Fast-cured lightweight board applicable to prefabricated buildings and preparation method thereof

A fast-curing and assembled technology, applied in the field of building materials, can solve problems such as low early strength, slow setting time, and limited production cycle of the production line, and achieve the effect of good stability and high early strength

Active Publication Date: 2018-11-20
WUHAN UNIV OF TECH
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing lightweight boards are mainly cement-based, which has disadvantages such as slow setting time, low early strength, and slow strength development, which severely limits the production cycle of the production line, resulting in a significant drop in output, and the cement-based material itself has the problem of shrinkage and cracking It also limits its application to some extent
Chinese patent CN106565181A discloses a preparation method of lightweight concrete prefabricated slabs, which can realize demoulding within 6 to 8 hours, and has the characteristics of high finished product strength and light surface density. Defects include chemical shrinkage, drying shrinkage and carbonization shrinkage, etc., which cannot overcome the shortcomings of sheet shrinkage and cracking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fast-cured lightweight board applicable to prefabricated buildings and preparation method thereof
  • Fast-cured lightweight board applicable to prefabricated buildings and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Prepare a fast-curing lightweight board suitable for prefabricated buildings. The raw materials and weight parts are: 70 parts of cement, 20 parts of grade II fly ash, composite early strength agent (sulfoaluminate cement and sodium sulfate according to the quality Ratio 10:1 Compounding) 4 parts, phosphogypsum dihydrate 6 parts, phosphogypsum dihydrate whiskers 3 parts, EPS 1.1 parts, nano-silica sol 0.3 parts, water reducing agent 0.2 parts, air-entraining agent 0.05 parts, water retention dose 0.1 part.

[0027] According to the above formula, weigh cement, secondary fly ash, composite early strength agent, phosphogypsum dihydrate, and phosphogypsum dihydrate whiskers and dry mix for 60 seconds, add nano-silica sol, water reducing agent, air-entraining agent, and water-retaining agent. At the same time, add water according to the water-to-material ratio of 0.34 and stir in the mixer for 2 minutes, then add EPS particles into the mixer and stir for 3 minutes, inject t...

Embodiment 2

[0030] To prepare a fast-curing lightweight board suitable for prefabricated buildings, the raw materials and weight parts are as follows:

[0031] 80 parts of cement, 10 parts of grade II fly ash, 2 parts of composite early strength agent (obtained by compounding sulphoaluminate cement and sodium sulfate at a mass ratio of 10:1), 10 parts of dihydrate phosphogypsum, dihydrate phosphogypsum crystal 5 parts of whiskers, 1.3 parts of EPS, 0.1 parts of nano-silica sol, 0.1 parts of water reducing agent, 0.1 parts of air-entraining agent, and 0.15 parts of water-retaining agent.

[0032] According to the above formula, weigh cement, secondary fly ash, composite early strength agent, phosphogypsum dihydrate, and phosphogypsum dihydrate whiskers and dry mix for 60 seconds, add nano-silica sol, water reducing agent, air-entraining agent, and water-retaining agent. At the same time, add water according to the water-to-material ratio of 0.34 and stir in the mixer for 2 minutes, then ad...

Embodiment 3

[0035] To prepare a fast-curing lightweight board suitable for prefabricated buildings, the raw materials and weight parts are as follows:

[0036] 60 parts of cement, 30 parts of grade I fly ash, 6 parts of composite early strength agent (obtained by compounding sulphoaluminate cement and sodium sulfate at a mass ratio of 10:1), 5 parts of dihydrate phosphogypsum, dihydrate phosphogypsum crystal 1 part of whisker, 0.6 part of EPS, 0.5 part of nano silica sol, 0.3 part of superplasticizer

[0037] According to the above formula, weigh cement, secondary fly ash, composite early strength agent, phosphogypsum dihydrate, and phosphogypsum dihydrate whiskers and dry mix for 60 seconds, add nano-silica sol, water reducing agent, air-entraining agent, and water-retaining agent. At the same time, add water according to the water-to-material ratio of 0.31 and stir in the mixer for 2 minutes, then add EPS particles into the mixer and stir for 3 minutes, inject the prepared slurry into t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a fast-cured lightweight board applicable to prefabricated buildings and a preparation method thereof. The fast-cured lightweight board comprises the following components as raw materials in parts by weight: 60-80 parts of cement, 10-30 parts of fly ash, 2-6 parts of a compound early strength agent, 5-10 parts of phosphogypsum, 1-5 parts of fiber, 0.6-1.3 parts of lightweight aggregate, 0.1-0.5 part of nanometer silica sol, 0.1-0.3 part of a water reducing agent, 0-0.1 part of an air entraining agent and 0-0.15 part of a water retaining agent. The fast-cured lightweight board provided by the invention is high in early strength and free of retraction in later strength, achieves the demoulding strength after 8h-12h, has the 1d strength being higher than 60% of the 28d strength, has adjustable volume weight within the range of 600-1000Kg / m<3>, has the heat conductivity coefficient being smaller than 0.15W / (m.K), is high in stability and free of obvious layering and cracking, and can be used as a prefabricated wall board for the prefabricated buildings.

Description

technical field [0001] The invention belongs to the technical field of building materials, and relates to a fast-curing lightweight board suitable for prefabricated buildings and a preparation method thereof. Background technique [0002] As a new direction of architectural development, prefabricated buildings have been increasingly popularized. Lightweight panels can be used as prefabricated wall materials, and their development and application play an important role in the development of prefabricated buildings. Existing lightweight boards are mainly cement-based, which has disadvantages such as slow setting time, low early strength, and slow strength development, which severely limits the production cycle of the production line, resulting in a significant drop in output, and the cement-based material itself has the problem of shrinkage and cracking It also limits its application to a certain extent. Chinese patent CN106565181A discloses a preparation method of lightweig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/40
CPCC04B28/04C04B2111/40C04B2201/20C04B2201/32C04B2201/50C04B18/08C04B22/147C04B7/32C04B22/144C04B14/383C04B16/08C04B14/062C04B24/24C04B24/20C04B24/383
Inventor 马保国金子豪李玉博戚华辉孙仲达
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com