ABS alloy material easy to clean and preparation method thereof

An alloy material, easy-to-clean technology, applied in the field of easy-to-clean ABS alloy materials and its preparation, to prevent long-term accumulation, not easy to accumulate dust, and improve performance

Inactive Publication Date: 2019-05-24
ORINKO NEW MATERIAL CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a kind of easy-to-clean ABS alloy material and preparation method thereof, to solve the problem of facilitating the cleaning of ABS alloy material proposed in the above-mentioned background technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ABS alloy material easy to clean and preparation method thereof
  • ABS alloy material easy to clean and preparation method thereof
  • ABS alloy material easy to clean and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An easy-to-clean ABS alloy material and a preparation method thereof, characterized in that: the alloy material is prepared from the following components in parts by weight:

[0029]

[0030] A kind of preparation method of easy-to-clean ABS alloy material is as follows:

[0031] (1) Mix polycarbonate with strong base and weak salt to obtain a mixture, and then place the mixture in a reactor under low pressure (30Pa) (the outer wall of the reactor is a stainless steel circular container, and two parallel diameters are installed in the center of the reaction chamber. Disc electrodes with a distance of 25 cm and a distance of 10 cm, the upper plate and the container wall are grounded, and the lower plate is connected to a radio frequency power supply) and treated with CF4 radio frequency plasma for 20 minutes;

[0032] (2) Put the polycarbonate treated in step (1) and the mixture of strong base and weak acid salt into the screw extruder, and at the same time, put ABS r...

Embodiment 2

[0035]

[0036]

[0037] A kind of preparation method of easy-to-clean ABS alloy material is as follows:

[0038] (1) Mix polycarbonate with strong base and weak salt to obtain a mixture, and then place the mixture in a reactor under low pressure (30Pa) (the outer wall of the reactor is a stainless steel circular container, and two parallel diameters are installed in the center of the reaction chamber. Disc electrodes with a distance of 25 cm and a distance of 10 cm, the upper plate and the container wall are grounded, and the lower plate is connected to a radio frequency power supply) and treated with CF4 radio frequency plasma for 20 minutes;

[0039] (2) Put the polycarbonate treated in step (1) and the mixture of strong base and weak acid salt into the screw extruder, and at the same time, put ABS resin, filler, surface modifier, phase modifier into the screw extruder Compatible agent, antioxidant and lubricant, through melt extrusion and pelletizing, to obtain prima...

Embodiment 3

[0042]

[0043]

[0044] A kind of preparation method of easy-to-clean ABS alloy material is as follows:

[0045] (1) Mix polycarbonate with strong base and weak salt to obtain a mixture, and then place the mixture in a reactor under low pressure (30Pa) (the outer wall of the reactor is a stainless steel circular container, and two parallel diameters are installed in the center of the reaction chamber. Disc electrodes with a distance of 25 cm and a distance of 10 cm, the upper plate and the container wall are grounded, and the lower plate is connected to a radio frequency power supply) and treated with CF4 radio frequency plasma for 20 minutes;

[0046] (2) Put the polycarbonate treated in step (1) and the mixture of strong base and weak acid salt into the screw extruder, and at the same time, put ABS resin, filler, surface modifier, phase modifier into the screw extruder Compatible agent, antioxidant and lubricant, through melt extrusion and pelletizing, to obtain prima...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an ABS alloy material easy to clean and a preparation method thereof. The ABS alloy material is characterized by being prepared from, by weight, 50-90 parts of ABS resin, 10-60parts of polycarbonate, 1-10 parts of filler, 2-10 parts of a surface modifier, 1-5 parts of a compatilizer, 0.3-1 part of an antioxidant, 0.5-2.5 parts of a lubricant, 0.2-1 part of an organic solvent and 0.2-1 part of a strong base weak acid salt. The prepared ABS alloy material is not likely to accumulate dust and is easy to wipe clean.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an easy-to-clean ABS alloy material and a preparation method thereof. Background technique [0002] At present, the development of the home appliance industry around the world is increasingly based on human nature. Customer experience and safety have gradually become the core focus of products. In terms of life, the cleaning and removal of dust and oil has become the number one headache for people; Organs are very harmful, especially the particles that are accompanied by metal ions, benzene, formaldehyde and other pollutants in the decoration. Through the nasal cavity, upper respiratory tract and other organs, they will damage the mucous membrane tissue of the human body, causing headaches, dizziness, vision loss, difficulty breathing, nerve membranes, etc. A series of diseases, such as handicap, can be life-threatening in severe cases. [0003] At the same time, in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L69/00C08L35/06C08L33/20C08L91/06C08K13/04C08K13/02C08K7/26C08K3/36C08K5/13C08K5/134C08K5/20C08K5/12C08J3/28
Inventor 杨亚娣文听雷任东方吴摞李荣群
Owner ORINKO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap