A kind of durable and antibacterial easy-to-dye hydrophilic polyester fiber fabric and preparation method thereof

A polyester fiber and hydrophilic technology, applied in the field of polyester fiber fabrics, can solve problems such as single performance, and achieve the effects of improving antistatic and antifouling properties, easy dyeing, and improving hydrophilicity

Active Publication Date: 2019-12-27
义乌市大宇袜业股份有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the performance of the above two is single

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of durable and antibacterial easy-to-dye hydrophilic polyester fiber fabric and preparation method thereof
  • A kind of durable and antibacterial easy-to-dye hydrophilic polyester fiber fabric and preparation method thereof
  • A kind of durable and antibacterial easy-to-dye hydrophilic polyester fiber fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A durable and antibacterial easy-to-dye hydrophilic polyester fiber fabric, using double quaternary ammonium salt modified monomers as hydrophilic and antibacterial monomers, the polyester fiber molecular main chain contains a large number of quaternary ammonium salt groups; using 1, 4-dihydroxybutane-2-sodium sulfonate is an easily dyeable anion-modified monomer, and the sulfonate anion group is located on the branched chain of polyester fiber; its preparation method, in parts by weight, comprises the following steps:

[0024] In a reactor equipped with a stirrer and a heating device, 22 parts of diquaternary ammonium salt modified diol monomer, 27 parts of ethylene glycol, 148 parts of terephthalic acid, 0.3 part of antimony trioxide, 0.02 Add trimethyl phosphate and 0.015 part of BASF antioxidant 1010 into the reactor, stir and beat at room temperature, heat to 240°C after beating, and react for 2.5 hours; then add 2.5 parts of 1,4-dihydroxybutyrate into the reactor ...

Embodiment 2

[0028] A durable and antibacterial easy-to-dye hydrophilic polyester fiber fabric, using double quaternary ammonium salt modified monomers as hydrophilic and antibacterial monomers, the polyester fiber molecular main chain contains a large number of quaternary ammonium salt groups; using 1, 4-dihydroxybutane-2-sodium sulfonate is an easily dyeable anion-modified monomer, and the sulfonate anion group is located on the branched chain of polyester fiber; its preparation method, in parts by weight, comprises the following steps:

[0029] In a reactor equipped with a stirrer and a heating device, 25 parts of diquaternary ammonium salt modified diol monomers, 25 parts of ethylene glycol, 150 parts of terephthalic acid, 0.5 parts of titanium glycol, 0.03 Add one part of tris(nonylphenyl)phosphite and 0.03 part of tris(2,4-di-tert-butylphenyl)phosphite into the reactor, stir and beat at room temperature, heat to 250°C after beating, and react for 2h ; Then add 3 parts of 1,4-dihydrox...

Embodiment 3

[0033] A durable and antibacterial easy-to-dye hydrophilic polyester fiber fabric, using double quaternary ammonium salt modified monomers as hydrophilic and antibacterial monomers, the polyester fiber molecular main chain contains a large number of quaternary ammonium salt groups; using 1, 4-dihydroxybutane-2-sodium sulfonate is an easily dyeable anion-modified monomer, and the sulfonate anion group is located on the branched chain of polyester fiber; its preparation method, in parts by weight, comprises the following steps:

[0034]In a reactor equipped with a stirrer and a heating device, 20 parts of diquaternary ammonium salt modified diol monomer, 28 parts of ethylene glycol, 130 parts of terephthalic acid, 0.1 part of antimony acetate, 0.01 part of phosphoric acid Add trimethyl ester and 0.01 part of tris(2,4-di-tert-butylphenyl) phosphite into the reactor, stir and beat at room temperature, heat to 230°C after beating, and react for 3 hours; then add 1.5 parts of 1,4-di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to durable antibacterial easy-to-dye hydrophilic polyester fiber fabric and belongs to the technical field of polyester fiber fabrics. Biquaternary ammonium salt modified monomers are used as hydrophilic antibacterial monomers, and a main chain of a polyester fiber contains a large number of quaternary ammonium salt groups; sodium 1,4-dihydroxybutane-2-sulfonate is used as aneasy-to-dye anion modified monomer, and sulfonate anion groups are located on a branch chain of the polyester fiber. The polyester fiber fabric disclosed by the invention is easy to dye, has the comprehensive effects of hydrophilicity, antistatic property and lasting antibacterial property, and has a wide application prospect.

Description

technical field [0001] The invention belongs to the technical field of polyester fiber fabrics, and relates to a durable and antibacterial easy-to-dye hydrophilic polyester fabric and a preparation method thereof. Background technique [0002] Polyester fiber is a synthetic fiber obtained by spinning polyester obtained by polycondensation of organic dibasic acid and dibasic alcohol. The polyester fiber produced in large quantities in industrialization is made of polyethylene terephthalate, and the trade name in China is polyester. Polyester fiber has the advantages of high strength, high modulus, good elasticity and light resistance, good dimensional stability, easy washing and quick drying, etc., and is a relatively popular textile material. [0003] However, due to the regular arrangement of the molecular structure of the polyester itself, high crystallinity, large modulus, and lack of polar functional groups, the hygroscopicity of the fiber is very poor. The moisture reg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04B1/16D04B21/00D01F1/10D01F6/92C08G63/685C08G63/688