Preparation process for wood adhesive with high adhesion strength
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A wood adhesive and bonding strength technology, applied in the direction of adhesives, non-polymer adhesive additives, non-polymer organic compound adhesives, etc., can solve the problems of poor water resistance of adhesives and achieve bonding strength. high effect
Inactive Publication Date: 2019-03-08
邳州市铁富九龙公共服务有限公司
View PDF3 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] However, the above-mentioned adhesives have the problem of poor water resistance.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
[0019] The preparation method of the above-mentioned wood adhesive comprises the following steps: uniformly mixing vinyl acetate, starch emulsion, dibutyl phthalate, nano-silica sol, glucomannan, chitosan, and soybean protein denaturant , raise the temperature to 75°C, stir for 2.3 hours, cool to room temperature, add ammonium salt modified acrylate emulsion, raise the temperature to 110°C, react for 25min, and then cool.
Embodiment 2
[0021] Wood adhesive, comprising the following raw materials in parts by weight: 20 parts of vinyl acetate, 10 parts of starch emulsion, 10 parts of ammonium salt modified acrylate emulsion, 10 parts of dibutyl phthalate, 20 parts of nano-silica sol 10 parts of glucomannan (extracted from Haematococcus), 20 parts of polyurethane chitosan, and 10 parts of carboxylic acid.
[0022] The preparation method of the above-mentioned wood adhesive comprises the following steps: uniformly mixing vinyl acetate, starch emulsion, dibutyl phthalate, nano-silica sol, glucomannan, chitosan, and soybean protein denaturant , heat up to 70°C, stir for 2 hours, cool to room temperature, add ammonium salt modified acrylate emulsion, heat up to 100°C, react for 20min, and then cool.
Embodiment 3
[0024] Wood adhesive comprises the following raw materials in parts by weight: 90 parts of vinyl acetate, 30 parts of starch emulsion, 20 parts of ammonium salt modified acrylate emulsion, 12 parts of dibutyl phthalate, 30 parts of nano-silica sol 60 parts of glucomannan (extracted from Haematococcus), 40 parts of acrylate chitosan, and 15 parts of acid anhydride.
[0025] The preparation method of the above-mentioned wood adhesive comprises the following steps: uniformly mixing vinyl acetate, starch emulsion, dibutyl phthalate, nano-silica sol, glucomannan, chitosan, and soybean protein denaturant , heat up to 80°C, stir for 3 hours, cool to room temperature, add ammonium salt modified acrylate emulsion, heat up to 120°C, react for 30min, and then cool.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a preparation process for a wood adhesive with high adhesion strength. The preparation process comprises the following raw materials in parts by weight: 20-90 parts of vinyl acetate, 10-30 parts of a starchemulsion, 10-20 parts of an ammonium salt modified acrylateemulsion, 10-12 parts of dibutyl phthalate, 20-30 parts of nanosilicon dioxide sol, 10-60 parts of gulcomannan, 20-40 parts of chitosan and 10-15 parts of a soybean protein denaturant. The preparation method comprises the following steps: uniformly mixing the vinyl acetate, the starchemulsion, the dibutyl phthalate, the nanosilicon dioxide sol, the gulcomannan, the chitosan and the soybean protein denaturant, heating to 70-80 DEG C, stirring to carry out a reaction for 2-3 hours, cooling to the room temperature, adding the ammonium salt modified acrylate emulsion, heating to 100-120 DEG C to carry out a reaction for 20-30 minutes, and cooling. The wood adhesive disclosed by the invention has the advantages of being high in adhesion strength and good in water resistance.
Description
technical field [0001] The invention relates to a preparation process of a wood adhesive with high bonding strength. Background technique [0002] The most prominent feature of wood adhesives is that they are used in large quantities. The cost, variety, and quality of adhesives directly affect the cost, quality, and use of wood-based panels. Therefore, most wood processing enterprises in my country have their own glue-making workshops. The main types of glue produced are urea-formaldehyde resin glue, phenolic resin glue and Melamine resin glue. At the same time, with the increase in the variety of wood glued products and the continuous improvement of their quality requirements, specialized glue-making enterprises have emerged. Adhesive industry is one of the fast-growing fine chemical industries in China since the implementation of the reform and opening up policy. Adhesives are easy to use and have good economic benefits, providing an effective way for various industries ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).