Sound insulating material and preparation method thereof

A technology of sound insulation materials and foam ceramics, applied in the field of materials, can solve problems such as flammability, high VOC concentration, and complicated preparation process, and achieve the effects of reducing bulk density, promoting uniform distribution, and high melting point

Active Publication Date: 2018-12-21
广州凝博科技有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it has the disadvantages of complicated preparation process, high VOC concentration and flammability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sound insulating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A sound insulation material, made of the following components in parts by weight: 60 parts of high damping silicone rubber, 4 parts of hydroxyl silicone oil, 12 parts of silica airgel, 1 part of dicumyl peroxide, PP resin 60 parts, 18 parts of turpentine, 20 parts of white carbon black, 23 parts of foam ceramic powder, 2 parts of barium sulfate, 0.4 parts of sodium stearate, 0.3 parts of active zinc oxide, 6 parts of diatomaceous earth, 3 parts of zinc borate, high ethylene 5 parts of base silicone oil, 0.2 parts of silane coupling agent, 3 parts of vulcanizing agent, and 1.4 parts of accelerator.

[0032] A method for preparing a sound-insulating material, comprising the steps of:

[0033] Step 1. Weighing: Weigh the components used according to the weight ratio;

[0034] Step 2. Melting: Add PP resin pellets to the kneader to melt and plasticize, slowly add silica airgel, foam ceramic powder, barium sulfate, diatomaceous earth, zinc borate, high vinyl silicone oil, alu...

Embodiment 2

[0044] A sound insulation material, made of the following components in parts by weight: 65 parts of high damping silicone rubber, 4.5 parts of hydroxyl silicone oil, 15 parts of silica airgel, 1.2 parts of dicumyl peroxide, PP resin 65 parts, 19 parts of turpentine, 22 parts of white carbon black, 25 parts of foam ceramic powder, 2.5 parts of barium sulfate, 0.5 parts of sodium stearate, 0.35 parts of active zinc oxide, 7 parts of diatomaceous earth, 4 parts of zinc borate, high ethylene 6 parts of base silicone oil, 0.25 parts of aluminate coupling agent, 3.5 parts of vulcanizing agent, and 1.5 parts of accelerator.

[0045] A method for preparing a sound-insulating material, comprising the steps of:

[0046] Step 1. Weighing: Weigh the components used according to the weight ratio;

[0047] Step 2. Melting: Add PP resin pellets to the kneader to melt and plasticize, slowly add silica airgel, foam ceramic powder, barium sulfate, diatomaceous earth, zinc borate, high vinyl s...

Embodiment 3

[0057] A sound insulation material, made of the following components in parts by weight: 70 parts of high damping silicone rubber, 5 parts of hydroxyl silicone oil, 18 parts of silica airgel, 1.4 parts of dicumyl peroxide, PP resin 70 parts, 21 parts of turpentine, 24 parts of white carbon black, 29 parts of foam ceramic powder, 3 parts of barium sulfate, 0.7 parts of sodium stearate, 0.45 parts of active zinc oxide, 8 parts of diatomaceous earth, 5 parts of zinc borate, high ethylene 7 parts of base silicone oil, 0.35 parts of aluminate coupling agent, 4 parts of vulcanizing agent, and 1.7 parts of accelerator.

[0058] A method for preparing a sound-insulating material, comprising the steps of:

[0059] Step 1. Weighing: Weigh the components used according to the weight ratio;

[0060] Step 2. Melting: Add PP resin pellets to the kneader to melt and plasticize, slowly add silica airgel, foam ceramic powder, barium sulfate, diatomaceous earth, zinc borate, high vinyl silicon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
tensile strength at breakaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a sound insulating material. The sound insulating material is prepared from the following components in parts by weight: 60 to 80 parts of high damping silicone rubber, 4 to 6parts of hydroxy silicone oil, 12 to 25 parts of silica aerogel, 1 to 2 parts of dicumyl peroxide, 60 to 80 parts of PP resin, 18 to 25 parts of turpentine, 20 to 30 parts of white carbon black, 23 to38 parts of foam ceramic powder, 2 to 4 parts of barium sulfate, 0.4 to 0.9 part of sodium stearate, 0.3 to 0.5 part of active zinc oxide, 6 to 10 parts of diatomaceous earth, 3 to 7 parts of zinc borate, 5 to 8 parts of high vinyl silicone oil, 0.2 to 0.4 part of aluminate coupling agent, 3 to 5 parts of vulcanizing agent, and 1.4 to 1.9 parts of accelerator. The invention also discloses a preparation method of the sound insulating material. The sound insulating material provided by the invention has the characteristics of light weight, good mechanical performance, fire retarding, and effectively absorbing low-frequency sound waves, and has the advantages of simple preparation method, low cost and mass production.

Description

technical field [0001] The invention relates to the technical field of materials, in particular to a sound-insulating material and a preparation method thereof. Background technique [0002] Noise pollution has become a global environmental problem and has seriously affected people's production and life. The demand for sound-absorbing materials in modern society is increasing, and the performance requirements for sound-absorbing materials are also getting higher and higher. Existing sound-absorbing materials have good sound-absorbing performance in the high-frequency band of noise, but poor sound-absorbing performance in the low-frequency band. How to improve the sound-absorbing performance of sound-absorbing materials in the low-frequency range has become a difficult point in the field of sound-absorbing materials research. [0003] Existing decorative materials have waterproof, fireproof, anti-aging, poor impact resistance, high energy consumption of materials, are not e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08L23/12C08L83/07C08K7/26C08K3/36C08K3/30C08K3/22C08K3/38C08K5/098C08K5/10
CPCC08L23/12C08L83/04C08K2003/3045C08K2003/2296C08K2003/387C08L2205/035C08L2205/025C08L2201/02C08K7/26C08K3/36C08K3/30C08K3/22C08K3/38C08K5/098C08K5/10
Inventor 海苗苗李明珠
Owner 广州凝博科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap