A production process of base paper for engineering duplication
A production process and engineering technology, which is applied in the field of engineering copy base paper production process, can solve the problems of ecological environment and human injury, cannot meet the needs of large-scale use, and produce ammonia nitrogen gas, etc., and achieve the effect of meeting market demand and good printing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0048] A kind of production process of base paper for engineering duplication, the specific steps are as follows:
[0049] (1) Preparation of pulp raw materials: the ratio of various pulps is: 30% of coniferous chemical pulp, 67% of broadleaf chemical pulp, and 3% of chemical mechanical pulp.
[0050] (2) Paper making process: beat the above pulp raw materials in proportion, wherein the coniferous chemical pulp is beaten to 46 ° SR, the broadleaf chemical pulp is beaten to 25 ° SR, and the chemical mechanical pulp is beaten to 48 ° SR, and then the above-mentioned beating The final slurry is transported to the mixed pulp tank and mixed evenly in proportion; add 0.27kg / ton of pulp anionic garbage treatment agent and 5.6kg / ton of pulp whitening agent into the mixed pulp tank, and mix uniformly; fully mix the above The uniform slurry is pumped into the forebay, and sequentially add 0.13kg / ton of pigment blue, 0.1kg / ton of pigment violet, 0.75kg / ton of ASA sizing agent, 150kg / ton ...
Embodiment 2
[0059] A kind of production process of base paper for engineering duplication, the specific steps are as follows:
[0060] (1) Preparation of slurry raw materials: various slurry ratios are: 30% of coniferous chemical pulp, 65% of broadleaf chemical pulp, and 5% of chemical mechanical pulp.
[0061] (2) Papermaking process: beat the above-mentioned pulp raw materials in proportion, wherein the coniferous chemical pulp is beaten to 50°SR, the broadleaf chemical pulp is beaten to 21°SR, and the chemical mechanical pulp is beaten to 52°SR, and then the above-mentioned beating The final slurry is transported to the mixed pulp tank and mixed uniformly in proportion; add 0.3kg / ton of pulp anionic garbage treatment agent and 6.0kg / ton of pulp whitening agent into the mixed pulp tank, and mix uniformly; fully mix the above The uniform slurry is pumped into the forebay, and 0.135kg / ton of pigment blue, 0.108kg / ton of pigment purple, 0.79kg / ton of ASA sizing agent, 157kg / ton of filler a...
PUM
Property | Measurement | Unit |
---|---|---|
whiteness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com