A kind of extraction method of cowhide collagen

An extraction method and original protein technology, which is applied in the field of cowhide collagen extraction, can solve the problems of demanding extraction temperature, high collagen loss, and restricting the development of enzymatic methods, so as to simplify the pre-extraction treatment process, reduce protein hydrolysis, shorten The effect of extraction time

Active Publication Date: 2021-11-16
GUIZHOU MOUNT FANJING ECOLOGICAL AGRI INC
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the hair removal and degreasing process of the prior art causes a lot of collagen loss, and the pre-extraction treatment generally first removes the hair and then degreases, which increases the process and requires harsh extraction temperatures, which limits the development of enzymatic methods, and most researchers are committed to How to optimize the extraction effect of enzyme combination, but there are few studies on how to reduce the loss rate of collagen in the process of hair removal and degreasing and how to reduce the extraction temperature requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of extraction method of cowhide collagen
  • A kind of extraction method of cowhide collagen

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A method for extracting cowhide collagen, comprising the steps of:

[0034] S1 degreasing and hair removal: immerse the cowhide in water 2.5 times the weight of the cowhide, control the temperature at 40°C, add a hair removal and degreasing compound enzyme preparation with a weight of 0.002 cowhide, treat at a constant temperature for 3 hours, drain, and wash with water;

[0035] S2 Immunization treatment: Put the cowhide in a sodium carbonate solution 1.5 times the weight of the cowhide, maintain the pH at 8.5, and keep the temperature at 25°C. After rotating for 20 minutes, take it out and drain it, add water 1.3 times the weight of the cowhide, and heat it at 600 rpm. Stir at a high speed under the condition of 1 min to make a paste, and process it with a high-pressure homogenizer to make a kraft pulp;

[0036] S3 extraction: Add organic acid solution to the cowhide pulp after immune treatment to adjust the pH to 6.8, then add an activated compound enzyme preparation...

Embodiment 2

[0048] A method for extracting cowhide collagen, comprising the steps of:

[0049] S1 degreasing and hair removal: immerse the cowhide in water twice the weight of the cowhide, control the temperature at 35°C, add a hair removal and degreasing compound enzyme preparation with a weight of 0.001 cowhide, treat at a constant temperature for 2 hours, drain, and wash with water;

[0050] S2 immune treatment: place cowhide in a sodium carbonate solution 1.2 times the weight of cowhide, keep the pH at 7.8, and keep the temperature at 20 °C. Stir at a high speed under the condition of 1 min to make a paste, and process it with a high-pressure homogenizer to make a kraft pulp;

[0051] S3 extraction: Add organic acid solution to the cowhide pulp after immune treatment to adjust the pH to 6, then add an activated compound enzyme preparation 0.002 times the weight of cowhide, stir at 100r / min for 5h at natural temperature, and use a filter press to solidify The liquid is separated to ob...

Embodiment 3

[0063] A method for extracting cowhide collagen, comprising the steps of:

[0064] S1 degreasing and hair removal: immerse the cowhide in water 2.2 times the weight of the cowhide, control the temperature at 37°C, add a hair removal and degreasing compound enzyme preparation with a weight of 0.0012 cowhide, treat it at a constant temperature for 2.5 hours, drain it, and wash it with water;

[0065] S2 immune treatment: place cowhide in a sodium carbonate solution 1.3 times the weight of cowhide, keep the pH at 8.0, and at a temperature of 25°C, turn it for 18 minutes, take it out and drain it, add water 1.2 times the weight of cowhide, and heat at 550 rpm Stir at a high speed under the condition of 1 min to make a paste, and process it with a high-pressure homogenizer to make a kraft pulp;

[0066] S3 extraction: Add organic acid solution to the cowhide pulp after immune treatment to adjust the pH to 6.5, then add an activated compound enzyme preparation 0.003 times the weight...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to the technical field of biological collagen preparation, in particular to a method for extracting cowhide collagen, comprising the following steps: S1 degreasing and depilation: immersing the cowhide in water, adding a depilatory degreasing compound enzyme preparation under temperature control, constant temperature treatment, draining Take out and wash with water; S2 immune treatment: put cowhide in sodium carbonate solution, maintain pH 7.8-8.5, temperature 20-25°C, rotate for 15-20min, take out and drain, add water and stir at high speed into a paste, processed with a high-pressure homogenizer to make kraft pulp; S3 extraction: add organic acid solution to the kraft pulp to adjust pH, add activated compound enzyme preparation, stir at natural temperature for 5‑7h, and separate solid and liquid , to obtain an extract for subsequent use; S4 purification: the extract is centrifuged to obtain a supernatant to obtain a collagen solution; the method of the invention improves the purity and yield of the collagen, and shortens the extraction time.

Description

technical field [0001] The invention relates to the technical field of biological collagen preparation, in particular to a method for extracting cowhide collagen. Background technique [0002] Collagen is a natural biopolymer synthesized by animal cells. It is widely found in animal skin, bone, cartilage, teeth, tendons, ligaments and blood vessels. The role of the body. Collagen has a stable nature, and it is difficult to decompose it under general processing temperature and short-term heating, so it is difficult to be absorbed by the human body, and the utilization rate of food is low. [0003] At present, the commonly used extraction methods include enzymatic degradation, acid extraction, alkali extraction and recombinant DNA extraction. The acid-base method is not suitable for industrial application due to the violent reaction of strong acid and strong alkali and serious corrosion of equipment. The extraction effect of recombinant DNA is good, but the process is compl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C12P21/06C07K14/78C07K1/14
CPCC07K14/78C12P21/06
Inventor 蒋宇王小清
Owner GUIZHOU MOUNT FANJING ECOLOGICAL AGRI INC