C-C-B4C combined tread sweeper grinder and preparation method thereof

A C-C-B4C, cleaner technology, applied in the direction of vehicle cleaning, vehicle maintenance, transportation and packaging, etc., can solve the problems of slag dropping and adverse effects caused by the environment, and achieve stability, avoid heat decay, and high bonding strength Effect

Active Publication Date: 2019-02-05
马鞍山市雷狮轨道交通装备有限公司
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the serious slag phenomenon caused by the thermal decomposition of the resin in the existing grinding wheel, and the problem that the thermal decomposition of the resin during the friction process and the release of organic gas may cause adverse effects on the environment, the present invention provides a C-C-B 4 C combined with tread cleaner grinder and its preparation method, so that the resin is decomposed in the manufacturing stage and forms a carbon bonded network. In the process of use, B is used 4 C prevents oxidation of the carbon-binding network and generates B 2 o 3 This low-melting product eventually forms a C-C-B 4 C-Combined Tread Sweeper Grinder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • C-C-B4C combined tread sweeper grinder and preparation method thereof
  • C-C-B4C combined tread sweeper grinder and preparation method thereof
  • C-C-B4C combined tread sweeper grinder and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The present invention will be described below with reference to specific examples. Those skilled in the art can understand that these examples are only used to illustrate the present invention and do not limit the scope of the present invention in any way.

[0038] A kind of C-C-B of this embodiment 4 C is combined with the preparation method of tread sweeper grinder, specifically comprises the following steps:

[0039] (1) Batching: Batching according to the following formula, the specific parameters are shown in Table 3, the batching can be carried out by using the case name or automatic batching and feeding system, and the batching error is required to be ±0.05g, including the following components and weight percentage content: 8% CARBORES P , 12% copper-plated graphite, 20% SiC coated carbon fiber, 15% 55% copper fiber, 5% 1000 mesh boron carbide, 40% 100 mesh secondary reduced iron powder;

[0040] (2) Mixing: After the raw materials are prepared according to the...

Embodiment 2

[0055] A kind of C-C-B of this embodiment 4 C is combined with the preparation method of tread sweeper grinder, specifically comprises the following steps:

[0056] (1) Batching: Batching according to the following formula, the specific parameters are shown in Table 3, the batching can be carried out by using the case name or automatic batching and feeding system, and the batching error is required to be ±0.05g, including the following components and weight percentage content: 5% CARBORES P , 15% copper-coated graphite, 15% SiC coated carbon fiber, 13% 55% copper fiber, 7% 1000 mesh boron carbide, 45% iron powder;

[0057] (2) Mixing: After the raw materials are prepared according to the formula ratio, they are put into the mixer in turn for pre-homogenization and fiber opening, and the pre-homogenization time is 900 seconds;

[0058] (3) Granulation: Add 6% organic solvent afterwards, wherein the organic solvent includes FF liquid (furfural) and ethylene glycol, W (FF liquid...

Embodiment 3

[0064] A kind of C-C-B of this embodiment 4 C is combined with the preparation method of tread sweeper grinder, specifically comprises the following steps:

[0065] (1) Batching: Batching according to the following formula, the specific parameters are shown in Table 3, the batching can be carried out by using the case name or the automatic batching and feeding system, and the batching error is required to be ±0.05g, including the following components and weight percentage content: 6% CARBORES P , 18% copper-coated graphite, 12% SiC coated carbon fiber, 15% 55% copper fiber, 6% 1000 mesh boron carbide, 43% iron powder;

[0066] (2) Mixing: After the raw materials are prepared according to the formula ratio, they are put into the mixer in turn for pre-homogenization and fiber opening, and the pre-homogenization time is 900 seconds;

[0067] (3) Granulation: Then add 8% FF liquid to carry out granulation, the granulation time is 5 minutes, and then the material can be discharged...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a C-C-B4C combined tread sweeper grinder and a preparation method thereof, and belongs to the field of railway transportation equipment. The C-C-B4C combined tread sweeper grinder comprises 5%-10% of a binding agent, 10%-20% of graphite, 10%-25% of carbon fibers, 10%-20% of copper fibers, 5%-8% of boron carbide and 40%-50% of iron powder, the materials are put into a mixerto be homogenized for 10 min to 20 min, then 5%-10% of an organic solvent is added, then pelleting is carried out for 2 min to 5 min for discharging, then the material is put in a drying roller for rotary secondary pelleting and is dried till volatile matter is smaller than 1%, a qualified mixture is obtained, and then the qualified mixture is subjected to cold pressing forming and cured and firedinto the C-C-B4C combined tread sweeper grinder. The carbon-carbon combined manner is adopted, heat fading generated by the grinder in the friction process is effectively avoided, boron carbide serves as a reinforcement assistant to be combined with carbon-carbon combination, the structure is stable, and the situation that residues fall off cannot happen in the friction process.

Description

technical field [0001] The invention belongs to the field of rail transit equipment, and more specifically relates to a C-C-B 4 C Combined tread sweeper grinder and method of making the same. Background technique [0002] The tread cleaner plays the role of cleaning the wheel and increasing the wheel-rail adhesion coefficient to ensure the safety of the service brake. The part of the tread cleaner that directly acts on the wheel is called a grinder. The grinder is a friction part in the tread cleaner that has the functions of cleaning, thickening, and rounding. In view of the above functions, the grinder is formed by pressing and solidified. Due to the thermal decomposition characteristics of phenolic resin, the grinder During the long-term grinding process, the grinder plays an extremely important role in driving safety. In the production process of the grinding wheel, phenolic resin is generally used as a binder for hot pressing molding. During the friction process, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C49/08C22C49/14C22C47/14B60S1/68C22C101/10C22C121/02
CPCB60S1/68C22C47/14C22C49/08C22C49/14
Inventor贺子铭彭程林
Owner马鞍山市雷狮轨道交通装备有限公司