UV infiltration bottom for calcium silicon plate

A technology of silicon-calcium board and silicone defoamer, which is applied in polyurea/polyurethane coatings, coatings, etc., can solve the problems of failing to meet market and customer requirements, restricting the development and promotion of UV paint, and affecting the economic benefits of the UV industry. , achieve excellent leveling, good interlayer adhesion, and promote economic development

Inactive Publication Date: 2019-06-21
HUIZHOU CHANGRUNFA PAINT +1
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the outdoors will be exposed to the sun and rain, and as the rain soaks, there will be problems of falling between the paint films and poor adhesion
The existing UV permeable bottoms used for calcium-silicon boards have problems such as poor yellowing resistance and poor outdoor weather resistance, which cannot meet the requirements of the market and customers
This severely restricts the development and promotion of UV paint, and affects the economic benefits of the UV industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A UV permeable bottom for calcium-silicon boards, comprising the following components in parts by weight:

[0031] 35 parts of aromatic polyurethane acrylic resin;

[0032] 10 parts of aliphatic polyurethane acrylate;

[0033] 29 parts of propoxylated neopentyl glycol diacrylate;

[0034] 20 parts of trimethylolpropane triacrylate;

[0035] 0.2 parts of silicone defoamer;

[0036] 5 parts of photoinitiator;

[0037] The photoinitiator is a mixture of TPO and 1173.

[0038] The UV penetrating primer provided in this example has a viscosity of 550±100 mPa.s (measured at a temperature of 25°C), and the construction method is roller coating, and the coating amount is 40-50g / m 2 , The curing energy has reached 800-1000mj.

[0039] The UV permeable bottom for silicon-calcium board provided by this embodiment is carried out by making aromatic urethane acrylic resin, aliphatic urethane acrylate, propoxylated neopentyl glycol diacrylate and trimethylolpropane triacrylate ...

Embodiment 2

[0041] A UV permeable bottom for calcium-silicon boards, comprising the following components in parts by weight:

[0042] 45 parts of aromatic polyurethane acrylic resin;

[0043] 15 parts of aliphatic polyurethane acrylate;

[0044] 35 parts of propoxylated neopentyl glycol diacrylate;

[0045] 25 parts of trimethylolpropane triacrylate;

[0046] 0.4 parts of silicone defoamer;

[0047] 8 parts of photoinitiator;

[0048] The photoinitiator is a mixture of TPO and 1173.

[0049] The UV penetrating primer provided in this example has a viscosity of 600±100 mPa.s (measured at a temperature of 25°C), and the construction method is roller coating, and the coating amount is 40-45g / m 2 , The curing energy reached 900mj.

[0050] The UV permeable bottom for silicon-calcium board provided by this embodiment is carried out by making aromatic urethane acrylic resin, aliphatic urethane acrylate, propoxylated neopentyl glycol diacrylate and trimethylolpropane triacrylate The combi...

Embodiment 3

[0052] A UV permeable bottom for calcium-silicon boards, comprising the following components in parts by weight:

[0053] 30 parts of aromatic polyurethane acrylic resin;

[0054] Aliphatic urethane acrylate 5 parts;

[0055] 25 parts of propoxylated neopentyl glycol diacrylate;

[0056] 15 parts of trimethylolpropane triacrylate;

[0057] 0.1 part of silicone defoamer;

[0058] 6 parts of photoinitiator;

[0059] The photoinitiator is a mixture of TPO and 1173.

[0060] The viscosity of the UV penetrating primer provided in this example is 500±100 mPa.s (measured at 25°C), and the construction method is roller coating, and the coating amount is 45-50g / m 2 , The curing energy reached 800mj.

[0061] The UV permeable bottom for silicon-calcium board provided by this embodiment is carried out by making aromatic urethane acrylic resin, aliphatic urethane acrylate, propoxylated neopentyl glycol diacrylate and trimethylolpropane triacrylate The combination makes the UV penet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a UV infiltration bottom for a calcium silicon plate, wherein the UV infiltration bottom comprises: an aromatic polyurethane acrylic resin, aliphatic polyurethane acrylate, propoxylated neopentyl glycol diacrylate, trimethylolpropane triacrylate, an organosilicon antifoaming agent and a photoinitiator. According to the present invention, by compounding aromatic polyurethaneacrylic resin, aliphatic polyurethane acrylate, propoxylated neopentyl glycol diacrylate and trimethylolpropane triacrylate, the obtained UV infiltration bottom has good water resistance, can providegood interlayer adhesion to substrates and paint films, further has advantages of excellent leveling property, excellent yellowing resistance and excellent outdoor weather resistance, and can well meet the applications of the UV infiltration bottom in outdoor wall surfaces, especially in calcium silicon plates.

Description

technical field [0001] The invention relates to the technical field of chemical coatings, in particular to a UV permeable bottom for calcium-silicon boards. Background technique [0002] UV paint is a light-curing paint. It is currently a widely used furniture paint. Its main features are: after strong ultraviolet light curing treatment, the color is stable and always new. The UV paint film has a three-dimensional structure with high hardness, good wear resistance, and good transparency. The product is scratch-resistant and friction-resistant, and can stand the test of time. UV paint is widely used in office furniture, etc. In recent years, it has become more and more widely used in indoor and outdoor decorative panels. [0003] As a decorative board, calcium silicate board is also widely used in UV paint on outdoor walls. However, it will be exposed to the sun and rain outdoors, and as the rain soaks, there will be problems of falling between the paint films and poor adhe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14
Inventor 陈腾练世斌戴超
Owner HUIZHOU CHANGRUNFA PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More