates have the lowest surface tension and are the most widely used. Most of the fluorine-containing water repellents contain perfluoroalkyl (C n f 2n+1 , n≥8), these perfluoroalkyl long carbon chains have excellent water and oil repellency, but the final degradation products are mostly perfluorooctylsulfonyl compounds (PFOS) and perfluorooctanoic acid (PFOA). W...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/24C08F220/18C08F220/20C08F220/38C08F220/32C08F2/28C08F2/30D06M15/277
CPCD06M15/277C08F2/28C08F2/30C08F220/18C08F220/24C08F220/38D06M2200/12D06M2200/11C08F220/387C08F220/1818C08F220/20C08F220/325C08F220/1804
Inventor 王鸿博钱海洪杜金梅傅佳佳王文聪
Owner JIANGNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com