Novel magnesium-based cementing material and magnesium-based cementing material floor preparation method

A magnesia cementitious material and a new type of technology, applied in buildings, building structures, floors, etc., can solve the problems of complex installation and maintenance, high price, easy to mildew and service life, and achieve simple installation and maintenance and improve utilization rate. , the effect of improving physical properties

Inactive Publication Date: 2018-12-18
上海唐盾材料科技有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] (1) Solid wood flooring, the resources are becoming more and more scarce, the price is high, the physical properties are poor, the installation and maintenance are complicated, and the non-combustibility is poor;
[0004] (2) Solid wood composite flooring has poor non-combustibility and high price. When the cost is reduced, the adhesive may have free formaldehyde;
[0005] (3) Laminate flooring reduces texture and comfort;
[0006] (4) The performance and comfort of bamboo flooring are average, the installation and maintenance are more complicated, the service life is short due to mildew, and the non-combustibility is poor;
[0007] (5) PVC flooring is mainly a by-product of the petroleum industry, with average texture and comfort. It is widely used in public places, and its non-combustibility is not the highest;
[0008] (6) Traditional floors are rarely used in ground radiant heating environments. On the one hand, the problem of deformation, discoloration, cracking, and abnormal noise has not been completely resolved; key performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel magnesium-based cementing material and magnesium-based cementing material floor preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Prepare magnesia cemented boards with a thickness of 8mm, use commercially available environmentally friendly adhesives to compound solid wood veneers with a thickness of 2mm, cut and shape according to sales requirements, and make tenons and grooves in double-end milling equipment, and the style is flat buckles.

[0047]According to embodiment 1, the thick 10mm of the magnesia gel floor made, density is 1.2g / cm 3 , dry flexural strength (tested according to 7019-1997 "Fiber Cement Products Test Method", refer to the standard GB25970-2010 "non-combustible inorganic composite board") 22.8mPa, wet flexural strength 21.2mPa, flexural strength softening coefficient is 0.93 (21.2 / 22.8), 24h water absorption thickness expansion rate of 0.2%, formaldehyde emission of 0.1mg / L, surface resistance to cold and heat cycles without cracks and bubbles, non-flammability level is A.

[0048] The magnesia cementitious floor prepared according to Example 1 has the appearance and texture ...

Embodiment 2

[0050] Prepare a 10mm thick magnesia cementitious plate, surface UV printing treatment, cut and shape according to sales requirements, and make tenons and grooves in double-end milling equipment, and the style is a lock.

[0051] The magnesia cementitious floor that makes according to embodiment 2 is thick 10mm, and dry state flexural strength (by 7019-1997 " fiber cement product test method " detects, with reference to standard GB25970-2010 " noncombustible inorganic composite board ") 33.5mPa, wet The flexural strength in the state is 29.5mPa, the softening coefficient is 0.88 (ie 29.5 / 33.5), the 24h water absorption thickness expansion rate is 0.2%, the formaldehyde emission is 0.1mg / L, the surface is resistant to cold and heat cycles without cracks and bubbles, and the non-flammability level is Grade A.

[0052] The magnesia cementitious floor prepared according to Example 2 is printed and decorated, and its appearance and texture can imitate many common decorative materia...

Embodiment 3

[0054] Prepare a magnesia cementitious board with a thickness of 12mm, use commercially available environmentally friendly adhesives to compound PVC materials with a thickness of 2mm, cut and shape according to sales requirements, and make tenons and grooves in double-end milling equipment, and the style is a lock.

[0055] The magnesia cementitious floor that makes according to embodiment 3 is thick 14mm, and density is 1.2g / cm Board") 31.3mPa, wet bending strength 29.5mPa, softening coefficient 0.94 (ie 29.5 / 31.3), 24h water absorption thickness expansion rate 0.2%, formaldehyde emission 0.1mg / L, surface resistance to cold and heat cycles without cracks Bubbling, non-combustibility level is A level. It has the appearance and texture of solid wood flooring, comfortable feet, simple installation and maintenance, greatly improved fire and water resistance, and significantly improved the utilization of wood resources and saved costs.

[0056] The magnesia gelled PVC floor prepa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of composite building decoration materials, particularly to a novel magnesium-based cementing material and a magnesium-based cementing material floor preparation method, wherein the raw materials of the magnesium-based cementing material comprise, by weight, 100 parts of magnesium oxide powder, 15-25 parts of sericite powder, 6-7 parts of an Al2O3 filler, 25-32 parts of bamboo chips, 5-7 parts of perlite, 0.2-1 part of citric acid, 0.5-1 part of a composite phosphate, and 45-60 parts of a composite sulfate. According to the present invention, the magnesium-based cementing material floor has the substantially improved physical property, can solve the disadvantages of fire intolerance, and easy deformation, cracking and discoloration after contacting of water and heat sources of the traditional floor, has advantages of simple installation, simple maintenance, heat storage, temperature adjustment, humidity adjustment and the like, and has the improved utilization rate in the case of the increasingly-reduced forest resources.

Description

technical field [0001] The invention relates to the field of composite building decoration materials, in particular to a novel magnesia cementitious material and a preparation method for the magnesia cementitious material floor. Background technique [0002] Commonly used floors include wood flooring and PVC flooring. Wooden flooring is mainly divided into solid wood flooring, solid wood composite flooring, laminate flooring, and bamboo flooring. Advantages of flooring, and excellent physical properties; Laminate flooring is wear-resistant and easy to take care of; Bamboo flooring is beautiful and practical, saving wood resources; PVC flooring is more wear-resistant, stain-resistant, environmentally friendly and non-toxic, etc., but the existing flooring products are also different to varying degrees There are the following technical defects: [0003] (1) Solid wood flooring, the resources are becoming more and more scarce, the price is high, the physical properties are poo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/10E04F15/08C04B111/20C04B111/28C04B111/60
CPCC04B28/105C04B2111/00017C04B2111/00025C04B2111/00612C04B2111/20C04B2111/28C04B2111/60C04B2201/20C04B2201/50E04F15/08C04B14/20C04B14/303C04B18/265C04B14/18C04B24/06C04B22/16C04B22/143C04B22/148C04B22/149C04B22/142
Inventor 沃成昌沃研
Owner 上海唐盾材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap