A kind of high-layer spacing artificial graphite material and preparation method thereof

A technology of artificial graphite and spacing, applied in chemical instruments and methods, carbon compounds, inorganic chemistry, etc., can solve the problems of limiting the application field and application effect of high-level spacing graphite materials, irregular interlayer structure, acidic pH value, etc. To achieve the effect of mild processing technology, good electrical conductivity and high layer spacing

Active Publication Date: 2021-11-26
贵州中科星城石墨有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional high-layer spacing graphite material is a worm-like substance obtained from flake natural graphite as raw material through oxidation intercalation, washing, drying, and thermal expansion. During the preparation process, the material has many characteristics of flake natural graphite. Obvious destructive effects, such as significantly reduced electrical conductivity of the material, extremely irregular interlayer structure, acidic PH value, etc., these destructive effects greatly limit the application field and application effect of high-layer spacing graphite materials
In addition, this traditional preparation method uses a large amount of concentrated acid, and the preparation process has a high degree of pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-layer spacing artificial graphite material and preparation method thereof
  • A kind of high-layer spacing artificial graphite material and preparation method thereof
  • A kind of high-layer spacing artificial graphite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The preparation method of 1# high-rise spacing artificial graphite material, the steps are as follows:

[0029] (I) Petroleum asphalt and biomass tar with a softening point of 90°C and D50=3.4 μm are used as raw materials, in which aromatic hydrocarbons in biomass tar account for 21%, phenols account for 45%, and the quality of asphalt and biomass tar The ratio is 5:1. Under the conditions of nitrogen atmosphere, 300rpm mechanical stirring, 400°C, 5atm, polycondensation and crosslinking were carried out for 12h to obtain crosslinked mesophase pitch.

[0030] (II) The cross-linked mesophase pitch was treated in a nitrogen atmosphere at a low temperature of 600°C for 5 hours, and the temperature was naturally cooled to room temperature to obtain green coke, which was then depolymerized by a multi-wheel mill.

[0031] (Ⅲ) The depolymerized green coke was heated up to 2600°C under a nitrogen atmosphere, kept for 1 hour to graphitize, and a high-layer spacing artificial gra...

Embodiment 2

[0033] The preparation method of 2# high-rise spacing artificial graphite material, the steps are as follows:

[0034] (I) Coal tar pitch and biomass tar with a softening point of 130°C and D50 = 4.1 μm are used as raw materials, in which aromatic hydrocarbons in biomass tar account for 32%, phenols account for 40%, and the quality of pitch and biomass tar The ratio is 10:3. Under the conditions of argon atmosphere, 300rpm mechanical stirring, 450°C and 16atm, polycondensation and crosslinking were carried out for 36h to obtain crosslinked mesophase pitch.

[0035] (II) The cross-linked mesophase pitch was treated in an argon atmosphere at a low temperature of 600°C for 3 hours, and the temperature was naturally cooled to room temperature to obtain green coke, which was then depolymerized by multiple round mills.

[0036] (Ⅲ) The depolymerized green coke was heated up to 3000°C in an argon atmosphere, kept for 2 hours for graphitization, and a high-layer spacing artificial gr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-layer spacing artificial graphite material and a preparation method thereof. The material is artificial graphite prepared by cross-linking, polycondensation and graphitization with asphalt as raw material. It has an obvious layered structure with a layer spacing of 0.34~0.38nm and good electrical conductivity. The preparation method of the high-rise spacing artificial graphite material provided by the present invention: using pitch as raw material, adding an appropriate amount of cross-linking agent, performing polycondensation and cross-linking reactions under high temperature and high pressure conditions to obtain cross-linked mesophase pitch, and then undergoing low-temperature treatment and graphitization A high-level spacing artificial graphite material is obtained.

Description

technical field [0001] The invention relates to a graphite material and a preparation method thereof, in particular to a high-layer spacing artificial graphite material and a preparation method thereof. Background technique [0002] High-layer spacing graphite material is a kind of functional carbon material widely used. It has the characteristics of high temperature resistance, corrosion resistance, electrical conductivity, softness and impermeability. It is widely used in petrochemical, sealing, energy storage and energy saving fields. play an important role. [0003] The traditional high-layer spacing graphite material is a worm-like substance obtained from flake natural graphite as raw material through oxidation intercalation, washing, drying, and thermal expansion. During the preparation process, the material has many characteristics of flake natural graphite. Obvious destructive effects, such as significantly reduced electrical conductivity of the material, extremely ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/205
CPCC01B32/205
Inventor 石磊王志勇陶振友邵浩明
Owner 贵州中科星城石墨有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com