Reflective thermal insulation coating

A reflective heat-insulating coating and heat-reflective technology, applied in the direction of reflection/signal coatings, coatings, etc., can solve the problems of high price, great influence on construction and heat insulation effects, and insufficient paint film, so as to solve uneven, good Thermal insulation effect, simple construction effect

Inactive Publication Date: 2018-10-12
赵永福 +1
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. In the case of the same addition amount, the coating made of glass hollow microspheres and ceramic microspheres requires high coating thickness and is easy to crack and has poor heat insulation performance;
[0004] 2. Unstable storage performance: products made of glass hollow microspheres or ceramic microspheres are prone to defects such as viscosity increase and floating during storage;
[0005] 3. Poor workability: due to the obvious post-thickening, it can only be diluted with water to achieve the scraping effect during construction. It is difficult to control the viscosity of the amount of water added, which has a great impact on construction and heat insulation effects;
[0006] 4. The price is relatively expensive: the high-quality glass hollow microspheres or ceramic microspheres selected for the preparation of reflective heat insulation coatings are mainly imported, and the price is generally high, which has a great impact on the production cost of the coating;
[0007] 5. Monotonous color: It is difficult to color the heat-insulating coating prepared with glass hollow microspheres or ceramic microspheres, mainly white;
[0008] 6. The heat-insulating coating made of hollow glass microspheres or ceramic microspheres has unevenness in the paint film after construction, and the paint film is not full, which cannot achieve the desired effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reflective thermal insulation coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Weigh 803 150kg of heat-reflecting insulation powder, 180kg of water, 350kg of styrene-acrylic emulsion, 150kg of rutile titanium dioxide, 150kg of calcium carbonate, 25kg of mica powder, 8kg of antifreeze, 15kg of alcohol ester twelve, 3kg of thickener, and dispersant 10kg, defoamer 3kg, fungicide 2.5kg, preservative 3kg.

[0046] The preparation method is as follows: first, dilute the thickener and water with water in a mass ratio of 1:1, and set aside; put the rest of the water, dispersant, antifreeze, defoamer, bactericide, and preservative into stirring In the tank, stir for 10 minutes at a speed of about 600 rpm; slowly add rutile titanium dioxide into the mixing tank, and stir for 30 minutes at a speed of about 1200 rpm; heat reflective heat insulation powder 803, calcium carbonate, Slowly add mica powder into the mixing tank, and stir for 20 minutes at a speed of about 1000 rpm; slowly add styrene-acrylic emulsion and alcohol ester twelve into the mixing tank, a...

Embodiment 2

[0048] Weigh 803 100kg of heat-reflecting insulation powder, 250kg of water, 300kg of styrene-acrylic emulsion, 200kg of rutile titanium dioxide, 100kg of calcium carbonate, 50kg of mica powder, 15kg of antifreeze, 20kg of alcohol ester twelve, 5kg of thickener, and dispersant 13kg, defoamer 1.5kg, fungicide 3kg, preservative 5kg.

[0049] The preparation method is as follows: first, dilute the thickener and water with water in a mass ratio of 1:1, and set aside; put the rest of the water, dispersant, antifreeze, defoamer, bactericide, and preservative into stirring In the tank, stir for 10 minutes at a speed of about 600 rpm; slowly add rutile titanium dioxide into the mixing tank, and stir for 30 minutes at a speed of about 1200 rpm; heat reflective heat insulation powder 803, calcium carbonate, Slowly add mica powder into the mixing tank, and stir for 20 minutes at a speed of about 1000 rpm; slowly add styrene-acrylic emulsion and alcohol ester twelve into the mixing tank, ...

Embodiment 3

[0051] Weigh heat reflective insulation powder 803 200kg, water 130kg, styrene-acrylic emulsion 330kg, rutile titanium dioxide 180kg, calcium carbonate 130kg, mica powder 35kg, antifreeze agent 10kg, alcohol ester twelve 18kg, thickener 4kg, dispersant 8kg, defoamer 2kg, fungicide 2kg, preservative 4kg.

[0052]The preparation method is as follows: first, dilute the thickener and water with water in a mass ratio of 1:1, and set aside; put the rest of the water, dispersant, antifreeze, defoamer, bactericide, and preservative into stirring In the tank, stir for 10 minutes at a speed of about 600 rpm; slowly add rutile titanium dioxide into the mixing tank, and stir for 30 minutes at a speed of about 1200 rpm; heat reflective heat insulation powder 803, calcium carbonate, Slowly add mica powder into the mixing tank, and stir for 20 minutes at a speed of about 1000 rpm; slowly add styrene-acrylic emulsion and alcohol ester twelve into the mixing tank, and stir for 10 minutes at a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a reflective heat insulation coating. The coating is prepared from the following components in parts by mass: 10-20 parts of heat-reflecting and heat-insulating powder, 30-35parts of styrene-acrylic emulsion, 15-20 parts of rutile-type titanium dioxide, 10-15 parts of calcium carbonate, 2.5-5 parts of mica powder, 0.8-1.5 parts of an antifreeze agent, 1.5-2 parts of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, 0.3-0.5 parts of a thickener, 0.8-1.3 parts of a dispersing agent, 0.15-0.3 parts of a defoaming agent, 0.2-0.3 parts of a fungicide, 0.3-0.5 parts of a preservative and 13-25 parts of water. The reflective heat insulation coating can achieve better heat insulation effect, and the problems about color matching, construction, suspension, thickening, filmplumpness and the like can be solved.

Description

technical field [0001] The invention relates to the field of heat-insulating coatings, and more specifically, the invention relates to a reflective heat-insulating coating. Background technique [0002] With the rapid development of the construction industry, the energy saving and environmental protection of buildings are becoming more and more important. Therefore, the issue of building energy conservation has been paid more and more attention. At present, my country's building energy consumption accounts for about 27% of the country's total energy, ranking first in all types of energy consumption in the country. In addition, the energy consumption of heating and air conditioning accounts for 55% of the total energy consumption of buildings, and it is still growing at a rate of 1% per year. Therefore, the research and development of building thermal insulation coatings has significant economic, environmental and social benefits. The use of coatings with heat-insulating f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/33C09D7/61
CPCC09D125/14C08K2003/2241C08K2003/265C09D5/004C09D7/61C08K3/22C08K3/26C08K3/34
Inventor 赵永福
Owner 赵永福
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products