A kind of waterproof microbead and preparation method thereof

A technology of microbeads and thin tails, which is applied in the field of waterproof microbeads and its preparation, can solve the problems of insufficient anti-seepage effect, high cost, and short timeliness, so as to improve the ability of anti-rainwater erosion, prevent the infiltration of water, and prepare The effect of simple method

Active Publication Date: 2021-04-27
柳州柳晶环保科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] There are internal spaces such as pores and crevices in natural soil, which are easy to permeate and form leakage, which is not conducive to the growth of plants
For the leakage of various water bodies, the method of plastic film bottoming is relatively common, but the method of plastic film bottoming is relatively expensive, the construction procedure is complicated and the cycle is long, the ventilation effect is not good, and the anti-seepage effect during use is not good enough. Short sex, poor application effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of waterproof microbead and preparation method thereof
  • A kind of waterproof microbead and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A waterproof microbead, comprising the following raw materials in mass fractions: 96% of tailings, 2% of paraffin, 1% of bentonite, 0.3% of calcium oxide, and 0.7% of nano-alumina powder.

[0021] The preparation method of waterproof microbead in the present embodiment, comprises the following steps:

[0022] (1) After mixing the tailings, paraffin, bentonite, calcium oxide and nano-alumina powder, add them to the stirring tank and stir at a stirring rate of 300 rpm for 20 minutes to obtain a mixture;

[0023] (2) adding the mixture into a granulator to granulate, and continuously heating and stirring during the granulation process, the heating temperature is 50°C, and the stirring rate is 100 rpm to obtain microbead particles;

[0024] (3) Discharging the microbead particles into a cooling barrel to cool evenly to room temperature and passing through an 80-mesh sieve to obtain waterproof microbeads.

Embodiment 2

[0026] A waterproof microbead, comprising the following raw materials in mass fractions: 90% of dust removal ash, 6% of paraffin, 3% of bentonite, 0.3% of calcium oxide, and 0.7% of nano-alumina powder.

[0027] The preparation method of waterproof microbead in the present embodiment, comprises the following steps:

[0028] (1) After mixing the dedusting ash, paraffin, bentonite, calcium oxide, and nano-alumina powder, add them to the stirring tank and stir at a stirring rate of 600 rpm for 30 minutes to obtain a mixture;

[0029] (2) Add the mixture to a granulator to granulate, and continuously heat and stir during the granulation process, the heating temperature is 70°C, and the stirring rate is 200 rpm to obtain microbeads;

[0030] (3) Discharging the microbead particles into a cooling barrel to cool evenly to room temperature and passing through a 100-mesh sieve to obtain waterproof microbeads.

Embodiment 3

[0032] A waterproof microbead, comprising the following raw materials in mass fractions: 63.7% of tailings, 30% of white carbon black, 3% of paraffin, 2% of bentonite, 0.5% of calcium oxide, and 0.8% of nano-alumina powder.

[0033] The preparation method of waterproof microbead in the present embodiment, comprises the following steps:

[0034] (1) After mixing the tailings, paraffin, bentonite, calcium oxide, and nano-alumina powder, add them to the stirring tank and stir at a stirring rate of 400 rpm for 22 minutes to obtain a mixture;

[0035] (2) adding the mixture into a granulator to granulate, and continuously heating and stirring during the granulation process, the heating temperature is 55° C., and the stirring rate is 120 rpm to obtain microbead particles;

[0036] (3) Discharging the microbead particles into a cooling barrel to cool evenly to room temperature and passing through a 100-mesh sieve to obtain waterproof microbeads.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of waterproof materials, in particular to a waterproof microbead and a preparation method thereof. The waterproof microsphere of the present invention comprises the following raw materials in mass fractions: 90-96% of fine tailings, 2-6% of paraffin, 1-3% of bentonite, 0.3-0.6% of calcium oxide, and 0.7-0.9% of nano-alumina powder. It is prepared by mixing and stirring, heating granulation, cooling and sieving. Through the synergistic effect of various raw materials, the prepared waterproof microbeads have high strength, waterproof and anti-cracking functions, can reduce soil water seepage, improve soil air permeability, and can also effectively improve soil and facilitate plant growth.

Description

technical field [0001] The invention relates to the field of waterproof materials, in particular to a waterproof microbead and a preparation method thereof. Background technique [0002] There are internal spaces such as pores and crevices in natural soil, which are easy to permeate and form leakage, which is not conducive to the growth of plants. For the leakage of various water bodies, the method of plastic film bottoming is relatively common, but the method of plastic film bottoming is relatively expensive, the construction procedure is complicated and the cycle is long, the ventilation effect is not good, and the anti-seepage effect during use is not good enough. Short, poor application effect. Contents of the invention [0003] In view of the above technical problems, the present invention provides a waterproof microbead and a preparation method thereof. [0004] The present invention adopts following technical scheme: [0005] A waterproof microbead, comprising th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/26
CPCC04B26/26C04B2111/27C04B22/064C04B14/303C04B14/104C04B18/12C04B18/062
Inventor 任文强
Owner 柳州柳晶环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com