Green high-performance polymer cement waterproof mortar adopting aeolian sand and preparation method of waterproof mortar

A high-performance polymer, waterproof mortar technology, applied in the field of building waterproof materials, can solve problems such as scarcity of raw materials, and achieve the effects of improving mechanical properties and impermeability, saving resources, and achieving significant waterproofing effects.

Pending Publication Date: 2019-06-21
NANJING FORESTRY UNIV
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The demand for waterproofing in construction projects is increasing day by day, and the research enthusiasm for high-performance green waterproof materials is also increasing, but its raw materials are increasingly scarce

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Green high-performance polymer cement waterproof mortar adopting aeolian sand and preparation method of waterproof mortar
  • Green high-performance polymer cement waterproof mortar adopting aeolian sand and preparation method of waterproof mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A green high-performance polymer cement waterproof mortar using aeolian sand, in parts by weight, including the following components:

[0034] PO·42.5 grade ordinary Portland cement 35%, quartz sand 30%, aeolian sand 25%, rubber powder 9%, polypropylene fiber 0.5%, water reducing agent 0.3%, defoaming agent 0.2%.

[0035] Preparation:

[0036] (1) Weigh the required materials, including: PO·42.5 grade ordinary Portland cement, quartz sand, aeolian sand, rubber powder, polypropylene fiber, water reducer and defoamer;

[0037] (2) Put the weighed PO·42.5 grade ordinary Portland cement, rubber powder, water reducing agent and defoamer into the Enrich-R three-dimensional mixer in turn, stir at low speed, and the rotor speed is 150 rpm , The rotating speed of the mixing disc is 40 revolutions per minute, and the mixing time is 100 minutes to obtain a uniform mixture M1;

[0038] (3) Add quartz sand and aeolian sand to the above-mentioned mixture M1, and stir at low speed, wherein the...

Embodiment 2

[0042] A green high-performance polymer cement waterproof mortar using aeolian sand, in parts by weight, including the following components:

[0043] PO·42.5 grade ordinary Portland cement 37%, quartz sand 28%, aeolian sand 26%, rubber powder 8%, polypropylene fiber 0.6%, water reducing agent 0.2%, defoaming agent 0.2%.

[0044] Preparation:

[0045] (1) Weigh the required materials, including: PO·42.5 grade ordinary Portland cement, quartz sand, aeolian sand, rubber powder, polypropylene fiber, water reducer and defoamer;

[0046] (2) Put the weighed PO·42.5 grade ordinary Portland cement, rubber powder, water reducing agent and defoamer into the Enrich-R three-dimensional mixer in turn, stir at low speed, and the rotor speed is 150 rpm , The rotating speed of the mixing disc is 40 revolutions per minute, and the mixing time is 100 minutes to obtain a uniform mixture M1;

[0047] (3) Add quartz sand and aeolian sand to the above-mentioned mixture M1, and stir at low speed, wherein the...

Embodiment 3

[0051] A green high-performance polymer cement waterproof mortar using aeolian sand, in parts by weight, including the following components:

[0052] PO·42.5 grade ordinary Portland cement 39%, quartz sand 28%, aeolian sand 26%, rubber powder 7%, polypropylene fiber 0.8%, water reducing agent 0.1%, defoaming agent 0.1%.

[0053] Preparation:

[0054] (1) Weigh the required materials, including: PO·42.5 grade ordinary Portland cement, quartz sand, aeolian sand, rubber powder, polypropylene fiber, water reducer and defoamer;

[0055] (2) Put the weighed PO·42.5 grade ordinary Portland cement, rubber powder, water reducing agent and defoamer into the Enrich-R three-dimensional mixer in turn, stir at low speed, and the rotor speed is 150 rpm , The rotating speed of the mixing disc is 40 revolutions per minute, and the mixing time is 100 minutes to obtain a uniform mixture M1;

[0056] (3) Add quartz sand and aeolian sand to the above-mentioned mixture M1, and stir at low speed, wherein the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses green high-performance polymer cement waterproof mortar adopting aeolian sand and a preparation method of the waterproof mortar. The mortar is prepared from components as follows: 34-36 parts of cement, 29-32 parts of quartz sand, 23-26 parts of the aeolian sand, 8-10 parts of latex powder, 0.2-0.6 parts of fibers, 0.1-0.2 parts of a water reducer and 0.2-0.4 parts of a defoaming agent. The aeolian sand is utilized to equivalently replace part of the quartz sand, so that the green high-performance polymer cement waterproof mortar with properties including liquidity, caking property, impermeability and the like better than those of common polymer cement waterproof mortar is prepared. The problem of shortage of existing building raw materials is solved, the problem ofincreasingly serious desertization at present can be solved, the aeolian sand as a waste resource is sufficiently utilized, waste is changed into wealth, and sustainable development of the building waterproofing industry can be promoted.

Description

Technical field [0001] The invention belongs to the field of building waterproof materials, and particularly relates to a green high-performance polymer cement waterproof mortar using aeolian sand and a preparation method thereof. Background technique [0002] Due to the increasing complexity of construction projects, higher requirements are also put forward for building waterproofing. In recent years, the frequent occurrence of accidents such as leakage of external walls, bulging of tiles, and injuries to people due to problems with waterproof materials have attracted people's attention. Therefore, improving and improving the performance of waterproof materials through material design and optimization is an important problem to be solved urgently. Traditional waterproof materials have experienced long-term development, and now the new type of waterproof material, green high-performance polymer cement waterproof mortar, is the latest development trend in the building waterproofi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/27
Inventor 褚洪岩王元纲黄凯健王立彬侯彦明董峰辉丁明珉
Owner NANJING FORESTRY UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com