Insulating and heat-insulating spray-coated polyurethane foam

A technology for spraying polyurethane and thermal insulation, applied in the field of spraying polyurethane foam, can solve the problems of inconvenient use and cumbersome maintenance, and achieve the effects of high thermal insulation effect, improved thermal insulation effect and low water absorption

Inactive Publication Date: 2019-01-25
酷泰克保温科技江苏有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing thermal insulation materials are all assembled in modules for thermal insulation. For pressure vessels and equipment with different shapes, it is necessary to customize thermal insulation materials of different shapes, which is inconvenient to use and cumbersome to maintain.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0014] The invention is an insulating and heat-insulating spray polyurethane foam. The formula is mainly divided into two kinds of materials, A and B. When used, the ratio is 1:1. Among them, the material A is isocyanate, and the formula of B material is: polyester polystyrene Ether 20%, A phenol polymer 20%, polyether polyol 20%, hexafluoropropane 10%, B polymer 10%, triphosphonate 10%, triethyl phosphate 5%, dihydroxydiethyl ether 2%, triethanolamine 1%, dimethylcyclohexylamine 1%, dibutyltin dilaurate <1%, isopropenylbenzene <1%.

example 2

[0016] The invention is an insulating and heat-insulating spray polyurethane foam. The formula is mainly divided into two kinds of materials, A and B. When used, the ratio is 1:1. Among them, the material A is isocyanate, and the formula of B material is: polyester polystyrene Ether 20%, phenol polymer of A 18%, polyether polyol 21%, hexafluoropropane 13%, polymer of B 12%, triphosphonate 8%, triethyl phosphate 4%, dihydroxydiethyl ether 1%, triethanolamine 1%, dimethylcyclohexylamine 1%, dibutyltin dilaurate <1%, isopropenylbenzene <1%.

example 3

[0018] The invention is an insulating and heat-insulating spray polyurethane foam. The formula is mainly divided into two kinds of materials, A and B. When used, the ratio is 1:1. Among them, the material A is isocyanate, and the formula of B material is: polyester polystyrene Ether 17%, phenol polymer of A 18%, polyether polyol 18%, hexafluoropropane 13%, polymer of B 13%, triphosphonate 9%, triethyl phosphate 4%, dihydroxydiethyl ether 3%, triethanolamine 3%, dimethylcyclohexylamine 1%, dibutyltin dilaurate <1%, isopropenylbenzene <1%.

[0019] In the above example, the phenol polymer of A is a phenol polymer obtained by the reaction of formaldehyde, propylene oxide and ethylene oxide; the polymer of B is produced by the reaction of ethylenediamine and methyloxyflurane polymer.

[0020] The above examples are sprayed using the following spraying process, the steps are as follows:

[0021] 1) Preparation: Keep the ambient temperature above 10°C, keep the humidity below 70%,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an insulating and heat-insulating spray-coated polyurethane foam, wherein the components of the formula are mainly divided into two materials A and B, the material A and the material B are matched according to a ratio of 1:1 during the use, the material A is made of isocyanate, and the material B comprises 15-25% of polyester polyether, 10-20% of the phenol polymer of the material A, 15-25% of polyether polyol, 5-15% of hexafluoropropane, 5-15% of the polymer of the material b, 5-15% of triphosphonate, 3-7% of triethyl phosphate, 1-5% of diethylene glycol, 1-5% of triethanolamine, 1-3% of dimethylcyclohexylamine, less than 1% of dibutyltin dilaurate, and less than 1% of isopropenyl benzene. According to the present invention, the insulating and heat-insulating spray-coated polyurethane foam is provided, and has advantages of improved heat resistance, improved heat insulation effect, strong viscosity, high heat resistance, fire retardation, low water absorption and low deformation rate.

Description

technical field [0001] The invention belongs to the field of heat insulation, and in particular relates to a sprayed polyurethane foam for heat insulation and heat insulation. Background technique [0002] Existing thermal insulation materials are all assembled in modules for thermal insulation. For pressure vessels and equipment with different shapes, it is necessary to customize thermal insulation materials of different shapes, which is inconvenient to use and cumbersome to maintain. [0003] The full name of polyurethane foam (PUR) is a one-component polyurethane foam caulking agent, commonly known as foaming agent and foaming glue. It is the product of the cross combination of aerosol technology and polyurethane foam technology. It is a polyurethane prepolymer A special polyurethane product filled with foaming agent, catalyst and other components in a pressure-resistant aerosol can. When the material is sprayed out of the aerosol can, the foamy polyurethane material will...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/66C08G18/40C08G18/48C08G18/42C08G18/32C08J9/14C08K5/521C08K5/5333C08G101/00
CPCC08G18/3206C08G18/3281C08G18/4018C08G18/4244C08G18/4804C08G18/4879C08G2101/00C08J9/146C08J2203/142C08J2375/06C08J2375/08C08K5/521C08K5/5333
Inventor 冀怀岩司飞
Owner 酷泰克保温科技江苏有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap