All-solid-state lithium battery and preparation method thereof

A lithium battery, all-solid-state technology, used in the manufacture of electrolyte batteries, secondary batteries, non-aqueous electrolyte batteries, etc., can solve the problems of mutual diffusion of elements and large interface impedance.

Active Publication Date: 2018-09-07
BYD CO LTD
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present disclosure is to provide an all-solid-state lithium battery and its preparation method, which can solve the problems of large interface impedance between the positive electrode and the solid-state electrolyte and interdiffusion of elements during the cycle in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] The preparation method of the present disclosure can uniformly modify the surface of the positive electrode material to obtain a positive electrode active material whose surface is coated with a fluorine-containing lithium titanate layer with a controllable thickness. When the positive electrode active material is used in an all-solid lithium battery, the positive electrode can be avoided The interfacial reaction or element diffusion occurs between the material and the solid electrolyte to reduce the interfacial impedance.

[0039] In addition to the preparation method of the present disclosure, methods such as chemical vapor deposition, chemical vapor transport or vacuum laser sputtering can also be used to prepare the positive electrode active material coated with a lithium fluoride titanate layer, but the cost of the above method is very high. However, when the preparation method described in the present disclosure is adopted, a fluorine-containing lithium titanate la...

Embodiment 1

[0063] (1) Contains F-Li 4 Ti 5 o 12 Preparation of positive electrode active material for layer

[0064] 100 g (grams) of positive electrode active material LiCoO 2 , 12 g of TiF 4 Mixed with 2 g of anhydrous LiOH evenly, and added to 500 mL of ethanol for stirring, the stirring time was 2 h, evaporated to dryness at 70 °C, the obtained precursor was fully ground and sintered at 700 °C at high temperature, the obtained The final product is F-Li 4 Ti 5 o 12 Material coated LiCoO 2 Cathode material.

[0065] (2) Preparation of positive electrode sheet C

[0066] 930g containing F-Li 4 Ti 5 o 12 Material coated LiCoO 2 Anode material (93%), 30 g binder PVDF (3%), 20 g acetylene black (2%), 20 g conductive agent carbon fiber (2%) were added to 1500 g solvent NMP (nitrogen methylpyrrolidone), Then stir in a vacuum mixer to form a stable and uniform cathode slurry. The positive electrode slurry was uniformly and intermittently coated on both sides of aluminum foil (a...

Embodiment 2

[0074] The electrolyte and lithium-ion battery of this example are prepared by the method in Example 1, the difference is that in step (1), the TiF 4 The amount of anhydrous LiOH was changed to 6 g and 1 g respectively, and other steps and operations were the same. The all-solid-state lithium battery CEA2 of this embodiment was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to an all-solid-state lithium battery and a preparation method thereof. The all-solid-state lithium battery comprises a positive plate, a negative plate and a solid electrolyte layer, wherein the positive plate comprises a positive active substance, and the positive active substance comprises positive material particles and a fluorine-containing lithium titanate layer coatingthe surfaces of the positive material particles. According to the method for preparing the positive active substance with a positive material coated by the fluorine-containing lithium titanate layerfrom the positive material, titanium tetrafluoride and a lithium salt through mixing and sintering, the surface of the positive material can be uniformly modified so as to obtain the positive materialwith controllable fluorine content and fluorine-containing lithium titanate layer thickness on its surface. When the positive material is used in the all-solid lithium battery, the structure of a coating can be stabilized, interfacial reaction or element diffusion between the positive material and the solid electrolyte can be avoided, and interface impedance is reduced.

Description

technical field [0001] The present disclosure relates to the field of solid-state lithium batteries, in particular, to an all-solid-state lithium battery and a preparation method thereof. Background technique [0002] Due to the serious interface effect between the positive electrode material and the solid-state electrolyte and the element diffusion problem at the interface of the all-solid-state lithium battery, the interface impedance between the positive electrode and the solid-state electrolyte is greatly increased, which greatly affects the performance of the battery. In the technology, the above-mentioned technical problems are usually solved by coating the surface of the positive electrode material, wherein the coating is usually an oxide, a lithium-containing transition metal oxide, or a fluoride. The cathode material is usually LiNbO 3 , LiTaO 3 , Li 4 Ti 5 o 12 、Al 2 o 3 、BaF 2 or CaF 2 etc., where for LiNbO 3 The cathode material for surface coating is t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/0525H01M10/058
CPCH01M10/0525H01M10/058Y02E60/10Y02P70/50
Inventor 历彪郭姿珠宋威易观贵谢静
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap