Method for processing antiqued ceramics

A processing method and ceramic technology, applied in the field of ceramic processing, can solve problems such as failure to achieve service performance, mechanical quality damage, etc., and achieve the effects of good service performance, comprehensive quality improvement, and good antique effect.

Inactive Publication Date: 2019-05-31
张立
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the above-mentioned processes only optimize and improve the glaze, so that the phase of the ceramic is changed. However, in actual use, it is found that the mechanical quality of the ceramic is usually damaged, and the high performance cannot be achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A processing method for antique ceramics, comprising the steps of:

[0026] 1) Embryo body preparation:

[0027] a. First weigh the following raw materials according to the corresponding parts by weight: 30 parts of corundum, 20 parts of potassium feldspar, 12 parts of kaolin, 5 parts of mullite, 1 part of zinc oxide, 1 part of zirconia, 3 parts of Shuangfei powder, 4 parts of yellow clay;

[0028] b. Put the above-mentioned raw materials weighed in operation a into the ball mill together, then add water to carry out wet ball milling, then take them out and put them into the mud refining machine for mud refining treatment, and finally process and shape the refined mud material The embryonic body is ready for use;

[0029] 2) Glaze preparation:

[0030] a. First weigh the following materials in corresponding parts by weight: 30 parts of potassium feldspar, 15 parts of quartz, 4 parts of talcum powder, 3 parts of sericite powder, 2 parts of coal gangue, 0.5 part of car...

Embodiment 2

[0042] A processing method for antique ceramics, comprising the steps of:

[0043] 1) Embryo body preparation:

[0044] a. First weigh the following raw materials in corresponding parts by weight: 33 parts of corundum, 22 parts of potassium feldspar, 14 parts of kaolin, 8 parts of mullite, 2 parts of zinc oxide, 1.5 parts of zirconia, 5 parts of Shuangfei powder, 6 parts of yellow clay;

[0045] b. Put the above-mentioned raw materials weighed in operation a into the ball mill together, then add water to carry out wet ball milling, then take them out and put them into the mud refining machine for mud refining treatment, and finally process and shape the refined mud material The embryonic body is ready for use;

[0046] 2) Glaze preparation:

[0047] a. First weigh the following materials in corresponding parts by weight: 33 parts of potassium feldspar, 18 parts of quartz, 6 parts of talcum powder, 5 parts of sericite powder, 4 parts of coal gangue, 0.8 part of carbon nanotu...

Embodiment 3

[0059] A processing method for antique ceramics, comprising the steps of:

[0060] 1) Embryo body preparation:

[0061] a. First weigh the following raw materials according to the corresponding parts by weight: 35 parts of corundum, 25 parts of potassium feldspar, 15 parts of kaolin, 10 parts of mullite, 3 parts of zinc oxide, 2 parts of zirconia, 6 parts of Shuangfei powder, 8 parts of yellow clay;

[0062] b. Put the above-mentioned raw materials weighed in operation a into the ball mill together, then add water to carry out wet ball milling, then take them out and put them into the mud refining machine for mud refining treatment, and finally process and shape the refined mud material The embryonic body is ready for use;

[0063] 2) Glaze preparation:

[0064] a. First weigh the following materials in corresponding parts by weight: 35 parts of potassium feldspar, 20 parts of quartz, 7 parts of talcum powder, 6 parts of sericite powder, 5 parts of coal gangue, 1 part of ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
aspect ratioaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for processing antiqued ceramics. The method comprises the following steps of 1) preparation of a green body; 2) preparation of a glaze; 3) processing of a finished product. The invention provides the method for processing the ceramics, an overall processing technology is simple, the method is suitable for being manufactured by large and medium-sized enterprises, the obtained ceramics have a good antiqued effect, the use performance such as strength, impact resistance and the like is good, comprehensive qualities are effectively improved, and the ceramics havemarket competitiveness and production economic benefits.

Description

technical field [0001] The invention belongs to the technical field of ceramic processing, and in particular relates to a processing method of antique ceramics. Background technique [0002] Ceramics is a common material in modern people's life. It is not only widely used in tableware containers, but also widely used in industrial building materials. With the continuous improvement of people's pursuit of products, the demand for antique ceramics is increasing, and the appearance and hue of ceramics are improved to increase the aesthetic feeling. For example, the application number is: 2016107957143.1 discloses an antique copper craft ceramics and its manufacturing process. Through the special preparation of glaze raw materials, the ceramic material made has the appearance of antique copper; the application number is: 201110409839.7 discloses a The invention discloses a bright red glaze for ceramics and a preparation method thereof. By matching the ingredients in the glaze, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/10C04B35/622C03C8/00C04B41/89C04B41/80
Inventor 张立
Owner 张立
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com