Modified glass bead thermal insulation mortar and preparation method thereof

A technology of glass microspheres and thermal insulation mortar, which is applied in the field of building materials, can solve the problems of vitrified microspheres being easily broken, and achieve the effects of strengthening hollow glass microspheres, good water retention and construction performance, and reducing water absorption

Pending Publication Date: 2018-09-28
芜湖市颂晖商贸有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a modified glass microbead thermal insulation mortar and a preparation method thereof, which solves the problem that the vitrified microspheres in the existing thermal insulation mortar are easily broken

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] This embodiment provides a modified glass bead insulation mortar, which is made of the following raw materials in parts by weight: 40 parts of Portland cement, 8 parts of quartz sand, 12 parts of kaolin, 25 parts of hollow glass beads, blast furnace slag 2.5 parts, 2.5 parts of styrene-acrylic emulsion, 5 parts of hydroxypropyl methylcellulose, 4 parts of polypropylene staple fiber, 4 parts of polyvinyl alcohol, and 4 parts of potassium dihydrogen phosphate.

[0021] The preparation method of the modified glass bead thermal insulation mortar in this embodiment comprises the following steps:

[0022] (1) Take blast furnace slag, grind it into 200-mesh fine powder, put it into a high-speed shearing machine with styrene-acrylic emulsion, then add water equivalent to the weight of inorganic mineral powder and styrene-acrylic emulsion, and stir and mix at 7000r / min for 35min to obtain The mixture is sprayed on the surface of the hollow glass microspheres by a thermal atomiza...

Embodiment 2

[0025] This embodiment provides a modified glass microsphere insulation mortar, which is made of the following raw materials in parts by weight: 30 parts of Portland cement, 10 parts of quartz sand, 10 parts of kaolin, 30 parts of hollow glass microspheres, blast furnace slag 2 parts, 3 parts of styrene-acrylic emulsion, 4 parts of hydroxypropyl methylcellulose, 5 parts of polypropylene staple fiber, 3 parts of polyvinyl alcohol, 5 parts of potassium dihydrogen phosphate.

[0026] The preparation method of the modified glass bead thermal insulation mortar in this embodiment comprises the following steps:

[0027] (1) Take blast furnace slag, grind it into 100-mesh fine powder, add styrene-acrylic emulsion to a high-speed shearing machine, then add water equivalent to the weight of inorganic mineral powder and styrene-acrylic emulsion, and stir and mix at 8000r / min for 30min to obtain The mixture is sprayed on the surface of the hollow glass microspheres by a thermal atomizatio...

Embodiment 3

[0030] This embodiment provides a kind of modified glass microsphere insulation mortar, which is made of the following raw materials in parts by weight: 50 parts of Portland cement, 5 parts of quartz sand, 15 parts of kaolin, 20 parts of hollow glass microspheres, 3 parts of phosphorus slag 2 parts, 2 parts of styrene-acrylic emulsion, 6 parts of hydroxypropyl methylcellulose, 3 parts of polypropylene staple fiber, 5 parts of polyvinyl alcohol, 3 parts of potassium dihydrogen phosphate.

[0031] The preparation method of the modified glass bead thermal insulation mortar in this embodiment comprises the following steps:

[0032] (1) Take phosphorus slag, grind it into 200-mesh fine powder, add styrene-acrylic emulsion to a high-speed shearing machine, then add water equivalent to the weight of inorganic mineral powder and styrene-acrylic emulsion, and stir and mix at 6000r / min for 40min to obtain a mixture , using thermal atomization spraying method to spray on the surface of h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Bond strengthaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses modified glass bead thermal insulation mortar and a preparation method thereof and belongs to the technical field of building materials. The mortar is prepared from 30-50 partsof portland cement, 5-10 parts of quartz sand, 10-15 parts of kaolin, 20-30 parts of hollow glass beads, 2-3 parts of inorganic mineral powder, 2-3 parts of styrene acrylic emulsion, 4-6 parts of hydroxypropyl methyl cellulose, 3-5 parts of polypropylene short fibers, 3-5 parts of polyvinyl alcohol and 3-5 parts of mono potassium phosphate. According to the modified glass bead thermal insulationmortar, after the glass beads are modified, film with high adhesive strength is formed on the surfaces of the hollow glass beads and has the effects of blocking the hollow glass beads and sealing theincomplete glass beads, the smashing rate of the glass beads is lowered, and accordingly the water absorption rate is lowered. Meanwhile, the polymer film on the surfaces of the hollow glass beads hascertain strength and toughness and has the effect of strengthening the hollow glass beads.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a modified glass bead thermal insulation mortar and a preparation method thereof. Background technique [0002] Building thermal insulation mortar reduces building energy consumption by improving the thermal insulation performance of buildings, which is the most basic way to achieve building energy conservation. Insulation mortar is a kind of ready-mixed dry powder mortar made of various light materials as aggregate, cement as cement, mixed with some modified additives, and mixed by the production enterprise. It is mainly used to construct building surface insulation As a kind of building material, it has excellent properties such as thermal insulation, flame retardant, water resistance and weather resistance, and has a wide market demand. [0003] Compared with organic wall insulation materials, vitrified microbead thermal insulation mortar has the advantages of good...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B20/10
Inventor 汪琦郭元
Owner 芜湖市颂晖商贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com