An environmentally friendly and emergency technology, applied in the direction of first aid kits, etc., can solve the problems of easy scrapping, large amount of garbage, and treatment of people who cannot need ambulance, so as to reduce personnel loss, reduce work intensity, and facilitate treatment.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0062] An environmentally friendly device for emergency rescue, such as Figure 1-9 As shown, it includes a square casing 1, four grooves 3 are symmetrically opened on the front side of the square casing 1, and a cover plate 2 is hinged on the rear side of the square casing 1, and the four grooves The inside of the groove 3 is fixedly equipped with a round rod 5, and a cloth belt 4 is fixedly sewn between two adjacent round rods 5 in the same vertical direction, and the left and right sides of the square casing 1 are fixed symmetrically. Two fixed sleeves 10 are installed, and an inverted U-shaped bracket 11 is movably installed between the two fixed sleeves 10. Two installation grooves 13 are symmetrically opened at the junction of the bottom of the square housing 1 and the rear side, and the The bottom of the square housing 1 is symmetrically fixed with two rubber feet 6 close to its front side, and guide wheels 14 are installed in the inside of the two installation grooves ...
Embodiment 2
[0084] The difference from Example 1 is that a protective layer is also provided on the surface of the square housing 1, and the protective layer is prepared by the following method:
[0085] Take the following raw materials and weigh them by weight: 22 parts of epoxy resin, 10 parts of calcium carbonate powder, 10 parts of zinc oxide powder, 20 parts of porcelain powder, 8 parts of mica powder, 15 parts of polyurethane, 3 parts of glycerin, 2 parts of alcohol ester twelve 2 parts of high carbon alcohol fatty acid ester complex, 2 parts of triethanolamine, 1 part of alkyl modified organosiloxane and 30 parts of ethanol;
[0086] S1. Add the weighed glycerin, alcohol ester dodecane, triethanolamine, high-carbon alcohol fatty acid ester complex, alkyl modified organosiloxane and ethanol into the mixer and stir for 20min at a stirring speed of 600r / min. Prepare a mixed solution;
[0087] S2, adding epoxy resin, calcium carbonate powder, zinc oxide powder, porcelain powder, mica ...
Embodiment 3
[0093] The difference with embodiment 2 is the preparation of protective layer, and its specific preparation method is as follows:
[0094] Take the following raw materials and weigh them by weight: 24 parts of epoxy resin, 12 parts of calcium carbonate powder, 11 parts of zinc oxide powder, 23 parts of porcelain powder, 9 parts of mica powder, 17 parts of polyurethane, 4 parts of glycerin, 3 parts of alcohol ester twelve 3 parts of high carbon alcohol fatty acid ester complex, 3 parts of triethanolamine, 2 parts of alkyl modified organosiloxane and 40 parts of ethanol;
[0095] S1. Add the weighed glycerin, alcohol ester dodecane, triethanolamine, high-carbon alcohol fatty acid ester complex, alkyl modified organosiloxane and ethanol into the mixer and stir for 25min at a stirring speed of 650r / min. Prepare a mixed solution;
[0096] S2, adding epoxy resin, calcium carbonate powder, zinc oxide powder, porcelain powder, mica powder and polyurethane into the pulverizer and pul...