A technology of epoxy resin and flame retardancy, applied in the field of epoxy resin composition and its synthesis, to achieve good processability and processability, excellent flame retardancy and flame retardancy durability, electrical properties and reliability. Effect

Active Publication Date: 2020-06-12
吴先锋
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Boron-based flame retardants are also divided into two categories: additive type and reactive type. Zinc borate is a representative of additive type flame retardants and is widely used, but it also has the defects of additive type flame retardants.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of epoxy resin composition with excellent flame retardancy and flame retardancy durability and preparation method thereof
  • A kind of epoxy resin composition with excellent flame retardancy and flame retardancy durability and preparation method thereof
  • A kind of epoxy resin composition with excellent flame retardancy and flame retardancy durability and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A preparation method of an epoxy resin composition with excellent flame retardancy and flame-retardant durability is as follows:

[0040] Premix epoxy resin, self-made N-B synergistic high flame retardant curing agent (A), other curing agents, curing accelerators and inorganic fillers according to the ratio of parts by mass. The premixing time is 3 to 10 minutes, and the speed is 600 ~1200r / min; melt extrusion mixing, extruder temperature 80~160°C, extruder speed 800~2400r / min, tablet cooling and crushing, crushing and sieving through ACM mill to obtain the epoxy resin combination.

[0041] Wherein, the synthetic method of N-B synergistic high flame retardant curing agent (A):

[0042] (1) After finishing the four-neck flask, stirrer, distillation column, condenser tube and temperature-controlled heating mantle, add 120g of neopentyl glycol and 168.21g of 1,3-dimethylol-5,5-dimethylhydantoin, and raise the temperature To 110~130℃, stirring and melting;

[0043] (2) A...

Embodiment 2

[0049] A preparation method of an epoxy resin composition with excellent flame retardancy and flame-retardant durability is as follows:

[0050] Premix epoxy resin, self-made N-B synergistic high flame retardant curing agent (B), other curing agents, curing accelerators and inorganic fillers according to the ratio of parts by mass. The premixing time is 3 to 10 minutes, and the speed is 600 ~1200r / min; melt extrusion mixing, extruder temperature 80~160°C, extruder speed 800~2400r / min, tablet cooling and crushing, crushing and sieving through ACM mill to obtain the epoxy resin combination.

[0051] Wherein, the synthetic method of N-B synergistic high flame retardant curing agent (B):

[0052] (1) After finishing the four-neck flask, stirrer, distillation column, condenser tube and temperature-controlled heating mantle, add 105g of neopentyl glycol and 184.33g of 1,3-dimethylol-5,5-dimethylhydantoin, and raise the temperature To 110~130℃, stirring and melting;

[0053] (2) A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
epoxy valueaaaaaaaaaa
acid valueaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to an epoxy resin composition with the excellent flame resistance and flame resistant durability and a preparation method thereof. The epoxy resin composition is powdery, and prepared from the components, in parts by mass: 24-40 parts of epoxy resin, 10-26 parts of self-made N-B synergistic high flame resistance curing agent, 0-6 parts of other curing agent, 0.02-0.6 part ofcuring accelerator, 15-30 parts of flame resistant synergist and 20-35 parts of organic filler. The epoxy resin composition adopts nitrogen and boron to resist flame synergistically, the flame resistant elements are all located on the molecular chain, thus flame resistance, free of halogen and free of phosphate of an electronic packaging material are achieved, and the electronic packaging materialis endowed with the outstanding flame resistant durability. The epoxy resin composition has the multi-branched structure, and the machinability, the using manufacturability, the physical and chemicalproperty, the electrical property and the reliability of the electronic packaging material can be effectively considered.

Description

technical field [0001] The invention belongs to the field of electronic packaging materials, in particular to an epoxy resin composition which can be used in electronic packaging materials and has excellent flame retardancy and durability and a synthesis method thereof. Background technique [0002] Epoxy resin refers to a polymer containing two or more epoxy groups, with aliphatic, alicyclic or aromatic organic compounds as the backbone and formed by the reaction of epoxy groups; epoxy groups can be located in the molecular chain The end, middle or ring structure of the segment; it is one of the most widely used matrix resins in polymer matrix composites. Due to the special molecular structure of epoxy resin, epoxy resin has excellent adhesion, heat resistance, chemical resistance and excellent electrical insulation properties, and is easy to process, low shrinkage, small linear expansion coefficient and low cost. Advantages such as low cost. Widely used in the packaging ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L63/00C08K3/36C08K3/34C08K3/26C08K3/30C08K3/22C08K3/38C08G59/42C08G59/40
CPCC08G59/4071C08G59/4078C08G59/4284C08K3/22C08K3/26C08K3/30C08K3/34C08K3/36C08K3/38C08K2003/2224C08K2003/2227C08K2003/265C08K2003/3045C08K2003/387C08L2201/02C08L2201/22C08L63/00
Inventor 吴先锋
Owner 吴先锋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap