Preparation method of semi-aromatic polyamide
A semi-aromatic and polyamide technology, applied in the field of semi-aromatic polyamide preparation, can solve the problems that the low-temperature solution polycondensation method is not suitable for industrialized large-scale production, high requirements for reaction equipment, and inability to operate continuously, etc., achieving low cost , Low production cost, easy to recycle
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0046] Example 1
[0047] The preparation of semi-aromatic polyamide includes the following steps:
[0048] 1mol (i.e., 166.13g) terephthalic acid, 1.01mol (i.e., 174.05g) decanediamine, 0.01mol (i.e. 1.22g) benzoic acid, 0.34g sodium hypophosphite, 1.00g N,N'-bis-( 3-(3,5-Di-tert-butyl-4-hydroxyphenyl)propionyl)hexamethylenediamine and 510g of deionized water were added to the high temperature and high pressure polymerization reactor, the air in the reactor was replaced with nitrogen 10 times, the stirring was turned on, and the speed The temperature is 100rpm, the temperature is raised to 80°C in 0.5h, and the salt-forming reaction is performed at a constant temperature. The salt-forming reaction time is 1h; after the salt-forming reaction is completed, the temperature is raised to 220°C in 2h, during which the pressure is controlled by exhausting the gas in the kettle No more than 2.8MPa, the pre-polymerization reaction is performed at a constant temperature, and the pre-polyme...
Example Embodiment
[0050] Example 2
[0051] For the preparation of semi-aromatic polyamide, the method steps are the same as in Example 1, except that the speed of the stirrer is changed to 120 rpm. The product performance test results are shown in Table 1.
Example Embodiment
[0052] Example 3
[0053] For the preparation of semi-aromatic polyamide, the method steps are the same as those in Example 1, except that the pre-polymerization temperature is changed to 210°C. The product performance test results are shown in Table 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap