High-performance alloy steel flanges and forgings and manufacturing method thereof

An alloy steel, high-performance technology, applied in the field of alloy steel forging, can solve the problems that cannot meet the performance requirements of alloy steel flanges and forgings, achieve the effect of less internal defects, reduce harmful elements, and guarantee performance requirements

Active Publication Date: 2018-08-03
无锡市法兰锻造有限公司
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem mainly solved by the present invention is that it cannot meet the performance requirements of alloy steel flanges and forgings for oil and gas pipeline projects and nuclear power projects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance alloy steel flanges and forgings and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Embodiment 1: Make a φ900×120mm flange cover, made of 15CrMo alloy steel.

[0043] Acceptance requirements: Rm 480~640MPa, Rp0.2≥280MPa, A≥20%, where A represents the growth rate, and when the impact test is performed at -20°C, the impact energy is not less than 100J; the austenite grain size is ≥7 ; According to NB / T47013 for magnetic particle testing and ultrasonic testing, level 1 qualified.

[0044] The specific process flow is:

[0045] Raw material smelting→cutting→forging→heat treatment→sampling→performance testing→nondestructive testing→machining→finished products.

[0046] 1.05 tons of steel ingots were used as raw materials, and 15% of the riser end of the ingot and 5% of the nozzle end were cut off, and then the steel ingot was smelted. The specific smelting method was electric furnace smelting + refining outside the furnace + vacuum degassing. The chemical composition of the steel ingot is shown in Table 1;

[0047] Table 1 Chemical Composition %

[0048]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
crystal sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of alloy steel forging and discloses high-performance alloy steel flanges and forgings and a manufacturing method thereof. Alloy steel comprises the components of, by weight, 0.14%-0.17% of carbon, 0.10%-0.60% of silicon, 0.60%-0.80% of manganese, 0-0.005% of phosphorus, 0-0.003% of sulfur, 1.00%-1.25% of chromium, 0.55%-0.65% of molybdenum, and the balance iron. The forgings produced through the manufacturing process are excellent in performance, the performance index of the forgings far exceeds that of forgings produced through a traditional process, and the defect number and size found in forging nondestructive testing are also far superior to those of the traditional process.

Description

technical field [0001] The invention relates to the technical field of alloy steel forging, in particular to a high-performance alloy steel flange, a forging and a manufacturing method thereof. Background technique [0002] Alloy steel flanges and forgings are widely used in machinery, electric power, petroleum, chemical industry, metallurgy and other fields. Usually, the performance of alloy steel flanges and forgings can meet the relevant standards, but in recent years, with the advancement of technology Accelerated, the performance index design requirements of flanges and forgings used in many projects greatly exceed the requirements of national standards and industry standards, and the technical conditions of customers' orders are significantly higher than these standards. [0003] In the NB / T47008 standard, the chemical composition of 15CrMo is C 0.12%~0.18%, Si 0.10%~0.60%, Mn 0.30%~0.80%, P≤0.025%, S≤0.010%, Cr 0.80%~1.25%, Mo 0.45% to 0.65%, and the rest is Fe eleme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/22C22C33/06C21D1/18B21J5/00
Inventor 石宏亮
Owner 无锡市法兰锻造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com