Boron-carbon-nitrogen film encapsulating highly-oriented boron nitride nanocrystal and preparation method of boron-carbon-nitrogen film
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A nanocrystalline, boron nitride technology, applied in metal material coating process, vacuum evaporation plating, coating and other directions, can solve the problems of poor film stability and immaturity
Active Publication Date: 2019-01-08
JILIN UNIV
View PDF3 Cites 6 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The boron carbon nitrogen thin films obtained by different preparation methods are different, most of them are amorphous structure, there is phase separation in some thin films, and the stability of thin films is not good
Previous studies most
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] The preparation of boron carbon nitrogen film under different substrate temperature of embodiment 1
[0033] (1) After the silicon (100) single wafer cut according to the required size is ultrasonically cleaned in acetone, ethanol, and deionized water, it is dried with nitrogen and sent to the vacuum deposition chamber; the vacuum degree in the deposition chamber is pumped to 3×10 -5 Pa, set the substrate temperature as room temperature, 250°C, 400°C, 500°C, 600°C.
[0034] (2) Continue vacuuming until the back vacuum of the deposition chamber reaches 3×10 -5 Pa, feed the reaction working gas argon until the working pressure is 2Pa, and the flow rate of the working gas argon is 50 sccm (no nitrogen added).
[0035] (3) The distance between the substrate and the target is 8 cm, and the negative bias of the substrate is -100V, and the sputtering power of the target is set to 150W, and then it starts to glow. After 2 minutes of pre-sputtering, the target baffle is removed...
Embodiment 2
[0040] Preparation of boron-carbon-nitrogen thin films under different nitrogen flow rates in Example 2
[0041] (1) After the silicon (100) single wafer cut according to the required size is ultrasonically cleaned in acetone, ethanol, and deionized water, it is dried with nitrogen and sent to the vacuum deposition chamber; the vacuum degree in the deposition chamber is pumped to 3×10-5 Pa, heat the substrate to 500°C.
[0042] (2) Continue vacuuming until the back vacuum of the deposition chamber reaches 3×10 -5 At Pa, the reaction working gas argon and nitrogen are introduced until the working pressure is 2Pa. The flow rate of the working gas argon is 50 sccm, and the flow rate of nitrogen is set to 0 sccm, 10 sccm, 20 sccm, 30 sccm, 40 sccm, 50 sccm respectively.
[0043] (3) The distance between the substrate and the target is 8 cm, and the negative bias of the substrate is -150V, and the sputtering power of the target is set to 150W, and then it starts to glow. After 2 m...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a boron-carbon-nitrogen film encapsulating highly-oriented boron nitride nanocrystal and a preparation method of the boron-carbon-nitrogen film, and belongs to the technical field of film materials and preparation thereof. The boron-carbon-nitride film is of an amorphous structure containing boron nitride nanocrystals and growing on a silicon substrate. According to the preparation method, boron nitride containing carbon is used as a target material, and the boron-carbon-nitrogen film is prepared in a deposition chamber of a radio frequency magnetron sputtering device,wherein the substrate temperature ranges from room temperature to 600 DEG C, working gases comprise an argon gas and a nitrogen gas, flow rates are 50 sccm and 0-50 sccm respectively, and the workingpressure is 1 to 3 Pa. Ordered and controllable growth of the orientation of boron nitride nanocrystals in a film can be realized by adjusting technological parameters, and the obtained boron-carbon-nitride film has an optical band gap of about 2.7 to 4.5 eV, and has good and adjustable optical properties. The preparation method provided by the invention has the advantages of simple and safe process, mature technology, high sputtering rate, uniform deposition film, controllable size and the like, and is suitable for industrial mass production and promotion.
Description
technical field [0001] The invention belongs to the technical field of thin film materials and preparation thereof, and specifically relates to a boron carbon nitrogen thin film enveloping oriented boron nitride nanocrystals and a method for preparing a thin film with controllable orientation of boron nitride nanocrystals. Background technique [0002] Boron carbon nitrogen materials have attracted extensive attention because of their excellent properties such as high hardness, wear resistance, low friction coefficient, low dielectric constant, thermal stability and chemical stability of carbon materials and boron nitride materials. In addition to being used as Outside the hard protective coating, the bandgap can be adjusted by adjusting its composition and chemical bond content, which is very important for its application in semiconductor devices, luminescent materials, sensors, light energy conversion materials, field effect transistors, electromagnetic storage, vacuum micr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more