Method for improving curing forming quality of L-shaped composite material laminated plate

A composite material layer, curing and forming technology, applied in the field of composite materials, can solve the problems of L-shaped composite material laminates, such as wrinkles, and achieve the effects of avoiding uneven pressure, suppressing micro-buckling, and ensuring manufacturing tolerances.

Active Publication Date: 2019-04-16
WUHAN UNIV OF TECH
View PDF12 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, there is a need for a method to solve the defect that the curvature of the L-shaped composite laminate is prone to wrinkling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving curing forming quality of L-shaped composite material laminated plate
  • Method for improving curing forming quality of L-shaped composite material laminated plate
  • Method for improving curing forming quality of L-shaped composite material laminated plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1: Using elastic buffer soft mold to improve the surface quality of L-shaped sample in autoclave molding

[0027] This embodiment provides a method for improving the surface quality of a composite component with curvature, which specifically includes the following steps:

[0028] (1) According to the external dimensions of the L-shaped sample, the radius of the outer chamfer is 10mm, the length of the right-angled side is 100mm, and the width is 200mm. The inner radius of the elastic buffer soft mold is determined to be 10mm, the thickness is 10mm, the length of the right-angled side is 110mm, and the width is 10mm. 220mm, see the specific size diagram Figure 4 .

[0029] (2) Referring to the size of the elastic buffer soft film designed in (1), make a mold cavity for pouring. Then take 500g of silica gel and curing agent to blend according to the mass ratio of 100:15, and pour it into the cavity after defoaming. Wait 12 hours for the silicone to fully cure....

Embodiment 2

[0033] Example 2: Using elastic buffer soft film to improve the surface quality of L-shaped sample in autoclave forming

[0034] This embodiment provides a method for improving the surface quality of a composite component with curvature, which specifically includes the following steps:

[0035] (1) According to the design dimensions of the L-shaped sample, the radius of the outer chamfer is 14mm, the length of the right-angled side is 120mm, and the width is 220mm. , the thickness is 8mm and the specific size diagram is shown in Figure 7 .

[0036] (2) According to the external dimensions determined in step (1), the natural rubber elastic cushioning soft mold is customized, and its Shore hardness is required to be between 50±20HA, and the elongation at break is greater than 100%.

[0037] (3) After the elastic cushioning soft mold is finished, use a hollow needle to drill uniform vent holes with a diameter of 1mm and an interval of 8mm on the silicone pad, such as Figure ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for improving a curing forming quality of an L-shaped composite material laminated plate. The method comprises the following steps that (1), an elastomer material is selected, and an elastomer buffer flexible film is manufactured according to the contour dimension of a component; (2) vent holes are uniformly formed in the elastomer buffer flexible film in the thickness direction after the elastomer buffer flexible film is formed; and (3) the L-shaped composite material component is prepared, a prepreg laminated layer is paved on a rigid die according to the paving ratio, the outer surface of the laminated layer is covered with the prepared elastomer buffer flexible film, and a vacuum bag pressing method or a drying oven is adopted for curing and forming according to the set temperature and pressure curves. According to the method, the pressure borne by a part with the curvature of the composite material component in the forming process can be balanced through the introduction of the elastomer buffer flexible film, fibers can be prevented from generating micro-bending in the forming process, fiber wrinkles are prevented from being generated on the surface of the composite material laminated plate, and therefore the surface quality of the composite material laminated plate is improved, and the stability of the outer side dimension of the compositematerial component with the curvature is ensured.

Description

technical field [0001] The invention relates to the technical field of composite materials, in particular to a method for improving the curing molding quality of an L-shaped composite material laminate. Background technique [0002] Due to their high specific strength and high specific modulus, composite materials have been widely used in the aerospace field, and are regarded as key materials for the manufacture of new rail transit and new energy vehicles. With the development of composite component manufacturing towards integration, the structural shape becomes more and more complex, and a large number of curvature-containing parts appear. Taking composite wings as an example, L-shaped composite components are widely found in spar, rib and long truss structures. At present, a large number of composite material components are prepared by the prepreg process. The prepreg laminate is laid on the outer surface of the mold, sealed with a vacuum bag, and cured in an autoclave or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/34B29C70/54
CPCB29C70/342B29C70/54
Inventor 李书欣彭昊阳胡海晓于晓东曹子荷
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com