Method for improving selectivity of citronellol synthesized through citronellal hydrogenation

A technology for citronellol and citronellal, which is applied in the field of improving the selectivity of citronellal hydrogenation to synthesize citronellol, can solve the problems of cumbersome process and low selectivity, and achieves improved selectivity, mild catalytic conditions, high efficiency and high efficiency. high yield effect

Active Publication Date: 2018-10-02
NANJING UNIV OF TECH
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the traditional preparation methods often have

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving selectivity of citronellol synthesized through citronellal hydrogenation
  • Method for improving selectivity of citronellol synthesized through citronellal hydrogenation
  • Method for improving selectivity of citronellol synthesized through citronellal hydrogenation

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0033] Example 1:

[0034] Preparation of Pt@ZIF-67 catalyst

[0035] Under normal temperature and pressure, 32.84mg 2-methylimidazole, 58.205mg Co(NO 3 ) 2 ·6H 2 O and 0.3 mL of a methanol solution of about 3 nm of Pt nanoparticles dispersed by pvp were mixed and allowed to stand at room temperature for 24 hours, and the obtained precipitate was washed, centrifuged, and dried to obtain Pt@ZIF-67. Among them, pvp dispersed about Pt nanoparticles such as figure 1 As shown, the XRD diagram of Pt@ZIF-67 is as figure 2 As shown, the TEM image of Pt@ZIF-67 is as image 3 Shown.

[0036] Pt@ZIF-67 as a catalyst for catalytic reaction

[0037] Weigh the Pt@ZIF-67 catalyst in a vacuum oven at 120℃ for 10 hours to activate it. Put 15 mg of the activated Pt@ZIF-67 catalyst in a polytetrafluoroethylene liner, add 15 mL of methanol as a solvent, and ultrasound for 10 minutes to disperse the catalyst. Evenly; then add 100μL of citronellal and a magnetic stirrer, assemble the autoclave and put i...

Example Embodiment

[0038] Example 2:

[0039] Preparation of Pd@ZIF-67 catalyst

[0040] The preparation method of the Pd@ZIF-67 catalyst is the same as in Example 1, except that the Pt nanoparticles are replaced with Pd nanoparticles.

[0041] Weigh the Pt@ZIF-67 catalyst in a vacuum oven at 100°C for 12 hours for activation. Weigh 15 mg of the activated Pd@ZIF-67 catalyst into a polytetrafluoroethylene liner, add 15 mL of methanol as a solvent, and ultrasound for 10 minutes The catalyst is evenly dispersed; then 100μL of citronellal and a magnetic stirrer are added, the autoclave is assembled and hydrogen is introduced. The reaction conditions were set as follows: hydrogen pressure 0.1MPa, temperature 150°C, stirring speed 800rpm, reaction time 10h. Using GC to detect citronellal and its hydrogenated products, the result is: the conversion rate is about 85%, the selectivity of the main product citronellol> 90%.

Example Embodiment

[0042] Example 3:

[0043] Preparation of Pt@ZIF-8 catalyst

[0044] Under normal temperature and pressure, add 15mL 2-methylimidazole (25mM), 15mL Co(NO 3 ) 2 ·6H 2 O (25 mM) and 1 mL of pvp dispersed methanol solution of about 1 nm of Pt nanoparticles were mixed and allowed to stand for 24 hours at room temperature. The resulting precipitate was washed, centrifuged, and dried to obtain Pt@ZIF-8.

[0045] Among them, the SEM picture of Pt@ZIF-8 is as Figure 4 As shown, the TEM picture of Pt@ZIF-8 is as Figure 5 As shown, it can be seen from the data that Pt is evenly wrapped into MOFs, and different kinds of catalysts with good performance are obtained.

[0046] Pt@ZIF-8 as a catalyst for catalytic reaction

[0047] Weigh the Pt@ZIF-8 catalyst in a vacuum oven at 110°C for 11 hours to activate it, weigh 15 mg of the activated Pt@ZIF-8 catalyst into a polytetrafluoroethylene liner, add 15 mL of methanol as a solvent, and ultrasound for 10 min. The catalyst is evenly dispersed; then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for improving selectivity of citronellol synthesized through citronellal hydrogenation. The method comprises the following steps: taking metal nano-particle @MOFs as acatalyst, performing activating treatment, and catalyzing selective hydrogenation of citronellal to produce citronellol accompanying with stirring and heating under the conditions of a hydrogen atmosphere and a pressure of 0.1-1MPa. Compared with the traditional catalytic reaction process, the method disclosed by the invention is mild in catalytic conditions and high in efficiency and yield, andhas high selectivity of the principal product citronellol. Moreover, according to the method, the nanoscale metal nano-particles are coated in the MOFs, and due to a protective effect of the MOFs structure, the metal nano-particles do not agglomerate and re-grow in the reaction process, so that the continuous high efficiency and stability of the catalyst are ensured.

Description

technical field [0001] The invention relates to the technical field of MOFs composite materials and catalysts, in particular to a method for improving the selectivity of citronellal hydrogenation to synthesize citronellol. Background technique [0002] Citronellal is a very important raw material for the preparation of various fine chemicals. The carbonyl group in the citronellal structure is selectively hydrogenated to generate the unsaturated alcohol-citronellol, which is widely used in perfume. Citronellol has a wide range of uses. It is a very important spice with a fresh rose aroma. It is usually blended with floral fragrances such as geraniol and phenylethyl alcohol, and can be used to manufacture hydroxydihydrocitronellol, hydroxy The raw material of dihydrocitronellal; it is also used in the preparation of soaps, room fresheners, etc.; citronellol can also be used in food flavors, such as soft drinks, baked goods, sugar, jelly and pudding. Citronellol, one of the r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C07C29/141C07C33/025B01J31/22
CPCB01J31/1691B01J31/1815B01J31/2239B01J35/006B01J35/0073B01J2231/645B01J2531/26B01J2531/845C07C29/141C07C33/025
Inventor 霍峰蔚张伟娜张文垒姬文兰褚慧敏张所瀛房传真孟凡辰
Owner NANJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap