Room temperature vulcanized rubber strip for automatic repair of conveyor belt and preparation method thereof

A technology of room temperature vulcanization and conveyor belts, which is applied in the direction of adhesives, adhesive types, adhesive additives, etc., which can solve the problems of inconvenient storage of adhesive strips, poor stickiness and repair quality, and improve the overall polarity and stickiness. Effects of emigration, dispersibility and solubility improvement

Active Publication Date: 2018-11-09
中德(扬州)输送工程技术有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a room temperature vulcanized rubber strip for automatic repair of conveyor belts and its preparation method, which solves the technical problems of inconvenient storage, poor viscosity and poor repair quality of rubber strips for conveyor belt repair in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Room temperature vulcanized rubber strip for automatic repair of conveyor belt and preparation method thereof
  • Room temperature vulcanized rubber strip for automatic repair of conveyor belt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A room temperature vulcanized rubber strip for conveyor belt automatic repair provided by the present invention comprises a rubber strip 1 and a rubber strip 2, and the rubber strip 1 includes the following raw materials in parts by weight: 80 parts of natural rubber plasticized rubber, terminal functional Melt-solution polystyrene-butadiene rubber 20 parts, zinc oxide 5 parts, stearic acid 1.5 parts, anti-aging agent 5 parts, alkyl phenolic tackifying resin 6 parts, high wear-resistant carbon black 30 parts, bisphenol A 5 parts, sulfur 2.0 The rubber strip two includes the following raw materials in parts by weight: 100 parts of end-group functionalized solution-polymerized styrene-butadiene rubber, 30 parts of carboxyl-terminated liquid nitrile rubber, 40 parts of high wear-resistant carbon black, zinc isopropyl xanthate 1.0 parts, 0.3 parts of phthalic anhydride.

[0024] Wherein, the molar mass ratio of the rubber strip 1 and the rubber strip 2 is 1:1, and the formu...

Embodiment 2

[0035]A room temperature vulcanized rubber strip for automatic repair of a conveyor belt, comprising a rubber strip 1 and a rubber strip 2, the rubber strip 1 comprising the following raw materials in parts by weight: 60 parts of natural rubber plasticized rubber, terminal functionalized solution polystyrene butadiene 40 parts of rubber, 4 parts of zinc oxide, 1.0 part of stearic acid, 5 parts of anti-aging agent, 10 parts of alkylphenolic tackifying resin, 40 parts of high wear-resistant carbon black, 10 parts of bisphenol A, 2.5 parts of sulfur; the rubber strip Two include the following raw materials in parts by weight: 80 parts of end-group functionalized solution-polymerized styrene-butadiene rubber, 20 parts of carboxyl-terminated liquid nitrile rubber, 40 parts of high wear-resistant carbon black, 1.8 parts of zinc isopropyl xanthate, phthalate 0.5 parts of formic anhydride.

[0036] Wherein, the molar mass ratio of the rubber strip 1 and the rubber strip 2 is 1:1, and ...

Embodiment 3

[0043] A room temperature vulcanized rubber strip for automatic repair of conveyor belts, comprising a rubber strip 1 and a rubber strip 2, the rubber strip 1 comprising the following raw materials in parts by weight: 50 parts of natural rubber plasticized rubber, terminal functionalized solution polystyrene butadiene 50 parts of rubber, 5 parts of zinc oxide, 1.5 parts of stearic acid, 5 parts of anti-aging agent, 10 parts of alkylphenolic tackifying resin, 45 parts of high wear-resistant carbon black, 10 parts of bisphenol A, 3.0 parts of sulfur; Bar 2 includes the following raw materials in parts by weight: 70 parts of end-group functionalized solution-polymerized styrene-butadiene rubber, 10 parts of carboxyl-terminated liquid nitrile rubber, 30 parts of high wear-resistant carbon black, 3.0 parts of zinc isopropyl xanthate, phthalate 1.0 parts of diformic anhydride.

[0044] Wherein, the molar mass ratio of the rubber strip 1 and the rubber strip 2 is 1:1, and the formula...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a room temperature vulcanized rubber strip for automatic repair of a conveyor belt and a preparation method thereof. The room temperature vulcanized rubber strip comprises a rubber strip 1 and a rubber strip 2. The rubber strip 1 is prepared from the following raw materials in parts by weight: 50 to 80 parts of natural rubber plasticated rubber, 20 to 50 parts of end groupfunctionalized solution polymerized styrene-butadiene rubber, 2 to 5 parts of zinc oxide, 0.5 to 1.5 parts of stearic acid, 5 parts of anti-aging agents, 4 to 10 parts of alkyl phenolic tackifying resins, 30 to 45 parts of high wear resistant carbon black, 5 to 10 parts of bisphenol A, and 1.0 to 3.0 parts of sulfur; the rubber strip 2 is prepared from the following raw materials in parts by weight: 70 to 100 parts of end group functionalized solution polymerized styrene-butadiene rubber, 10 to 30 parts of terminal carboxyl liquid nitrile rubber, 30 to 45 parts of high wear resistant carbon black, 1.0 to 3.0 parts of zinc isopropyl xanthate, and 0.3 to 1.0 part of phthalic anhydride. The room temperature vulcanized rubber strip for the automatic repair of the conveyor belt and the preparation method thereof solve technical problems that an adhesive tape for repairing the conveyor belt in the prior art is inconvenient to store, the viscosity is poor, and the repair quality is poor.

Description

technical field [0001] The invention relates to the technical field of conveyor belt rubber strips, in particular to a room temperature vulcanized rubber strip for automatic repair of conveyor belts and a preparation method thereof. Background technique [0002] Conveyor belts are mainly used in mines, ports, steel plants, power plants, construction, cement, coal mines and other industries, especially in iron ore, copper mines, coal mines and ports. It is easy to cause abnormal surface damage or scratches on the tape during its service life. If it is not repaired in time, the tape will be completely damaged, lose its use value, and cause tape loss to customers. Therefore, research on tape repair technology has always been the priority of conveyor belt manufacturers. Focus on work, high-quality repairs can completely restore more than 80% of the performance of the tape, creating significant economic benefits for customers, and also promoting the maximum use of resources. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J109/06C09J11/04C09J11/06C09J11/08
CPCC08K2003/2296C08L2205/025C08L2205/035C09J11/04C09J11/06C09J11/08C09J109/06C08L7/00C08L9/06C08L13/00C08L61/06C08K13/02C08K5/1539C08K3/22C08K5/09C08K3/04C08K5/18
Inventor 毛秋田尧韩学英
Owner 中德(扬州)输送工程技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com