Method for preparing non-burning cigarettes from corn husk fiber

A corn husk and fiber technology, which is applied in the field of preparing non-burning cigarettes from corn husk fiber, can solve the problems of not being able to completely avoid the harm of tobacco smoking, lack of sustainable development, high pollution, etc., achieve friendly production technology, increase additional value, the effect of avoiding harm

Active Publication Date: 2022-04-19
彭荣淮
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, non-burning cigarettes are mostly rolled from tobacco sheets, and tobacco sheets are still tobacco products (tobacco stems and tobacco powder in the tobacco processing process are manufactured by rolling or thick pulp method), and also The harm of smoking tobacco cannot be completely avoided; in addition, the process of preparing tobacco sheets is also a high-pollution, high-energy-consuming process, which is not sustainable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing non-burning cigarettes from corn husk fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1. Use a plant breaker with a sieve diameter of 10mm to crush the corn husks with a moisture content of 12%±1%, and only keep the fibers in the husks with a length of less than 10mm, and then cut the fibers with a length of less than 10mm into 3mm -10mm fibers, sieve out fibers, fines, and powders with a length of less than 3mm in the fibers, and prepare fibers with a length of 3mm-10mm and a diameter of 0.05-0.1mm, and obtain an ivory-colored corn husk fiber. ;

[0023] 2. Soak the prepared corn husk fiber in the prepared spices for 3-4 hours, remove and drain, then put the corn husk fiber in a constant temperature environment with an ambient temperature of 25°C to balance the water to 16%±1% reserve;

[0024] 3. Using commonly used silk feeding machine, cigarette rolling machine, and filter tipping machine, roll the corn bract fiber with aluminum foil paper into a tobacco rod with a diameter of 7mm and a length of 20mm, and then combine the tobacco rod and filter tip...

Embodiment 2

[0026] 1. Use a plant breaker with a sieve diameter of 10mm to crush the corn husks with a moisture content of 12%±1%, and only keep the fibers in the husks with a length of less than 10mm, and then cut the fibers with a length of less than 10mm into 3mm -10mm fiber, sieve out the fiber, fine powder and powder with a length of less than 3mm in the fiber, and prepare a fiber with a length of 3mm-10mm and a diameter of 0.05-0.1mm, and obtain an ivory-colored corn bract fiber;

[0027] 2. Soak the prepared corn husk fiber in the prepared spices for 3-4 hours, remove and drain, then put the corn husk fiber in a constant temperature environment with an ambient temperature of 25°C to balance the water to 16%±1% reserve;

[0028] 3. Press the corn husk fiber into a 20mm-diameter, loose-structured cylinder with an extrusion molding machine. There is a hole in the center of the cylinder with a diameter of 1mm-1.2mm, and then use special equipment to wrap the cylinder with aluminum foi...

Embodiment 3

[0030] 1. Use a plant breaker with a sieve diameter of 10mm to crush the corn husks with a moisture content of 12%±1%, and only keep the fibers in the husks with a length of less than 10mm, and then cut the fibers with a length of less than 10mm into 3mm -10mm fiber, sieve out the fiber, fine powder and powder with a length of less than 3mm in the fiber, and prepare a fiber with a length of 3mm-10mm and a diameter of 0.05-0.1mm, and obtain an ivory-colored corn bract fiber;

[0031] 2. Soak the prepared corn husk fiber in the prepared spices for 3-4 hours, remove and drain, then put the corn husk fiber in a constant temperature environment with an ambient temperature of 25°C to balance the water to 16%±1% reserve;

[0032] 3. Press the corn husk fiber with an extrusion molding machine to grow into a cylinder with a diameter of 10mm and a loose structure of 15mm. In the cylinder, there are many holes with a diameter of 1mm-1.2mm that are evenly distributed (like traditional br...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing non-burning cigarettes from corn husk fibers, which is characterized in that it comprises the following steps: a. Preparation of corn husk fibers: 1) taking corn husk leaves with yellow leaves; 2) beating the corn husk leaves Crush to make corn husk fibers with a length of 3mm‑10mm and a diameter of 0.05‑0.6mm; 3) Soak the corn husk fibers in spices for 3‑4h, remove and drain, and balance the water in a constant temperature environment of 25°C to 16%±1% for later use; b. Use aluminum foil paper to roll the corn husk fiber into a tobacco rod; c. Combine the tobacco rod and the cigarette holder with pine paper to form a non-burning cigarette. Beneficial effects of the present invention: 1. The harmfulness of smoking tobacco is avoided, and the smoking quality of non-burning cigarettes prepared by this method is better; 2. The preparation of non-burning cigarettes by this method is a purely physical method, the production process is friendly, and energy consumption and pollution are all reduced 3. The utilization rate of corn bracts is improved, the added value of agricultural products is increased, and the regeneration and utilization of corn bracts is in line with the national industrial development policy.

Description

technical field [0001] The invention belongs to the field of cigarette processing and production, and relates to the production of non-burning cigarettes, in particular to a method for preparing non-burning cigarettes from corn husk fiber. Background technique [0002] When the cigarette is burned, it goes through three combustion sections, namely cracking section, pyrolysis section and dry distillation section. Harmful substances in cigarette smoke are mainly produced in the pyrolysis zone and pyrolysis zone. A non-burning cigarette means that there is no need to light the cigarette, and an external heat source is used to provide a dry distillation environment for the cigarette to assist in evaporating the smoke that can be smoked. The non-burning cigarette has no cracking and pyrolysis combustion section, which effectively reduces the harm of smoking. [0003] At present, non-burning cigarettes are mostly rolled from tobacco sheets, and tobacco sheets are still tobacco p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A24B3/14A24B15/18
CPCA24B3/14A24B15/18
Inventor 彭荣淮葛良成时清屏彭程彭玮
Owner 彭荣淮