Light-steel house spray-building type bark-like wall paint

A bark and house technology, which is applied in the field of spray-type imitation bark wall coatings for light steel houses, to achieve the effects of reducing the number of repeated decorations, adjusting the air humidity, and having a small specific gravity

Inactive Publication Date: 2019-01-11
黎金莲
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no special wall coating for light steel houses in the prior art. With the development and popularity of light steel houses in our country, light steel houses and various building materials will surely become people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of spraying type imitation bark wall coating for light steel houses, comprising the following raw materials in parts by weight: 35 parts of shell powder, 25 parts of acrylic floor paint, 12 parts of diatom mud, 7.5 parts of plant fiber, 12.5 parts of gypsum, 3 parts of pigment, 11 parts of glue, 2 parts of additive.

[0032] The preparation method of the shell powder is as follows: soak the shells in an acid solution for 1 hour, then wash them twice with distilled water, dry them at 80°C for 5 hours, crush them into shell powder with a particle size of 1.0 mm, and place them in The catalyst is calcined at 1000°C to 1200°C for 1.5h, and after cooling, it is pulverized with a nano pulverizer to obtain shell powder with an average particle size of 500nm.

[0033] The plant fibers are derived from corn stalks and cotton stalks, and are extracted through grinding and processing.

[0034] The pigment is a combination of iron oxide brown, iron oxide yellow and iron oxi...

Embodiment 2

[0040] A kind of light-steel house spraying type bark-like wall surface coating, comprises the raw material of following parts by weight: 38 parts of shell powder, 27 parts of acrylic floor paint, 13 parts of diatom mud, 6 parts of plant fiber, 12 parts of gypsum, 4 parts of pigment, 10 parts of glue, 2 parts of additive.

[0041] The preparation method of the shell powder is as follows: soak the shells in an acid solution for 1 hour, then wash them twice with distilled water, dry them at 80°C for 5 hours, crush them into shell powder with a particle size of 1.0mm, and place them in The catalyst is calcined at 1000°C to 1200°C for 1.5h, and after cooling, it is pulverized with a nano pulverizer to obtain shell powder with an average particle size of 500nm.

[0042] The plant fiber is derived from soybean stalks and bamboo, and is made by crushing, processing and extracting.

[0043] The pigment is a combination of iron oxide brown, iron oxide yellow and iron oxide red.

[00...

Embodiment 3

[0049] A kind of light-steel house spraying type bark-like wall surface coating, comprises the following raw materials in parts by weight: 35 parts of shell powder, 26 parts of acrylic floor paint, 13 parts of diatom mud, 8 parts of plant fiber, 14 parts of gypsum, 3.5 parts of pigment, 12 parts of glue, 2 parts of additive.

[0050] The preparation method of the shell powder is as follows: soak the shells in an acid solution for 1 hour, then wash them twice with distilled water, dry them at 80°C for 5 hours, crush them into shell powder with a particle size of 1.0mm, and place them in The catalyst is calcined at 1000°C to 1200°C for 1.5h, and after cooling, it is pulverized with a nano pulverizer to obtain shell powder with an average particle size of 500nm.

[0051] The plant fiber is derived from rice husk, rice straw and wheat straw, and is made by crushing, processing and extracting.

[0052] The pigment is composed of iron oxide yellow, iron oxide black and iron oxide r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses light-steel house spray-building type bark-like wall paint. The light-steel house spray-building type bark-like wall paint is prepared from 30-40 parts by weight of shell powder, 20-30 parts by weight of acrylic floor paint, 10-15 parts by weight of diatom mud, 5-10 parts by weight of plant fibers, 10-15 parts by weight of gypsum, 1-5 parts by weight of a pigment, 7-15 parts by weight of glue and 1-3 parts by weight of additives. The light-steel house spray-building type bark-like wall paint has composite colors, three-dimensional texture, luxurious and elegant decorative effects, realistic bark imitation effects and natural, beautiful and decent texture, can be used for imitation of various patterns of the bark, has strong moisture-proof, waterproof, fire-proof, mildew-proof and alkali-resistant functions, is environmentally friendly, does not contain any toxic or harmful substances after testing, does not influence the human health and realizes direct use after spraying.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a spray-built bark-like wall surface paint for light steel houses. Background technique [0002] Light steel housing is a new type of housing construction technology that is popular in the world at present. This new construction technology of light steel housing is a project vigorously promoted by the country. Its invention subverts the entire structural model and improves the living environment. It is deeply loved by people. The construction technology of light-weight steel structure low-rise residential buildings evolved on the basis of North American-style wood structure construction technology. After more than a hundred years of development, it has formed a mature construction with excellent physical properties, flexible space and shape, easy construction, and various forms. system. In the North American continent, which is known as the best living environment in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B111/20C04B111/27C04B111/28C04B111/90
CPCC04B28/14C04B2111/00017C04B2111/00025C04B2111/00508C04B2111/20C04B2111/2092C04B2111/27C04B2111/28C04B2111/905C04B14/08C04B14/28C04B14/308C04B18/24C04B22/124C04B24/2623C04B24/2641C04B24/383C04B24/281C04B2103/0045
Inventor 邓天华黎金莲
Owner 黎金莲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com