Modified g-C3N4 activator for UV-EB radiation curing

A UV-EB, radiation curing technology, applied in the direction of coating, etc., can solve the problem of not having independent performance as a photoinitiator, and achieve excellent comprehensive performance, strong activity, and save curing costs.

Inactive Publication Date: 2018-11-06
NANJING INST OF TECH
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Studies have shown that g-C can be increased by a single acid activation, alkali treatment 3 N 4 The catalytic activity of the g-C activated by a single acid, base treatment after acid activation 3 N 4 It has the potential to improve the UV radiation curing and EB radiation curing effects, but it still does not have the performance as a photoinitiator independently, so it cannot effectively solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified g-C3N4 activator for UV-EB radiation curing
  • Modified g-C3N4 activator for UV-EB radiation curing
  • Modified g-C3N4 activator for UV-EB radiation curing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] (1) g-C 3 N 4 Acid activation modification: Take 1g of pure g-C 3 N 4 Powder and 50mL of concentrated hydrochloric acid solution (5.9mol·L -1 ) were mixed, stirred magnetically at room temperature for 10 minutes, poured the mixture into a 100mL hydrothermal reaction kettle, and reacted for 4 hours at 100°C. After cooling to room temperature naturally, after filtering, washing and drying, the Acid-activated modified g-C was obtained 3 N 4 ;

[0040] (2)g-C 3 N 4 Acid-base dual activation modification: take 0.2g of the acid-activated modified g-C obtained in step (1) 3 N 4 With 60mL of sodium hydroxide solution (0.2mol·L -1 ) were mixed, and ultrasonically dispersed at room temperature for 10 minutes, the mixture was poured into a 100mL hydrothermal reactor, and reacted at 100°C for 2.5 hours. After cooling to room temperature naturally, it was filtered, washed, dried, etc. Obtain acid-base dual activation modified g-C 3 N 4 active agent;

[0041] (3) Prepar...

Embodiment 2

[0045] (1) g-C 3 N 4 Acid activation modification: Take 1g of pure g-C 3 N 4 Powder and 30mL of concentrated hydrochloric acid solution (9.5mol L -1 ) were mixed, stirred magnetically at room temperature for 5 minutes, poured the mixture into a 50mL hydrothermal reaction kettle, and reacted for 2.5 hours at 150°C. After cooling to room temperature naturally, after filtering, washing and drying, the Acid-activated modified g-C was obtained 3 N 4 ;

[0046] (2)g-C 3 N 4 Acid-base dual activation modification: take 0.2g of the acid-activated modified g-C obtained in step (1) 3 N 4 With 50mL of potassium hydroxide solution (0.4mol·L -1 ) were mixed, and ultrasonically dispersed at room temperature for 15 minutes, the mixture was poured into a 100mL hydrothermal reaction kettle, and reacted at 120°C for 6 hours. Obtain acid-base dual activation modified g-C 3 N 4 active agent;

[0047] (3) Preparation of coatings: the g-C of step (2) obtained acid-base dual activation...

Embodiment 3

[0051] (1) g-C 3 N 4 Acid activation modification: Take 1g of pure g-C 3 N 4 Powder and 50mL of concentrated nitric acid solution (7.2mol L -1 ) were mixed, stirred magnetically at room temperature for 20 minutes, poured the mixture into a 100mL hydrothermal reaction kettle, and reacted at 85°C for 6 hours. After cooling to room temperature naturally, after filtering, washing and drying, the Acid-activated modified g-C was obtained 3 N 4 ;

[0052] (2)g-C 3 N 4 Acid-base dual activation modification: take 0.2g of the acid-activated modified g-C obtained in step (1) 3 N 4 With 40mL of concentrated ammonia solution (14mol L -1 ) were mixed, and ultrasonically dispersed at room temperature for 5 minutes, the mixture was poured into a 50mL hydrothermal reaction kettle, and reacted at 150°C for 3 hours. After cooling to room temperature naturally, it was filtered, washed, and dried. Obtain acid-base dual activation modified g-C 3 N 4 active agent.

[0053] (3) Prepara...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
thermal resistanceaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a modified g-C3N4 activator for UV-EB radiation curing. A UV-EB radiation curing body is firstly subjected UV (ultraviolet light) radiation curing, and then is subjected to EB (electron beam) radiation curing. The modified g-C3N4 activator is prepared from g-C3N4 according to an acid and alkali double activation modification method, and separately serves as a photoinitiatorand an active stabilizer in a curing system during a UV radiation curing process and an EB radiation curing process. The invention initiatively provides a g-C3N4 acid and alkali double activation modification method, successfully applies the modified g-C3N4 activator to a UV-EB radiation curing system, and obviously reduces energy consumption, improves the production efficiency and reduces the cost, and curing coating has excellent comprehensive operation performances.

Description

technical field [0001] The invention relates to the technical field of UV-EB radiation curing, in particular to a modified g-C for UV-EB radiation curing 3 N 4 Activator and method for its preparation. Background technique [0002] At present, radiation curing technology is widely used in coatings, inks, printing plate making, dental restoration and optical disc manufacturing and other fields. Compared with traditional curing technology, radiation curing technology has the advantages of environmental friendliness, energy saving, short time and fast curing. Especially in recent years, the call for eliminating pollution and protecting the environment has become higher and higher, and radiation curing technology has shown more and more vitality. [0003] UV radiation curing is to cure the system by UV light irradiation. The curing speed is fast, but the UV energy consumption is large, and there is a radiation "blind zone" for workpieces with complex shapes, which cannot be e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/00C08F2/48C08F2/54
CPCC08F2/48C08F2/54C09D4/00
Inventor 张金泉杭祖圣怀旭王维李悦唐林陈阳
Owner NANJING INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka