A production method and tile technology, applied in the field of tiles, can solve problems such as poor reflection effect, single layering, and poor air permeability, and achieve the effects of environmental protection, layering, and air permeability

Inactive Publication Date: 2018-09-21
福建省南安市荣达建材有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing tiles have poor air permeability, poor reflective effect, single layering, simple functions, and no unique fragrance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Breathable tile production method
  • Breathable tile production method
  • Breathable tile production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A production method of breathing tiles, characterized in that: comprising the following steps,

[0034] (1) Raw materials are crushed, and the collected porcelain stone china clay is put into a jaw crusher for crushing after preliminary removal of impurities. The crushing time should be 3 hours. After crushing, add water and pour it into a ball mill. The ball milling time should be 12 hours;

[0035] (2) To make powder, pour the mixture of ball-milled porcelain stone particles and water into the mixer, add material and color materials continuously during the mixing process until the mixing is complete, then pour it into the spray dryer, and get the powder after spray drying. material;

[0036] (3) To make brick embryos, mix the straw balls into the powder and pour them into the tile mold, and use a press to press them into brick embryos;

[0037] (4) Lay a reflective layer, lay a dotted tile coagulant in the middle of the surface of the brick embryo, and fix microprism...

Embodiment 2

[0055] A production method of breathing tiles, comprising the following steps,

[0056] (1) Raw materials are crushed, and the collected porcelain stone china clay is put into a jaw crusher for crushing after preliminary removal of impurities. The crushing time should be 3 hours. After crushing, add water and pour it into a ball mill. The ball milling time should be 12 hours;

[0057] (2) To make powder, pour the mixture of ball-milled porcelain stone particles and water into the mixer, add material and color materials continuously during the mixing process until the mixing is complete, then pour it into the spray dryer, and get the powder after spray drying. material;

[0058] (3) To make brick embryos, mix the straw balls into the powder and pour them into the tile mold, and use a press to press them into brick embryos;

[0059] (4), pave the reflective layer, lay a dotted tile coagulant at the middle position above the surface of the brick embryo, fix the microprism above ...

Embodiment 3

[0077] A production method of breathing tiles, comprising the following steps,

[0078] (1) Raw materials are crushed, and the collected porcelain stone china clay is put into a jaw crusher for crushing after preliminary removal of impurities. The crushing time should be 3 hours. After crushing, add water and pour it into a ball mill. The ball milling time should be 12 hours;

[0079] (2) To make powder, pour the mixture of ball-milled porcelain stone particles and water into the mixer, add material and color materials continuously during the mixing process until the mixing is complete, then pour it into the spray dryer, and get the powder after spray drying. material;

[0080] (3) To make brick embryos, mix the straw balls into the powder and pour them into the tile mold, and use a press to press them into brick embryos;

[0081] (4), pave the reflective layer, lay a dotted tile coagulant in the middle position above the surface of the brick embryo, fix the microprism above ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a breathable tile production method and relates to the technical field of tiles. The breathable tile production method includes the steps of smashing raw materials; making a powdery material; making tile blanks, wherein straw balls are mixed into the powdery material, then the mixture is poured into tile molds, and a pressing machine is used for pressing the mixture into the tile blanks; laying reflecting layers, wherein a dotted tile coagulant is laid in the middle of the upper portion of each tile blank surface layer, 3-5 microprisms are fixed above the tile coagulant, and the pressing machine is adopted for pressing the tile blank surface layers flat; conducting drying and glazing, wherein a bell jar type sprinkling mode is adopted for glazing the tile blanks; conducting firing; conducting polishing for preservation. The breathable tile is prepared from, by weight, 100-120 parts of china stone and clay, 2-8 parts of straw balls, 300-350 parts of water, 4-10 parts of tile coagulant, 2-6 parts of microprisms and 10-20 parts of glaze. The breathable tile has great breathability, a comfortable reflecting effect, diversified gradations, a unique flavor and a great mosquito repelling effect.

Description

technical field [0001] The invention relates to the technical field of tiles, in particular to a method for producing breathing tiles. Background technique [0002] Ceramic tiles are refractory metal oxides and semi-metal oxides, which are formed through the process of grinding, mixing, pressing, glazing and sintering, and are an acid and alkali resistant porcelain or stone construction or decoration material. It is generally called tiles, and its raw materials are mostly mixed with clay, quartz sand, etc. Before 4000 BC, tiles were also found in Mesopotamia. This kind of tiles are decorated with blue and white stripes. purpose, later appeared more styles and colors, China is the center of ceramic art, as early as Shang Yin period (1523-1028 BC), China produced a kind of exquisite white stoneware, which used Chinese Early glazes were used for whitewashing, and the decorative effect of tiles has increased over the centuries with the improvement of tile production methods, fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B38/06C04B35/16C04B35/622C04B35/632C04B35/63
CPCC04B35/16C04B35/622C04B35/6303C04B35/632C04B38/0675
Inventor 蔡荣法
Owner 福建省南安市荣达建材有限公司