A kind of plastic film that can be used on the inner surface of lunch box and its preparation method

A technology of plastic film and inner surface, applied in the field of plastic film and its preparation, can solve the problems of unfavorable health of consumers, unstable structure of fast food boxes, poor oil absorption, etc., so as to ensure human health, avoid oil leakage, guarantee effect of freshness

Active Publication Date: 2021-05-07
ZHEJIANG CHENGDE PACKAGING
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The main purpose of the present invention is to provide a plastic film that can be used on the inner surface of the lunch box and its preparation method, so as to solve the problem of unstable product structure and poor oil absorption of fast food boxes in the prior art, and at the same time, long-term use is not conducive to the health of consumers. , and the problem of difficult degradation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of plastic film that can be used on the inner surface of lunch box and its preparation method
  • A kind of plastic film that can be used on the inner surface of lunch box and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A plastic film that can be used on the inner surface of the lunch box

[0030] The raw materials for preparing the upper and lower surface layers of the plastic film that can be used on the inner surface of the lunch box include: polyethylene 5000g, tea polyphenols 1000g, purple potato starch 200g, methyl paraben 100g, sodium carboxymethyl cellulose 200g; the raw materials of the plastic film intermediate layer that can be used on the inner surface of the lunch box include by weight: polyethylene 5000g, tea polyphenols 1000g, purple potato starch 200g, methyl paraben 100g, carboxymethyl fiber Plain sodium 200g, sawdust 100g.

[0031] Prepared by:

[0032] In step a, the weight portion of sodium carboxymethylcellulose is prepared into a solution with a viscosity of 300 mpa·s, the weight portion of purple potato starch is added, and the temperature is 60° C., sonicated for 1 hour to obtain a mixed solution;

[0033] Step b, adding the polyethylene, tea polyphenol, and m...

Embodiment 2

[0038] A plastic film that can be used on the inner surface of the lunch box

[0039]The raw materials for preparing the upper and lower surface layers of the plastic film that can be used on the inner surface of the lunch box include: polyethylene 6000g, tea polyphenols 1500g, purple potato starch 400g, methyl paraben 150g, carboxymethyl cellulose Sodium 400g; The raw material that can prepare the plastic film intermediate layer that can be used on the inner surface of the lunch box includes by weight: polyethylene 6000g, tea polyphenols 1500g, purple sweet potato starch 400g, methyl paraben 150g, carboxymethyl Sodium cellulose 400g, sawdust 200g.

[0040] Prepared by:

[0041] In step a, the weight portion of sodium carboxymethylcellulose is formulated into a solution with a viscosity of 500 mpa·s, the weight portion of purple potato starch is added, and the temperature is 65° C., sonicated for 2 hours to obtain a mixed solution;

[0042] Step b, adding the polyethylene, t...

Embodiment 3

[0047] A plastic film that can be used on the inner surface of the lunch box

[0048] The raw materials for preparing the upper and lower surface layers of the plastic film that can be used on the inner surface of the lunch box include: polyethylene 5200g, tea polyphenols 1300g, purple potato starch 260g, methyl paraben 120g, sodium carboxymethyl cellulose 260g; the raw materials for preparing the plastic film intermediate layer that can be used on the inner surface of the lunch box include by weight: polyethylene 5200g, tea polyphenols 1300g, purple potato starch 260g, methyl paraben 120g, carboxymethyl fiber Sodium 260g, sawdust 120g.

[0049] Prepared by:

[0050] In step a, the weight part of sodium carboxymethyl cellulose is prepared into a solution with a viscosity of 400 mpa·s, the weight part of purple potato starch is added, and the temperature is 62 ° C, ultrasonic for 1.2 h to obtain a mixed solution;

[0051] Step b, adding the polyethylene, tea polyphenol, and m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a plastic film that can be used on the inner surface of a lunch box and a preparation method thereof. The plastic film that can be used on the inner surface of the lunch box includes upper and lower surface layers and an intermediate layer; Raw materials include: polyethylene, tea polyphenols, purple potato starch, methyl paraben, sodium carboxymethyl cellulose; raw materials for preparing the middle layer of plastic film that can be used on the inner surface of lunch boxes include: polyethylene, tea Polyphenols, purple potato starch, methyl paraben, sodium carboxymethyl cellulose, wood chips; using the preparation method of the present invention, each part of the raw materials cooperate with each other to prepare the plastic film that can be used on the inner surface of the lunch box The material is green and environmentally friendly, can be quickly degraded, and has the effect of efficiently absorbing oil stains; the preparation method is simple and can be widely used.

Description

technical field [0001] The invention relates to the field of film production and processing, in particular to a plastic film that can be used on the inner surface of a lunch box and a preparation method thereof. Background technique [0002] With the development of science and technology and the progress of the times, the living standards of human beings are gradually improving, and more and more people pay special attention to quality and service. The fast-paced pace of life has become the mainstream of the times, and the fast-food industry has developed rapidly. Takeaways and packed lunches can be seen everywhere, and fast-food boxes are widely used, and the quality requirements are getting higher and higher. After all The large-scale use will cause huge pressure on the environment. At the same time, whether the fast food box itself can be really healthy and harmless is also a topic of great concern to consumers. At present, it is particularly important to prepare a plast...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L3/02C08L1/28C08K5/134C08K5/13B29C48/10B29C48/18B29C55/28B29C59/02B29C69/02B32B3/24B32B27/06B32B27/18B32B27/32
Inventor 鲜志德陈华
Owner ZHEJIANG CHENGDE PACKAGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap