Flame-retardant engineering plastic and preparation method thereof

A technology of engineering plastics and raw materials, applied in the field of flame-retardant engineering plastics and its preparation, can solve problems such as equipment operation failure, unsatisfactory effect, coating peeling, etc., and achieve effective flame retardancy, light weight, and remarkable effect

Inactive Publication Date: 2018-12-25
桐城市和义塑业有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the prolongation of the running time, the phenomenon of coating peeling often occurs, which will cause the equipment to malfunction; The effect of surface wear resistance, but the effect is still not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of flame-retardant engineering plastics, which is composed of the following raw materials by weight:

[0023] 30 parts of high-density polyethylene, 30 parts of polyphenylene sulfide, 20 parts of polyethylene terephthalate, 10 parts of polytetrafluoroethylene, 10 parts of polypropylene, 15 parts of flame-retardant and fire-resistant quartz fiber filler, 10 parts of natural rubber , 5 parts of magnesium oxide, 6 parts of quartz fiber, 8 parts of modified polyphenylene ether, 5 parts of diatomaceous earth, 3 parts of halogen-free flame retardant, 2 parts of lubricant, 1 part of antioxidant, and 1 part of plasticizer.

[0024] A preparation method of flame-retardant engineering plastics, comprising the following steps:

[0025] (1) Get each component in the above-mentioned raw material by weight, and evenly mix and heat to molten state;

[0026] (2) kneading the raw materials obtained in the step (1) by a kneader;

[0027] (3) the raw material gained in the step (...

Embodiment 2

[0034] A kind of flame-retardant engineering plastics, which is composed of the following raw materials by weight:

[0035] 35 parts of high-density polyethylene, 35 parts of polyphenylene sulfide, 30 parts of polyethylene terephthalate, 15 parts of polytetrafluoroethylene, 15 parts of polypropylene, 17.5 parts of flame-retardant and fire-resistant quartz fiber filler, 15 parts of natural rubber , 6.5 parts of magnesium oxide, 7 parts of quartz fiber, 9 parts of modified polyphenylene ether, 6 parts of diatomaceous earth, 4 parts of halogen-free flame retardant, 3 parts of lubricant, 2 parts of antioxidant, and 2 parts of plasticizer.

Embodiment 3

[0037] A kind of flame-retardant engineering plastics, which is composed of the following raw materials by weight:

[0038] 40 parts of high-density polyethylene, 40 parts of polyphenylene sulfide, 40 parts of polyethylene terephthalate, 20 parts of polytetrafluoroethylene, 20 parts of polypropylene, 20 parts of flame-retardant and fire-resistant quartz fiber filler, 20 parts of natural rubber , 8 parts of magnesium oxide, 8 parts of quartz fiber, 10 parts of modified polyphenylene ether, 7 parts of diatomaceous earth, 5 parts of halogen-free flame retardant, 4 parts of lubricant, 3 parts of antioxidant, and 3 parts of plasticizer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses flame-retardant engineering plastic and a preparation method thereof. The flame-retardant engineering plastic is prepared from, by weight, 30-40 parts of high density polyethylene, 30-40 parts of polyphenylene sulfide, 20-40 parts of polyethylene terephathalate, 10-20 parts of polytetrafluoroethylene, 10-20 parts of polypropylene, 15-20 parts of flame-retardant and fireproof quartz fiber packing, 10-20 parts of natural rubber, 5-8 parts of magnesium oxide, 6-8 parts of quartz fiber, 8-10 parts of modified polyphenylene oxide, 5-7 parts of diatomite, 3-5 parts of a halogen-free flame retardant, 2-4 parts of a lubricating agent, 1-3 parts of an antiager and 1-3 parts of a plasticizer. The engineering plastic prepared is remarkable and durable in effect, good in mechanical properties, effective in flame retardance, light in weight, high in strength and wide in market prospect in application and popularization of flammable environments.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a flame-retardant engineering plastic and a preparation method thereof. Background technique [0002] Engineering plastics are engineering materials and plastics that replace metals to make machine parts, etc. Engineering plastics have excellent comprehensive performance, high rigidity, low creep, high mechanical strength, good heat resistance, and good electrical insulation. They can be used in harsh chemical and physical environments for a long time, and can replace metals as engineering structural materials. , but the price is more expensive and the output is smaller. Compared with general-purpose plastics, engineering plastics can meet higher requirements in terms of mechanical properties, durability, corrosion resistance, heat resistance, etc., and are more convenient to process and can replace metal materials. Engineering plastics are widely used in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L81/02C08L67/02C08L27/18C08L23/12C08L7/00C08L71/12C08K13/04C08K7/10C08K3/22C08K7/26C08K5/12
CPCC08L23/06C08K2003/222C08L2201/02C08L2205/035C08L81/02C08L67/02C08L27/18C08L23/12C08L7/00C08L71/126C08K13/04C08K7/10C08K3/22C08K7/26C08K5/12
Inventor 毕力高敏陈鹏刘勇
Owner 桐城市和义塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap