Light high-strength blue Miao silver alloy with excellent pressure casting performance and process thereof

A lightweight, high-strength technology, applied in the field of alloys, can solve problems such as sulfide corrosion deterioration, lack of rich color silver series, inappropriateness, etc., achieve performance optimization, increase market sales and user experience, and promote rapid development.

Inactive Publication Date: 2018-11-13
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is obviously not suitable for the field of Miao silver that requires low price
In addition, although a layer of colored film can be plated on the surface of Miao silver jewelry by ion plating, this colored film will inevitably expose the fresh matrix alloy due to corrosion, fading or wear after use, resulting in vulcanization. further deterioration of corrosion
[0008] But it is a pity that Miao silver alloy has not formed a rich color silver series like color K gold.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Lightweight and high-strength blue seedling silver alloy with excellent die-casting performance and its technology. In terms of weight percentage, the composition of the alloy is Sr: 0.5wt.%, Al: 5.0wt.%, Mg: 2.0wt.%, Be: 0.5wt.%, Co: 4.0wt.%, In: 12.0wt.% , Ag: 30.0wt.%, the balance is copper. The above-mentioned light-weight high-strength blue seedling silver alloy with excellent die-casting performance and its technology include the following steps: adding the above-mentioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; heat preservation at 1400 degrees during smelting 10 minutes, rely on high-frequency induction furnace to stir evenly; after stirring evenly, keep warm at 1400 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. The obtained ingot is rolled at room temperature, and the amount of reduction in each pass is...

Embodiment 2

[0022] Lightweight and high-strength blue seedling silver alloy with excellent die-casting performance and its technology. In terms of weight percentage, the composition of the alloy is Sr: 0.8wt.%, Al: 8.0wt.%, Mg: 3.0wt.%, Be: 0.8wt.%, Co: 5.0wt.%, In: 15.0wt.% , Ag: 50.0wt.%, the balance is copper. The above-mentioned light-weight high-strength blue seedling silver alloy with excellent die-casting performance and its technology include the following steps: adding the above-mentioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; heat preservation at 1400 degrees during smelting 10 minutes, rely on high-frequency induction furnace to stir evenly; after stirring evenly, keep warm at 1400 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. The obtained ingot is rolled at room temperature, and the amount of reduction in each pass is...

Embodiment 3

[0025] Lightweight and high-strength blue seedling silver alloy with excellent die-casting performance and its technology. In terms of weight percentage, the composition of the alloy is Sr: 0.6wt.%, Al: 5.8wt.%, Mg: 2.4wt.%, Be: 0.6wt.%, Co: 4.2wt.%, In: 12.5wt.% , Ag: 40.0wt.%, the balance is copper. The above-mentioned light-weight high-strength blue seedling silver alloy with excellent die-casting performance and its technology include the following steps: adding the above-mentioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; heat preservation at 1400 degrees during smelting 10 minutes, rely on high-frequency induction furnace to stir evenly; after stirring evenly, keep warm at 1400 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. Roll the obtained ingot at room temperature, and the amount of rolling in each pass is 20-30%...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a light high-strength blue Miao silver alloy with excellent pressure casting performance and a process thereof. The light high-strength blue Miao silver alloy is prepared from,by weight percent, 0.5 wt% to 0.8 wt% of Sr, 5.0 wt% to 8.0 wt% of Al, 2.0 wt% to 3.0 wt% of Mg, 0.5 wt% to 0.8 wt% of Be, 4.0 wt% to 5.0 wt% of Co, 12.0 wt% to 15.0 wt% of In, 30.0% to 50.0 wt% of Ag and the balance copper. According to the material, a weight-reducing selecting scheme is provided for the Miao silver alloy in our country, the obtained product has an excellent blue impression, andis extremely resistant to hydrogen sulfide corrosion. The needs of product updating and industry upgrading of the jewelry industry in our country can be effectively promoted through implementation and industrialization of the material.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a silver alloy. Background technique [0002] Wearing a silver crown, a silver necklace around the neck, and a chest full of silver ornaments, the image of a Miao girl in full attire constitutes the impression of the Miao people in most people's minds. As early as the Qing Dynasty, the use of silver jewelry by the Miao people was very common. Miao people, regardless of gender, old or young, regarded wearing silver jewelry as beautiful. In terms of the use of silver ornaments, southeast Guizhou is the heaviest, and there are many kinds of silver ornaments in Taijiang, Kaili, Leishan and other regions, and there are even more than 50 kinds of silver ornaments in full decoration. The girls in Miao Village are dressed in silver ornaments, the ornaments can reach half a person's height, and the parts can reach hundreds of pieces, weighing more than 20 to 30 catties. This complicated ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C5/08C22C9/00C22C30/02C22C1/02C22F1/00C22F1/08C22F1/14C22F1/02C23C8/12
CPCC22C5/08C22C1/02C22C9/00C22C30/02C22F1/00C22F1/02C22F1/08C22F1/14C23C8/12
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com