Moisture-curing polyurethane hot melt adhesive with excellent oil resistance and preparation method of moisture-curing polyurethane hot melt adhesive

A polyurethane hot-melt adhesive and moisture-curing technology, applied in the field of structural adhesives, can solve the problems of reducing the oil resistance, chemical corrosion resistance and aging resistance of the polyurethane hot melt adhesive coating, so as to improve the compatibility, The effect of improving oil resistance and improving leveling performance

Inactive Publication Date: 2019-04-26
SHUNDE POLYTECHNIC
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These non-reactive system tackifying resins cannot participate in curing to form a cross-linked network, which easily reduces the oil resistance, chemical corrosion resistance, and aging resistance of polyurethane hot melt adhesive coatings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisture-curing polyurethane hot melt adhesive with excellent oil resistance and preparation method of moisture-curing polyurethane hot melt adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] It is a moisture-curing polyurethane hot-melt adhesive with excellent oil resistance, which is prepared by the following steps:

[0028] Step 1: Synthesis of polyacrylic acid fluorocopolymer

[0029] 20 parts of dodecafluoroheptyl methacrylate DFMA, 20 parts of methyl methacrylate MMA, 20 parts of octadecyl methacrylate SMA and 4 parts of hydroxyethyl methacrylate HEMA were dissolved in 60 parts of In toluene, controlled at 85 ° C, under nitrogen protection, 1.9 parts of thermal initiator 2-ethylhexanoate tert-amyl peroxide was added, and the polymerization reaction was carried out for 30 hours. After the toluene was removed by rotary evaporation, a polyacrylic acid fluorine-containing copolymer was obtained. , the number average molecular weight of the polyacrylic acid fluorine-containing copolymer is 14000, and its chemical structure is: poly(dodecafluoroheptyl methacrylate-random-methyl methacrylate-random-octadecyl methacrylate-no Gauge-hydroxyethyl methacrylate) i...

Embodiment 2

[0033] It is a moisture-curing polyurethane hot-melt adhesive with excellent oil resistance, which is prepared by the following steps:

[0034] Step 1: Synthesis of polyacrylic acid fluorocopolymer

[0035]25 parts of dodecafluoroheptyl methacrylate DFMA, 30 parts of methyl methacrylate MMA, 10 parts of octadecyl methacrylate SMA and 6 parts of hydroxyethyl methacrylate HEMA were dissolved in 70 parts of In toluene, controlled at 90 ° C, under nitrogen protection, 1.7 parts of thermal initiator 2-ethylhexanoate tert-amyl peroxide was added, and the polymerization reaction was carried out for 20 hours. After the toluene was removed by rotary evaporation, a polyacrylic acid fluorine-containing copolymer was obtained. , the number average molecular weight of the polyacrylic acid fluorine-containing copolymer is 22000, and its chemical structure is: poly(dodecafluoroheptyl methacrylate-random-methyl methacrylate-random-octadecyl methacrylate-no Gauge-hydroxyethyl methacrylate) is...

Embodiment 3

[0039] It is a moisture-curing polyurethane hot-melt adhesive with excellent oil resistance, which is prepared by the following steps:

[0040] Step 1: Synthesis of polyacrylic acid fluorocopolymer

[0041] 35 parts of dodecafluoroheptyl methacrylate DFMA, 30 parts of methyl methacrylate MMA, 20 parts of octadecyl methacrylate SMA and 8 parts of hydroxyethyl methacrylate HEMA were dissolved in 90 parts of In toluene, controlled at 95 ℃, under nitrogen protection, add 0.7 parts of thermal initiator 2-ethylhexanoate tert-amyl peroxide, polymerize for 10 hours, remove toluene by rotary evaporation, and obtain polyacrylic acid fluorine-containing copolymer , the number average molecular weight of the polyacrylic acid fluorine-containing copolymer is 32000, and its chemical structure is: poly(dodecafluoroheptyl methacrylate-random-methyl methacrylate-random-octadecyl methacrylate-no Gauge-hydroxyethyl methacrylate) is P (DFMA-r-MMA-r-SMA-r-HEMA).

[0042] Step 2: Synthesize moist...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a moisture-curing polyurethane hot melt adhesive with excellent oil resistance and a preparation method of the moisture-curing polyurethane hot melt adhesive. The moisture-curing polyurethane hot melt adhesive is characterized by being prepared from 1-35 parts of polyether diols, 1-40 parts of liquid polyester diols, 1-60 parts of crystalline polyester diols, 1-45 parts ofa polyacrylic acid fluorine-containing copolymer, 1-50 parts of isocyanate, 0.1-2 parts of a catalyst, 0.1-3 parts of an antioxidant and 0.1-4 parts of a silane coupling agent. Poly(dodecafluoroheptylmethacrylate-random-methyl methacrylate-random-octadecyl methacrylate-random-hydroxyethyl methylacrylate) is synthesized firstly and added to a polyurethane prepolymer reaction, a hydroxy-containingacrylic acid functional monomer enables the polyacrylic acid fluorine-containing copolymer to partially participate in the polyurethane prepolymer synthesis reaction, a fluorinated acrylate copolymerchain segment is introduced, by means of an efficient synergistic effect of the formula, the hot melt adhesive shows better compatibility, composition and content of other raw materials are further adjusted, and therefore, oil resistance of the polyurethane hot melt adhesive is improved.

Description

technical field [0001] The invention belongs to the technical field of structural adhesives, and in particular relates to a moisture-curing polyurethane hot-melt adhesive with excellent oil resistance and a preparation method thereof, which are mainly used in the electronics and electrical appliances industry, the automobile industry, the textile and shoemaking industry, the food packaging industry, Structural bonding in wood processing and furniture industry. Background technique [0002] Polyurethane hot-melt adhesive is a new generation of structural adhesive that can provide excellent bonding properties. Polyurethane hot-melt adhesive is easy to use, environmentally friendly, and its performance is comparable to solvent-based hot-melt adhesives. In the past ten years, polyurethane hot melt adhesives have been rapidly developed and widely used in high-end fields such as the electronics and electrical appliances industry and the automotive industry. Polyurethane hot melt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J175/06C09J175/08C09J11/06C08F283/12C08F220/22C08F220/20C08F220/18C08G18/42C08G18/48C08G18/62C08G18/76C08G18/79C08G18/30
CPCC08F283/124C08G18/307C08G18/4063C08G18/4238C08G18/4825C08G18/4854C08G18/6295C08G18/7671C08G18/794C09J11/06C09J175/06C09J175/08C08K5/526C08K5/1345C08F220/1818
Inventor 唐秋实刘锋陈燕舞路风辉霍应鹏彭琦林雯雯洪银娜马倩琳
Owner SHUNDE POLYTECHNIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com