A preparation method of silica/shellac composite particles containing methylene blue with high fluorescence intensity

A technology of methylene blue and silicon dioxide, which is applied in the direction of chemical instruments and methods, luminescent materials, etc., to achieve the effect of simple process method, simple device and low price

Inactive Publication Date: 2021-03-19
SHANDONG UNIV OF TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, up to now, the preparation method of silica / shellac composite particles containing methylene blue to achieve high fluorescence intensity by shellac coating containing methylene blue has not been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of silica/shellac composite particles containing methylene blue with high fluorescence intensity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] (1) Add 92 ml of absolute ethanol, 17.2 ml of water, 2.48 ml of concentrated ammonia water and 0.10 g of methylene blue to the beaker in sequence. After stirring for 15 minutes, add 3.44 ml of ethyl orthosilicate. After stirring for 4 hours, centrifuge to obtain the sediment , the precipitate was first washed twice with 120 ml of ethanol, and then washed once with 20 ml of acetate buffer solution of pH = 3.6, and then the sediment obtained by centrifugation was dried at 70°C for 24 hours to obtain the Silica particles of methylene blue;

[0015] (2) Dissolving shellac in ethanol to prepare shellac solution, wherein the concentration of shellac is 5 grams per liter, put the silica particles containing methylene blue prepared in step (1) into 10 ml of shellac In the solution, the concentration of silica particles containing methylene blue was 10 g per liter. After ultrasonic treatment for 5 minutes, 30 ml of n-heptane was added to the insect containing silica particles co...

Embodiment 2

[0017] (1) Add 92 ml of absolute ethanol, 17.2 ml of water, 2.48 ml of concentrated ammonia water and 0.10 g of methylene blue to the beaker in sequence. After stirring for 15 minutes, add 3.44 ml of ethyl orthosilicate. After stirring for 4 hours, centrifuge to obtain the sediment , the precipitate was first washed twice with 120 ml of ethanol, and then washed once with 20 ml of acetate buffer solution of pH = 3.6, and then the sediment obtained by centrifugation was dried at 70°C for 24 hours to obtain the Silica particles of methylene blue;

[0018] (2) Dissolving shellac in ethanol to prepare a shellac solution, wherein the concentration of shellac is 10 grams per liter, put the silica particles containing methylene blue prepared in step (1) into 10 ml of shellac In the solution, the concentration of silica particles containing methylene blue was 10 g per liter. After ultrasonic treatment for 5 minutes, 30 ml of n-heptane was added to the insect containing silica particles...

Embodiment 3

[0020] (1) Add 92 ml of absolute ethanol, 17.2 ml of water, 2.48 ml of concentrated ammonia water and 0.10 g of methylene blue to the beaker in sequence. After stirring for 15 minutes, add 3.44 ml of ethyl orthosilicate. After stirring for 4 hours, centrifuge to obtain the sediment , the precipitate was first washed twice with 120 ml of ethanol, and then washed once with 20 ml of acetate buffer solution of pH = 3.6, and then the sediment obtained by centrifugation was dried at 70°C for 24 hours to obtain the Silica particles of methylene blue;

[0021] (2) Dissolving shellac in ethanol to prepare shellac solution, wherein the concentration of shellac is 20 grams per liter, put the silica particles containing methylene blue prepared in step (1) into 10 ml of shellac In the solution, the concentration of silica particles containing methylene blue was 10 g per liter. After ultrasonic treatment for 5 minutes, 30 ml of n-heptane was added to the insect containing silica particles c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for preparing methylene blue-containing silica / shellac composite particles with high fluorescence intensity, and belongs to the technical field of chemical raw material preparation. Add ammonia water, methylene blue and tetraethyl orthosilicate to the mixed solution containing water and ethanol, stir for 4 hours, centrifuge, wash and dry at 70 ° C, and disperse the prepared silica particles containing methylene blue in 5 ~ In the shellac solution of 20 grams per liter, add n-heptane dropwise, centrifuge after stirring for 2 hours, wash and dry at room temperature, promptly obtain the silica / shellac composite particles containing methylene blue with high fluorescence intensity. The method has the advantages of simple process, low raw material price and easy industrial production, and the obtained particles have good biocompatibility and high fluorescence intensity.

Description

technical field [0001] The invention discloses a method for preparing methylene blue-containing silica / shellac composite particles with high fluorescence intensity, belonging to the field of chemical raw material preparation methods. Background technique [0002] Dye molecules have high application value in fluorescence sensors, bioluminescence labeling, cell tracking and solid-state lasers, etc. The realization of these properties is related to the aggregation state of dye molecules. In high-concentration solutions or solid powders, dye molecules, such as methylene blue molecules, are easy to form aggregates, and the interaction between aggregated molecules will lead to the occurrence of fluorescence quenching effect, which will weaken the fluorescence signal, and then cause the fluorescence signal of methylene blue to be almost Unable to detect. Only in dilute aqueous solutions, such as concentrations of methylene blue molecules below 10 -6 The fluorescent signal of meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/02C09K11/06
CPCC09K11/025C09K11/06C09K2211/1037
Inventor 李成峰张伟王文浩郝志恒杨海玲葛筱璐
Owner SHANDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com