Printable plastic film and preparation method thereof

A technology for plastic films and raw materials, applied in the field of printable plastic films and their preparation, can solve the problems of high preparation cost of printable films, difficult preparation of film materials, and high preparation costs, and achieves enhanced printing effect, good adhesion, and improved The effect of the degree of binding

Inactive Publication Date: 2019-06-07
ZHEJIANG CHENGDE PACKAGING
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the thin film material provided by the invention patent is difficult to prepare, and the preparation cost is high, so it is not suitable for promotion
[0005] In order to solve the problem of high preparation cost of existing printable films, a printable plastic film with simple preparation and low preparation cost is now provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Printable plastic film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A printable plastic film

[0027] The raw materials of the printable plastic film include by weight percentage: 90% resin material, 7% conductive material and 3% oily material; the raw materials for preparing the resin material include: polyethylene 75%, C5 petroleum resin 25% ; The raw materials for preparing the conductive material include: 15% of carbon black, 20% of graphite, 20% of ferric oxide, 20% of carbon nanotubes and 25% of metal powder.

[0028] Prepared by:

[0029] Step 1, put the resin material into the mixer according to the above weight percentage, heat up to 110°C and stir and mix for 20 minutes;

[0030] Step II, continue to add carbon black, graphite, ferric oxide, carbon nanotubes and metal powder into the mixer according to the above weight percentage, stir and mix for 8 minutes, add the oily material in the above weight percentage, stir and mix evenly;

[0031] In step III, the mixture obtained in step II is transported to the extruder, cast and...

Embodiment 2

[0033] A printable plastic film

[0034] The raw materials of the printable plastic film include by weight percentage: 85% resin material, 10% conductive material and 5% oily material; the raw materials for preparing the resin material include: polyethylene 70%, C5 petroleum resin 30% ; The raw materials for preparing the conductive material include: 10% carbon black, 25% graphite, 15% ferric oxide, 25% carbon nanotube and 25% metal powder.

[0035] Prepared by:

[0036] Step I, put the resin material into the mixer according to the above weight percentage, heat up to 95°C and stir and mix for 25 minutes;

[0037] Step II, continue to add carbon black, graphite, ferric oxide, carbon nanotubes and metal powder into the mixer according to the above weight percentage, stir and mix for 10 minutes, add the oily material in the above weight percentage, stir and mix evenly;

[0038] In step III, the mixture obtained in step II is transported to the extruder, cast and extruded throu...

Embodiment 3

[0040] A printable plastic film

[0041] The raw materials of the printable plastic film include by weight percentage: 95% resin material, 3% conductive material and 2% oily material; the raw materials for preparing the resin material include: polyethylene 80%, C5 petroleum resin 20% ; The raw materials for preparing the conductive material include: 20% of carbon black, 15% of graphite, 25% of ferric oxide, 20% of carbon nanotubes and 20% of metal powder.

[0042] Prepared by:

[0043] Step 1, put the resin material into the mixer according to the above weight percentage, heat up to 120°C and stir and mix for 15 minutes;

[0044] Step II, continue to add carbon black, graphite, ferric oxide, carbon nanotubes and metal powder into the mixer according to the above weight percentage, stir and mix for 5 minutes, add the oily material in the above weight percentage, stir and mix evenly;

[0045] In step III, the mixture obtained in step II is transported to the extruder, cast and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a printable plastic film and a preparation method thereof. Raw materials of the printable plastic film comprise 85-95 wt% of a resin material, 3-10 wt% of a conductive materialand 2-5 wt% of an oily material; raw materials for preparing the resin material include 70-80 wt% of polyethylene or polypropylene and 20-30 wt% of C5 petroleum resin; and raw materials for preparingthe conductive material include 10-20 wt% of carbon black, 15-25 wt% of graphite, 15-25 wt% of ferriferrous oxide, 15-25 wt% of carbon nanotubes and 20-30 wt% of metal powder. The printable plastic film prepared in the invention has the advantages of good printability, good stability and low production cost, and the preparation method has the advantages of simplicity, easiness in process operation, and suitableness for large-scale promotion.

Description

technical field [0001] The invention relates to the field of film production and processing, in particular to a printable plastic film and a preparation method thereof. Background technique [0002] With the development of modern packaging printing, printing plastic film has become very common, but in the printing process, because the surface characteristics of plastic are different from other substrates, and some properties of printing ink can not be well adapted to plastic products, so printing Quality is often inconsistent. Therefore, the quality of printable plastic films must be improved. However, among the plastic films used for single-layer packaging in the market, double-sided heat-sealing films are often unprintable, and the printable plastic films are generally of low quality or high production cost, which will directly affect the application range of the film. [0003] The invention patent with application number 201410764684.2 provides a printable double-sided ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/12C08L57/00C08K13/02C08K3/04C08K3/22C08K3/08C08J5/18
Inventor 冯志伟鲜志德
Owner ZHEJIANG CHENGDE PACKAGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap