Preparation and application of a casein-chitosan composite fiber and its fabric

A composite fiber and composite fabric technology, applied in the direction of fabric, application, fiber chemical characteristics, etc., can solve the problems of limited wide application, fiber breakage, etc., and achieve the effect of high degree of bonding, enhanced tensile properties, and improved tensile properties.

Active Publication Date: 2021-04-06
SHANDONG ANQIER DECORATION ARTICLE CO LTD
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, in the current application process of casein fiber, if the thickness of the prepared fabric is relatively thin, it is easy to cause fiber breakage in the process of stretching and breaking, which limits its wide application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation and application of a casein-chitosan composite fiber and its fabric
  • Preparation and application of a casein-chitosan composite fiber and its fabric
  • Preparation and application of a casein-chitosan composite fiber and its fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A preparation method of casein-chitosan composite fiber, comprising the steps of: dissolving 4kg of casein in 80kg of water, adding 0.1kg of aminopropyltriethoxysilane and stirring for 30min, the stirring temperature is 50°C, adjusted by acetic acid The pH value of the system is 5.6-6.2, continue to stir for 18min, then add 1kg chitosan, 10kg water and grind for 2min, the grinding temperature is 80°C, the grinding pressure is 0.012Mpa, then add water until the water content is 80wt%, spinning to obtain a diameter of 0.01-0.06mm casein-chitosan composite fiber.

[0037] The specific steps of spinning are as follows: After spinning, it is sent to a coagulation bath for coagulation. The coagulation bath is a glutaraldehyde solution with a concentration of 0.1mol / L. The temperature of the coagulation bath is 40°C. After pre-drawing and drawing, densification The treatment was performed for 2 minutes, the densification treatment temperature was 134°C, followed by steam heat ...

Embodiment 2

[0040] A preparation method of casein-chitosan composite fiber, comprising the steps of: dissolving 10kg of casein in 30kg of water, adding 0.1kg of phenyltriethoxysilane and 0.08kg of octamethyltrisiloxane and stirring for 12min, Stirring temperature is 60°C, use acetic acid to adjust the pH value of the system to 5.6-6.2, continue to stir for 10 minutes, then add 3kg chitosan, 2kg water and grind for 10 minutes, the grinding temperature is 70°C, the grinding pressure is 0.018Mpa, and then add water to the water content The content is 70 wt%, and the casein-chitosan composite fiber with a diameter of 0.01-0.06 mm is obtained by spinning.

[0041] The specific steps of spinning are as follows: After spinning, it is sent to a coagulation bath for coagulation. The coagulation bath is a glutaraldehyde solution with a concentration of 0.18mol / L. The temperature of the coagulation bath is 20°C. After pre-drawing and drawing, densification The treatment was performed for 4 minutes, ...

Embodiment 3

[0044] A method for preparing casein-chitosan composite fiber, comprising the following steps: dissolving 5kg of casein in 75kg of water, adding 0.11kg of dimethyldichlorosilane and stirring for 28min at a stirring temperature of 51°C, using acetic acid to adjust the pH of the system The value is 5.6-6.2, continue to stir for 17 minutes, then add 1.2kg chitosan, 9kg water and grind for 3 minutes, the grinding temperature is 79 ° C, the grinding pressure is 0.013Mpa, then add water until the water content is 79wt%, spinning to obtain a diameter of 0.01 - 0.06mm casein-chitosan composite fiber.

[0045] The specific steps of spinning are as follows: After spinning, it is sent to a coagulation bath for coagulation. The coagulation bath is a glutaraldehyde solution with a concentration of 0.12mol / L. The temperature of the coagulation bath is 38°C. After pre-drawing and drawing, densification The treatment is 2.2 minutes, the densification treatment temperature is 132°C, followed b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a casein-chitosan composite fiber. The invention discloses a preparation method of the above-mentioned casein-chitosan composite fiber, comprising the following steps: dissolving casein in water, adding siloxane to stir, adjusting the pH value of the system to 5.6-6.2, continuing to stir, and then adding chitosan Sugar and water are ground, then water is added, and the casein-chitosan composite fiber is obtained by spinning. The invention discloses a casein-chitosan composite fabric. The invention discloses a preparation method of the above-mentioned casein-chitosan composite fabric. The above-mentioned casein-chitosan composite fiber is spun to obtain yarn, and then spun into a plain weave fabric. The invention discloses the application of the casein-chitosan composite fabric as an underwear fabric or a wound dressing.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a casein-chitosan composite fiber and a preparation method thereof, a casein-chitosan composite fabric and its preparation and application. Background technique [0002] The skin is the largest organ of the human body, composed of the epidermis, dermis and subcutaneous tissue. It is a natural barrier between the human body and the outside world. It plays the roles of protection, sensation, temperature regulation, secretion, excretion, absorption and immunity in the human body. The loss of water, electrolytes and acid-base balance will cause imbalance of water, electrolyte and acid-base balance, which will affect the normal absorption and metabolic balance of the human body. The skin is the first layer of barrier for the body to defend against external invasion, and it is also the largest tissue in the body. Foreign substances and microbial attack. There are many reasons for ski...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/02D01F8/18D01F1/10A41B17/00D03D15/292A61L15/32A61L15/28A61L15/42A61L15/46
Inventor 严春兰
Owner SHANDONG ANQIER DECORATION ARTICLE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap