Silicon carbide powder reinforced high-performance plastic and preparation method thereof

A technology of high-performance plastics and silicon carbide powder, applied in the field of high-performance plastics, can solve the problems of poor wear resistance of plastics, and achieve excellent friction and wear resistance, good physical and mechanical properties, and reasonable matching effects

Inactive Publication Date: 2019-07-05
赛兴(北京)科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to propose a high-performance wear-resistant plastic preparation method for the problem of poor wear resistance of plastics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of silicon carbide powder reinforced plastic material that the present invention proposes, its preparation method comprises the following steps:

[0022] (1) Weighing of raw materials:

[0023] Weigh the following raw materials in corresponding parts by weight for later use: 70 parts of polytetrafluoroethylene, 10 parts of silicon carbide powder, 8 parts of reagent graphite, 5 parts of molybdenum disulfide, 3 parts of bronze powder, 2 parts of carbon fiber powder, and 2 parts of glass fiber powder;

[0024] (2) Mixture drying:

[0025] Mix the raw materials weighed in step (1) evenly by weight, dry in an incubator at 70°C for 25 minutes, and take them out for use;

[0026] (3) Thermoforming:

[0027] Put the mixed and dried raw materials obtained in step (2) into the cleaned mould, place the mold on the template, and press the hot press lightly during the heating process to ensure that the upper template is always in contact with the upper gland of the mold (th...

Embodiment 2

[0035] A kind of silicon carbide powder reinforced plastic material that the present invention proposes, its preparation method comprises the following steps:

[0036] (1) Weighing of raw materials:

[0037] Weigh the following raw materials in corresponding parts by weight for later use: 68 parts of polytetrafluoroethylene, 12 parts of silicon carbide powder, 6 parts of reagent graphite, 5 parts of molybdenum disulfide, 5 parts of bronze powder, 2 parts of carbon fiber powder, and 2 parts of glass fiber powder;

[0038] (2) Mixture drying:

[0039] Mix the raw materials weighed in step (1) evenly by weight, dry in an incubator at 75°C for 28 minutes, and take them out for use;

[0040] (3) Thermoforming:

[0041] Put the mixed and dried raw materials obtained in step (2) into the cleaned mould, place the mold on the template, and press the hot press lightly during the heating process to ensure that the upper template is always in contact with the upper gland of the mold (th...

Embodiment 3

[0049] A kind of silicon carbide powder reinforced plastic material that the present invention proposes, its preparation method comprises the following steps:

[0050] (1) Weighing of raw materials:

[0051] Weigh the following raw materials in corresponding parts by weight for later use: 65 parts of polytetrafluoroethylene, 15 parts of silicon carbide powder, 10 parts of reagent graphite, 3 parts of molybdenum disulfide, 5 parts of bronze powder, 1 part of carbon fiber powder, and 1 part of glass fiber powder;

[0052] (2) Mixture drying:

[0053] Mix the raw materials weighed in step (1) evenly by weight, dry in a constant temperature box at 80°C for 30 minutes, and take them out for use;

[0054] (3) Thermoforming:

[0055] Put the mixed and dried raw materials obtained in step (2) into the cleaned mould, place the mold on the template, and press the hot press lightly during the heating process to ensure that the upper template is always in contact with the upper gland of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
purityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a silicon carbide powder reinforced high-performance plastic and a preparation method thereof. Raw materials of the silicon carbide powder reinforced high-performance plastic include, by weight, 65-70 parts of polytetrafluoroethylene, 10-15 parts of silicon carbide powder, 5-10 parts of a reagent graphite, 2-5 parts of molybdenum disulfide, 2-5 parts of bronze powder, 1-2 parts of carbon fiber powder and 1-2 parts of glass fiber powder. The preparation method comprises the following steps: (1) raw material weighing; (2) mixing, and drying; (3) hot pressing forming; and(4) preparation of the finished product. The preparation method of the high-performance plastic has the advantages of simple process, reasonable steps, and convenience in promotion and application, and the prepared plastic has the advantages of good physical and mechanical properties, excellent anti-friction and anti-wear performances, strong chemical stability, and great market competitiveness and production practical values.

Description

technical field [0001] The invention relates to the technical field of high-performance plastics, in particular to a silicon carbide powder-reinforced plastic material and a preparation method thereof. Background technique [0002] Plastic is a high molecular compound polymerized by addition polymerization or polycondensation reaction with monomer as raw material. It is commonly known as plastic or resin. It can freely change its composition and shape. , Colorants and other additives. The basic properties of plastics are mainly determined by the nature of the resin, but additives also play an important role. At present, many plastics have poor friction and wear resistance, which limits their application in specific environments. Contents of the invention [0003] The purpose of the present invention is to propose a high-performance wear-resistant plastic preparation method for the problem of poor wear resistance of plastics. [0004] The present invention is achieved th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/18C08K13/04C08K3/34C08K3/04C08K3/30C08K3/08C08K7/06C08K7/14
CPCC08K3/04C08K3/08C08K3/30C08K3/34C08K7/06C08K7/14C08K13/04C08K2003/085C08K2003/3009C08L27/18
Inventor 田秀梅张冀
Owner 赛兴(北京)科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com