Anti-fouling hydrophobic ceramic utensil and production method thereof

A production method and ceramic technology, which is applied in the field of ceramic materials, can solve the problems of water stains penetrating into the interior of ceramic vessels, water stains tend to stay on the surface of the vessel, and stain repellency is not strong, achieving significant anti-fouling and hydrophobic capabilities, anti-fouling and hydrophobic Strong ability and beautiful appearance

Active Publication Date: 2018-11-09
陈海雄
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ceramic cooking utensils often have the following disadvantages during their use: 1. After cleaning the ceramic utensils with water, water stains tend to stay on the surface of the utensils. After a long time, the water stains will penetrate into the interior of the ceramic utensils and easily breed microorganisms; 2. Traditional Ceramic is not very repellent to stains

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-fouling hydrophobic ceramic utensil and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment provides a kind of anti-fouling and hydrophobic ceramic utensil and its manufacturing method:

[0038] 1. The raw materials of the anti-fouling and hydrophobic ceramic utensils include: 96.00% of clay, 3.00% of silicon dioxide, 0.09% of aluminum oxide, and 0.91% of methyltrioxyethylsilane in terms of weight percentage.

[0039] 2. Production method:

[0040] S1. Forming of symmetrical ceramic utensils: Weigh the raw materials according to the proportion of the formula, add water ball mill, press filter, rough refining, stale, refining, rolling forming, and obtain the ceramic green body;

[0041] S2. Drying: microwave drying technology is used to dry the ceramic body, and the microwave frequency is 250 MHz;

[0042] S3. Blank trimming: Trimming the dried ceramic body by means of friction;

[0043] S4. Water replenishment: After soaking the trimmed ceramic body with clear water, rub the ceramic body;

[0044] S5. Glazing: use a ceramic glazing machine t...

Embodiment 2

[0052] This embodiment provides a kind of anti-fouling and hydrophobic ceramic utensil and its manufacturing method:

[0053] 1. The raw materials of the anti-fouling and hydrophobic ceramic utensils include, by weight percentage: 93.50% kaolin, 5.26% silicon dioxide, 0.18% aluminum oxide, and 1.06% methyltrioxyethylsilane.

[0054] 2. Production method:

[0055] S1. Irregular ceramic utensil molding: Weigh the raw materials according to the formula ratio, add water ball mill, press filter, rough refining, stale, refining, high-pressure grouting molding, and obtain the ceramic body;

[0056] S2. Drying: microwave drying technology is used to dry the ceramic body, and the microwave frequency is 295 MHz;

[0057] S3. Blank trimming: Trimming the dried ceramic body by means of friction;

[0058] S4. Water replenishment: After soaking the trimmed ceramic body with clear water, rub the ceramic body;

[0059] S5. Glazing: use a ceramic glazing machine to glaze the water-replenish...

Embodiment 3

[0067] This embodiment provides a kind of anti-fouling and hydrophobic ceramic utensil and its manufacturing method:

[0068] 1. The raw materials of the anti-fouling and hydrophobic ceramic utensils include: 94.28% of a mixture of kaolin and clay (any ratio is required), 4.75% of silicon dioxide, 0.12% of aluminum oxide, and 0.85% of methyltrioxyethylsilane .

[0069] 2. Production method:

[0070] S1. Forming of symmetrical ceramic utensils: Weigh the raw materials according to the proportion of the formula, add water ball mill, press filter, rough refining, stale, refining, rolling forming, and obtain the ceramic green body;

[0071] S2. Drying: microwave drying technology is used to dry the ceramic body, and the microwave frequency is 280 MHz;

[0072] S3. Blank trimming: Trimming the dried ceramic body by means of friction;

[0073] S4. Water replenishment: After soaking the trimmed ceramic body with clear water, rub the ceramic body;

[0074] S5. Glazing: use a ceram...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the ceramic processing technology, and discloses an anti-fouling hydrophobic ceramic utensil. The raw materials of the anti-fouling hydrophobic ceramic utensil comprise the following components in percentage by weight: 93.50--96.00% of ceramic clay, 3.00-5.50% of silicon dioxide, 0.09-0.18% of basic oxide, and 0.65-1.06% of methyl trioxyethyl silane; the invention also discloses the production method for the anti-fouling hydrophobic ceramic utensil; the anti-fouling hydrophobic ceramic utensil produced by the production method has good hydrophobicity and stain-resistant property.

Description

technical field [0001] The invention belongs to the technical field of ceramic materials, and in particular relates to an anti-pollution and hydrophobic ceramic utensil and a manufacturing method thereof. Background technique [0002] Ceramic cooking utensils have unique advantages such as good heat storage, environmental protection, and corrosion resistance. Various ceramic cooking utensils have appeared in common people's homes and catering industries, competing with traditional metal cooking utensils. Ceramic cooking utensils often have the following disadvantages during their use: 1. After cleaning the ceramic utensils with water, water stains tend to stay on the surface of the utensils. After a long time, the water stains will penetrate into the interior of the ceramic utensils and easily breed microorganisms; 2. Traditional Ceramic is not very repellent to stains. Contents of the invention [0003] In order to solve the above-mentioned problems in the prior art, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/34A47J36/04
CPCA47J36/04C04B33/13C04B33/34C04B2235/3217C04B2235/3418C04B2235/656
Inventor 陈海雄
Owner 陈海雄
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka