Wear-resistant rubber material for baseball cores

A wear-resistant rubber and baseball core technology, applied in the rubber field, can solve the problems that the quality and quality of baseball cannot meet market requirements, toughness and wear resistance cannot be satisfied, etc., to improve toughness, improve dispersion performance, and compatibility. Good results

Inactive Publication Date: 2019-03-08
TIANCHANG ZHENGMU ALUMINUM TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the core material of a solid soft baseball is generally synthetic rubber, and the toughness and wear resistance of the synthetic rubber in the prior art cannot meet the needs of actual use, making the quality and quality of the baseball far from reaching the market. Requirements, so there is an urgent need to develop a high toughness wear-resistant rubber material for baseball cores to solve the problems in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A wear-resistant rubber material for a baseball core. The raw materials include, by weight, 70 parts of nitrile rubber, 38 parts of urea-formaldehyde resin, 40 parts of modified furfural resin, 14 parts of silicon dioxide, 2 parts of calcium sulfate whiskers, nano 10 parts of carbon black, 3.2 parts of bamboo fiber, 2.5 parts of trioctyl trimellitate, 3 parts of liquid stone ester, 3.7 parts of aluminum polyphosphate, 0.3 parts of dicumyl peroxide, 2 parts of rare earth stabilizer, 1 part of glycerin parts, 3.5 parts of curing agent, and 0.2 parts of antioxidant.

Embodiment 2

[0018] A wear-resistant rubber material for a baseball core, the raw materials of which include by weight: 88 parts of nitrile rubber, 28 parts of urea-formaldehyde resin, 65 parts of modified furfural resin, 10 parts of silicon dioxide, 6.5 parts of calcium sulfate whiskers, nano 3 parts of carbon black, 5.7 parts of bamboo fiber, 0.5 part of trioctyl trimellitate, 5 parts of liquid stone ester, 1 part of aluminum polyphosphate, 0.8 part of dicumyl peroxide, 1 part of rare earth stabilizer, 2 parts of glycerin 1.5 parts of curing agent, 0.5 parts of antioxidant;

[0019] Wherein, the preparation method of described modified furfural resin is: barium tungstate and Ti 3 C 2 Perform ball milling and mixing, add furfural resin, and ultrasonically stir to obtain modified furfural resin.

Embodiment 3

[0021] A wear-resistant rubber material for a baseball core. The raw materials include, by weight, 80 parts of nitrile rubber, 33 parts of urea-formaldehyde resin, 55 parts of modified furfural resin, 12 parts of silicon dioxide, 4 parts of calcium sulfate whiskers, nano 6 parts of carbon black, 4 parts of bamboo fiber, 1.5 parts of trioctyl trimellitate, 4 parts of liquid stone ester, 2.5 parts of aluminum polyphosphate, 0.5 parts of dicumyl peroxide, 1.5 parts of rare earth stabilizer, 1.5 parts of glycerin 2 parts, 2 parts of curing agent, 0.35 parts of antioxidant;

[0022] Wherein, the preparation method of described modified furfural resin is: barium tungstate and Ti 3 C 2 Perform ball milling and mixing, add furfural resin, and ultrasonically stir to obtain modified furfural resin;

[0023] The nano barium tungstate, Ti 3 C 2 , The weight ratio of furfural resin is 0.3:0.55:1.45;

[0024] The ball milling speed is 100rpm, and the ball milling time is 2h;

[0025] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of rubber, in particular to a wear-resistant rubber material for baseball cores, which is made with, by weight, 70-88 parts of nitrile butadiene rubber, 28-38 parts of urea resin, 40-65 parts of modified furfural resin, 10-14 parts of silicon dioxide, 2-6.5 parts of calcium sulfate whiskers, 3-10 parts of nano carbon black, 3.2-5.7 parts of bamboo fiber, 0.5-2.5 parts of trioctyl trimellitate, 3-5 parts of liquid paraffin, 1-3.7 parts of aluminum polyphosphate, 0.3-0.8 part of dicumyl peroxide, 1-2 parts of a rare-earth stabilizer, 1-2 parts of glycerol, 1.5-3.5 parts of a curing agent, and 0.2-0.5 part of an antioxidant. The wear-resistant rubber material for baseball cores has high toughness, good corrosion resistance and good wear resistance.

Description

technical field [0001] The invention relates to the technical field of rubber, in particular to a wear-resistant rubber material for a baseball core. Background technique [0002] At present, the core material of a solid soft baseball is generally synthetic rubber, and the toughness and wear resistance of the synthetic rubber in the prior art cannot meet the needs of actual use, making the quality and quality of the baseball far from reaching the market. Requirement, therefore urgently need to develop a kind of baseball core to solve the problem in the prior art with high tenacity wear-resistant rubber material. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a wear-resistant rubber material for a baseball core. The invention has high toughness and good corrosion resistance and wear resistance. [0004] A wear-resistant rubber material for a baseball core proposed by the present inve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L61/24C08L61/00C08L97/02C08K13/04C08K3/36C08K7/08C08K3/04C08K3/32C08K3/24C08K3/16
CPCC08K2003/327C08K2201/011C08L9/02C08L2205/02C08L2205/035C08L2205/16C08L61/24C08L61/00C08L97/02C08K13/04C08K3/36C08K7/08C08K3/04C08K3/32C08K3/24C08K3/16
Inventor 周良正
Owner TIANCHANG ZHENGMU ALUMINUM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com