Smelting method for improving surface quality of steel plate
A technology of surface quality and smelting method, applied in the field of iron and steel smelting, can solve the problems of little effect, poor effect, neglecting the effect of materials, etc., to reduce the damage of surface quality, facilitate high-temperature desulfurization, and reduce the probability of grinding treatment.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0032] Example 1
[0033] This embodiment provides a smelting method for improving the surface quality of steel plates,
[0034] S1. Its chemical composition and mass percentage are as follows: C: 0.02%~0.20%, Si≤0.20%, Mn: 1.20%~2.20%, P≤0.030%, S≤0.0050%, Ni≤0.30%, Nb≤0.070% , Cu≤0.50%, N≤0.0050%, Ti: 0.006%~0.020%, Cr≤0.30%, Al: 0.015%~0.050%, the balance is Fe and impurities;
[0035] S2. The desulfurization station uses lime and magnesium powder for composite desulfurization. After desulfurization, the slag is cleaned, and the molten iron into the furnace S≤0.0020%, and the S after the converter is 0.0008%;
[0036] S3. Steelmaking adopts the process route of BOF→LF furnace refining→RH refining→continuous casting; converter tapping temperature is 1696℃; converter tapping uses pre-melted refining slag + active lime for slagging;
[0037] S4. After the molten steel reaches the LF furnace, the temperature is raised to melt the slag, and the composition meets the requirements of step ...
Example Embodiment
[0040] Example 2
[0041] This embodiment provides a smelting method for improving the surface quality of steel plates,
[0042] S1. Its chemical composition and mass percentage are as follows: C: 0.20%~0.60%, Si≤0.20%, Mn: 0.30%~1.60%, P≤0.030%, S≤0.0050%, Ni≤0.30%, Nb≤0.070% , Cu≤0.50%, N≤0.0050%, Ti: 0.006%~0.020%, Cr≤0.30%, Al: 0.015%~0.050%, the balance is Fe and impurities;
[0043] S2. The desulfurization station uses lime and magnesium powder for composite desulfurization. After desulfurization, the slag is cleaned, and the molten iron into the furnace S≤0.0020%, and the S after the converter is 0.0006%;
[0044] S3. Steelmaking adopts the process route of BOF→LF furnace refining→RH refining→continuous casting; converter tapping temperature is 1706℃; converter tapping uses pre-melted refining slag + active lime for slagging;
[0045] S4. After the molten steel reaches the LF furnace, the temperature is raised to melt the slag, and the composition meets the requirements of step ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap