A kind of cellulose triacetate film and polarizer

A technology of cellulose triacetate and cellulose ester, used in optics, polarizing elements, optical elements, etc., to achieve the effect of small fluctuation in appearance performance, improved production efficiency and controllability, and stable performance

Active Publication Date: 2021-02-23
乐凯光电材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in actual production, in order to obtain a dispersion with uniform and stable properties, it is not possible to rely solely on particles with a certain initial particle size.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cellulose triacetate film and polarizer
  • A kind of cellulose triacetate film and polarizer
  • A kind of cellulose triacetate film and polarizer

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] The preparation of cellulose triacetate film, including the steps of preparation of cotton glue solution, casting, drying and winding, will be described in detail below with reference to the accompanying drawings.

[0028] 1. If figure 1 Proceed to the preparation of the cotton glue solution as indicated.

[0029] Mix and dissolve

[0030] The accurately weighed organic solvent is prepared as a mixed solvent and sent to the mixing kettle 1. Mixed solvent comprises one or more in methylene chloride and methyl alcohol, ethanol, acetone, the mixed solvent of preferred methylene chloride and methyl alcohol of the present invention, the amount of mixed solvent is preferably accounted for 70-85% of cotton glue solution 27, further Preferably dichloromethane:methanol is 90:10.

[0031] Then, the cellulose triacetate particles are put into the mixing tank 1 , the amount of the cellulose triacetate particles is preferably 10-20% of the cotton gum solution 27 .

[0032] Then,...

Embodiment 1

[0063] Such as figure 1 As shown, in the mixing tank 1, 70% by weight of mixed solvent, 20% by weight of cellulose triacetate particles, 7% by weight of TPP and BDP plasticizer mixture, 2.99% by weight of UV928 and UV329 UV absorber mixture. Stir the above mixture at a constant speed for 20 minutes to obtain the initially dissolved cotton glue solution 2, heat the cotton glue solution 2 at 80°C and pressurize at 0.5MPa for 10 minutes, drop to normal temperature and pressure and continue to dissolve for 20 minutes. The control temperature of the cotton glue solution 2 transported by the pipeline 9 is 32° C., and the temperature difference is 0-0.5° C. The cotton glue solution 2 is filtered three times and then enters the thermostat 15 to stand still for defoaming, and then transported to the front end of the casting nozzle 28 to be mixed with the matting agent dispersion 17.

[0064] Such as figure 2 As shown, a small amount of cotton glue solution 2 and a mixed solvent are...

Embodiment 2

[0067] The TAC film preparation process is as in implementation 1, the difference is that in the mixing tank 1, drop into 75% by weight of the mixed solvent, drop into 15% by weight of cellulose triacetate particles, 5.95% by weight of TPP and BDP for plasticization Agent mixture, 4% by weight of UV928 and UV329 UV absorber mixture. Heat the initially dissolved cotton glue solution 2 at 90° C. and pressurize at 0.3 MPa for 20 minutes. The temperature of the cotton glue solution 2 in the delivery pipeline 9 is controlled to be 34°C, and the temperature difference is 0-0.3°C.

[0068] The specific surface area is 110m 2 / g of R972 is added to the diluted cotton glue solution to make dispersion 17, and is sent to dispersion device 21 (sand mill), and the matting agent in dispersion 17 is dispersed into an average particle diameter of 0.6 micron, and the dispersion The liquid a filter 23 filters the dispersion liquid 17, and the particles of the dispersion liquid matte agent with...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

A kind of cellulose triacetate film, during preparation, firstly carry out preparation of cotton glue solution, put mixed solvent, triacetate cellulose ester, additive into mixing kettle and carry out mixing and stirring and heat and pressurize, the cotton glue solution in conveying Perform temperature control and filtration, mix the dispersed matting agent with the cotton glue solution evenly, then perform casting, drying and winding to prepare a cellulose triacetate film, heat the cotton glue solution in the mixing tank for 80 -100°C, pressurize 0.2-0.5MPa, time 20-30 minutes; control the temperature of the cotton glue solution in the delivery pipeline to 32°C-36°C, and the temperature difference is 0-1.0°C. By controlling the average particle size and quantity distribution of matting agent particles, the present invention avoids the point-like disadvantages caused by adding large particles into the TAC film; the performance of the dispersion is more stable, and the average particle size stability time is extended from 1 day to more than 50 days, avoiding The deterioration of the dispersion caused by long-term parking is eliminated.

Description

technical field [0001] The invention relates to a film, in particular to a cellulose triacetate film with excellent appearance, good lubricity and anti-blocking performance between films, and a polarizer for liquid crystal display made of the film. Background technique [0002] Cellulose acetate with an average degree of esterification of 57.5-62.5% is generally called triacetate cellulose, and the triacetate cellulose film (hereinafter referred to as TAC film) made of it is used as a photosensitive material because of its strength and flame retardancy. support body. At the same time, due to the excellent optical isotropy of TAC film, this film is suitable for polarizer protective film or anti-glare film for liquid crystal display, anti-reflection film, phase difference film and other functional films and their base films. The market is expanding rapidly. . [0003] The preparation of TAC film usually adopts the solution casting method, that is, the partially hydrolyzed ce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J5/18C08L1/12G02B1/04G02B5/30
CPCC08J5/18C08J2301/12G02B1/04G02B5/30
Inventor 谢芸刘世军王力任孙晓龙
Owner 乐凯光电材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com