Spindle shaping process special antibacterial treatment process

A processing technology and molding technology, applied in the field of special antibacterial treatment technology, can solve the problems of bacteria, residual harmful substances, affecting human health, etc.

Inactive Publication Date: 2019-03-12
浙江恒祥棉纺织造有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In daily life, the clothes and socks we wear every day are made of yarn, and if we want the clothes and socks to have different colors, we must dye the yarn, and after dyeing and processing, it is inevitable Harmful substances and bacteria will remain, which will affect human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spindle shaping process special antibacterial treatment process
  • Spindle shaping process special antibacterial treatment process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A special antibacterial treatment process for spindle forming, comprising the following steps:

[0017] 1) Put 1000L of water required for the process into the pool, and add chelating agent in an amount of 3g / L for purification, and control the water temperature to 65°C, keep the water temperature for 36min, and then automatically cool the water to normal temperature ,spare;

[0018] 2) Take out 500L of the water purified in step 1) and put it into a container, add aluminum sulfate, white vinegar and salt water, the aluminum sulfate is added in an amount of 7g / L, the concentration of the salt water is 16%, and the amount added is 20% of the volume, the amount of white vinegar is the amount required to make the pH value of the mixed solution 6.6 after adding, then the temperature is controlled at 35°C, and finally the dyed spindles, printed or dyed fabrics are put into the container, And make the dyed spindles, printed and dyed or dyed fabrics completely soaked under wa...

Embodiment 2

[0025] A special antibacterial treatment process for spindle forming, comprising the following steps:

[0026] 1) Put 1000L of water required for the process into the pool, and add chelating agent in an amount of 1g / L for purification, and control the water temperature to 55°C, keep the water temperature for 30 minutes, and then automatically cool the water to normal temperature ,spare;

[0027] 2) Take out 500L of the water purified in step 1) and put it into a container, add aluminum sulfate, white vinegar and salt water, the aluminum sulfate is added in an amount of 5g / L, the concentration of the salt water is 10%, and the amount added is purified water 10% of the volume, the amount of white vinegar is the amount required to make the pH of the mixed solution 5.8 after adding, then the temperature is controlled at 25°C, and finally the dyed spindles, printed or dyed fabrics are put into the container, And make the spindles completely soaked under water, carry out color fixa...

Embodiment 3

[0034] A special antibacterial treatment process for spindle forming, comprising the following steps:

[0035] 1) Put 1000L of water required for the process into the pool, and add chelating agent in an amount of 2g / L for purification, and control the water temperature to 60°C, keep the water temperature for 33min, and then automatically cool the water to normal temperature ,spare;

[0036] 2) Take out 500L of the water purified in step 1) and put it into a container, add aluminum sulfate, white vinegar and salt water, the aluminum sulfate is added in an amount of 6g / L, the concentration of the salt water is 13%, and the amount added is purified water 15% of the volume, the amount of white vinegar is the amount required to make the pH value of the mixed solution 6.2 after adding, then the temperature is controlled at 30°C, and finally the dyed spindles, printed or dyed fabrics are put into the container, And make the dyed spindles, printed and dyed or dyed fabrics completely ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a spindle shaping process special antibacterial treatment process. The spindle shaping process special antibacterial treatment process comprises the steps of process water purification, spindle color fixation, metal ion removal, further spindle color fixation, surface modification, primary antibacterial treatment, secondary antibacterial treatment, color fixation cleaning and tertiary antibacterial treatment; chelating agent is applied to purifying process water to ensure water quality and complex and absorb metal ions on spindles; aluminum sulfate, white vinegar and salt solution can achieve the effects of color fixation and hazardous substance removal to ensure no color fading during antibacterial treatment as well as achieve further color fixation through plasmatreatment and primary antibacterial treatment; nanometer zinc oxide and nanometer silicon dioxide synthesize to perform secondary antibacterial treatment, and ultraviolet and titanium dioxide antibacterial agent are matched to achieve tertiary antibacterial treatment. Therefore, the spindle shaping process special antibacterial treatment process can achieve antibacterial treatment and hazardous substance removal with no color fading.

Description

technical field [0001] The invention specifically relates to a special antibacterial treatment process for spindle forming processing. Background technique [0002] The loom spins many plant fibers together into threads or yarns, which can be used to weave cloth. The earliest spinning machine mechanism is very simple, began to use in the 14th century. After the 18th century, people invented better spinning machines, which made the textile industry the number one industry. All of spinning machine the most only does two pieces thing: first substantial amounts of chopped fiber is aggregated into loose cotton thread, then a little release of cotton thread, is twined into fine and closely woven cotton thread, and cotton thread is the most elongated through afterturn. Spinning is divided into cotton spinning, hemp spinning, silk spinning, and wool spinning according to natural fibers, and the process and equipment are different. Pure spinning and blending of chemical fibers mos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M10/00D06M11/46D06M10/02D06M11/44D06M11/60D06M11/79D06M13/207D06M16/00D06P1/653D06P1/673D06P5/02
CPCD06M10/001D06M10/025D06M11/44D06M11/46D06M11/60D06M11/79D06M13/207D06M16/00D06P1/6533D06P1/67341D06P5/02
Inventor 朱在敏姜生祥刘德恩张国强王博根谭学平肖建仙郑丽
Owner 浙江恒祥棉纺织造有限公司