Chemical method silicone heat resistance paint and preparation method thereof

A technology of organic silicon and chemical method, which is applied in the field of heat-resistant paint to achieve strong adhesion, good mechanical properties and good heat insulation effect

Inactive Publication Date: 2019-03-05
陈兴月
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In 2008, the supply and demand of my country's heat-resistant paint market was roughly balanced, but the structure still needs to be optimized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chemical method silicone heat resistance paint and preparation method thereof
  • Chemical method silicone heat resistance paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A chemical method organic silicon heat-resistant paint, comprising the following raw materials in parts by weight: 10 parts of silicone resin solution, 25 parts of anatase titanium dioxide, 10 parts of ultramarine blue, 2 parts of chromium trioxide and 1 part of kaolin.

[0020] The raw materials also include 5 parts by weight of glass powder, 2 parts of asbestos wool, and 5 parts of vitreous silicon dioxide.

[0021] A preparation method of a chemical method organosilicon heat-resistant paint, comprising the following steps:

[0022] 1) Mix and stir the silicone resin liquid, anatase titanium dioxide, ultramarine blue, chromium trioxide and kaolin evenly according to the proportion to obtain a mixture;

[0023] 2) Take 5g of the mixture, brew it with 250ml of boiling water, let it stand for 10 minutes, and filter out the impurities to obtain the chemical method silicone heat-resistant paint.

Embodiment 2

[0025] A chemical method organic silicon heat-resistant paint, comprising the following raw materials in parts by weight: 40 parts of organic silicon resin liquid, 55 parts of anatase titanium dioxide, 20 parts of ultramarine blue, 3 parts of dichromium trioxide and 3 parts of kaolin.

[0026] The raw materials also include 10 parts by weight of glass powder, 3 parts of asbestos wool and 10 parts of vitreous silicon dioxide.

[0027] A preparation method of a chemical method organosilicon heat-resistant paint, comprising the following steps:

[0028] 1) Mix and stir the silicone resin liquid, anatase titanium dioxide, ultramarine blue, chromium trioxide and kaolin evenly according to the proportion to obtain a mixture;

[0029] 2) Take the mixture, add other ingredients to it in turn to obtain the chemical method silicone heat-resistant paint.

Embodiment 3

[0031] A chemical method organic silicon heat-resistant paint, comprising the following raw materials in parts by weight: 15 parts of organic silicon resin liquid, 30 parts of anatase titanium dioxide, 12 parts of ultramarine blue, 2.2 parts of dichromium trioxide and 1.5 parts of kaolin.

[0032] The raw materials also include 6 parts by weight of glass powder, 2.5 parts of asbestos wool, and 7 parts of vitreous silicon dioxide.

[0033] A preparation method of a chemical method organosilicon heat-resistant paint, comprising the following steps:

[0034] 1) Mix and stir the silicone resin liquid, anatase titanium dioxide, ultramarine blue, chromium trioxide and kaolin evenly according to the proportion to obtain a mixture;

[0035] 2) Take the mixture, add other ingredients to it in turn to obtain the chemical method silicone heat-resistant paint.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses chemical method silicone heat resistance paint which belongs to the technical field of heat resistance paint. The paint includes, by weight, the following raw materials: 10-40parts of a silicone resin liquid, 25-55 parts of anatase type titanium dioxide, 10-20 parts of ultramarine, 2-3 parts of chromium oxide, and 1-3 parts of kaolin. The chemical method silicone heat resistance paint utilizes the silicone resin liquid as a film-forming material and utilizes a vitreous silica material, a special ceramic material, zinc phosphate, and a fiber material as fillers to prepare heat preservation and insulation anticorrosion heat resistance paint. After curing, the heat resistance paint has the characteristics of heat resistance, oil resistance, moisture resistance, insulation, strong adhesion, good mechanical properties, and the like, and has good a heat insulation effect; and another purpose of the invention is to provide a preparation method of the chemical method silicone heat resistance paint.

Description

technical field [0001] The invention belongs to the technical field of heat-resistant paint, and in particular relates to a chemical-method organosilicon heat-resistant paint and a preparation method thereof. Background technique [0002] Latex paint is a common name for latex paint. It was born in the middle and late seventies of the 20th century. It is a large class of synthetic resin emulsion paint represented by acrylate copolymer emulsion. Latex paint is a water-dispersible paint. It is based on synthetic resin emulsion, and the filler is refined by adding various additives after grinding and dispersing. Latex paint has many advantages that are different from traditional wall paints, such as easy to paint, fast drying, water-resistant paint film, and good scrub resistance. In my country, it is customary for people to use synthetic resin emulsion as the base material, use water as the dispersion medium, add pigments, fillers (also known as body pigments) and additives, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D7/61C09D5/08C09D5/25
CPCC09D183/04C08K2003/2241C08K2003/2251C09D5/08C09D5/18C08K13/04C08K3/22C08K3/346C08K3/40C08K7/12C08K3/36
Inventor 陈兴月
Owner 陈兴月
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap